Liquid phase and aqueous solutions of poly(vinyl methyl ether) from highly purified vinyl methyl ether monomer
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C08F-002/06
C08F-006/08
C08F-116/18
출원번호
US-0105889
(1993-08-11)
발명자
/ 주소
Kulzick Matthew A. (Warrenville IL) Koning Paul A. (Aurora IL)
출원인 / 주소
Amoco Corporation (Chicago IL 02)
인용정보
피인용 횟수 :
3인용 특허 :
0
초록▼
A process is disclosed for the preparation of liquid and aqueous solutions of amorphous colorless poly (vinyl methyl ether) polymer with low level of impurities from purified vinyl methyl ether. The polymer has relatively high molecular weight, narrow molecular weight distribution and does not degra
A process is disclosed for the preparation of liquid and aqueous solutions of amorphous colorless poly (vinyl methyl ether) polymer with low level of impurities from purified vinyl methyl ether. The polymer has relatively high molecular weight, narrow molecular weight distribution and does not degrade readily due to the presence of impurities. The purification of the monomer uses a procedure selected from the group consisting of a vapor-liquid separation, a solid-liquid separation and combinations thereof to remove the impurities at a temperature within the range of from -20°C. to +30°C. The aqueous solution is prepared by devolitilization of solvent solutions of the polymerized purified vinyl methyl ether monomer. The solid polymer is prepared by heating the aqueous solution of the poly(vinyl methyl ether). The amorphous polymers of poly(vinyl methyl ether) are particularly suited for adhesive applications.
대표청구항▼
A process for preparation of liquid phase and aqueous solutions of poly(vinyl methyl ether) polymer from purified vinyl methyl ether monomer containing less than 750 parts per million total of impurities comprising water, methanol, ethanol, acetaldehyde, 1,1-dimethoxyethane, and ethylene glycol, sai
A process for preparation of liquid phase and aqueous solutions of poly(vinyl methyl ether) polymer from purified vinyl methyl ether monomer containing less than 750 parts per million total of impurities comprising water, methanol, ethanol, acetaldehyde, 1,1-dimethoxyethane, and ethylene glycol, said polymer containing less than 100 parts per million total of said impurities in the absence of water and less than 250 parts per million of a non-aromatic, non-chlorinated hydrocarbon solvent of from 2 to 20 carbon atoms, wherein said polymer is water-white, colorless, has a number average molecular weight Mn above 20,000, a weight average molecular weight Mw above 80,000, a molecular weight distribution Mw/Mn of less than 2.5, wherein said process comprises: a) purifying impure vinyl methyl ether monomer containing impurities comprising water, methanol, ethanol, acetaldehyde, 1,1-dimethoxyethane and ethylene glycol to levels less than 750 parts per million (ppm) by extracting said impurities from said monomer by a separation technique selected from the group consisting of a vapor-liquid extraction separation, a solid-liquid adsorption separation, and combinations thereof, said separation technique characterized as being at a temperature within the range of from about -20°C. to about +50°C. to about +50°C. and the said extracted monomer characterized as being water white in color; b) polymerizing said purified monomer in the presence of an alkyl aluminum halide catalyst and a co-catalyst activator to poly(vinyl methyl ether) polymer in a reaction mixture comprising said monomer and a non-aromatic, non-chlorinated hydrocarbon solvent of from 2 to 20 carbon atoms at a temperature within the range of from about -10°C. to about +20°C. at a pressure sufficient to maintain the reaction mixture in predominantly a liquid state, to prepare poly(vinyl methyl ether) polymer in said reaction mixture; c) extracting said catalyst and said co-catalyst from said poly(vinyl methyl ether) in said reaction mixture by adding to said reaction mixture a stoichiometric amount of base in water, and, alternatively, in a secondary alcohol selected from the group of secondary alcohols consisting of secondary alcohols of from 3 to 20 carbon atoms and adding the resultant reaction mixture into excess water present as a water wash, at a temperature of from about 0°C. to about 90°C. and a pH of not less than 5 in the aqueous phase wherein said temperature and pH are maintained to cause the said catalyst and said co-catalyst to partition into said wash water, and to remove said catalyst and said co-catalyst from said reaction mixture with said wash water in the absence of hydrolysis and polymerization of unreacted vinyl methyl ether and formation of emulsions to prepare solvent/poly(vinyl methyl ether) mixture; d) preparing an aqueous poly(vinyl methyl ether) solution by contacting said solvent/poly(vinyl methyl ether) mixture with a solvent selected from the group of water and water/organic ether mixtures at a temperature within the range from about 0°C. to about 35°C. under a vacuum within the range from about 0.1 mm Hg to about 600 mm Hg to remove the solvent by vaccum stripping said solvent to form a soluble mixture of water and poly(vinyl methyl ether) wherein said aqueous poly(vinyl methyl ether) solution has a poly(vinyl methyl ether) concentration in the range of from 5 to about 70 wt. %, residual solvent level of less than 250 ppm and total concentration of impurities comprising methanol, ethanol, acetaldehyde, 1,1-dimethoxyethane and ethylene glycol is less than 100 ppm; and, alternatively, e) preparing a solid poly(vinyl methyl ether) polymer by heating said aqueous poly(vinyl methyl ether) solution to a temperature within the range of from about 40°C. to about 100°C. to precipitate said poly(vinyl methyl ether) as a solid from said solution, separating said solid from said solution by solid/liquid separation technique to recover said solid poly(vinyl methyl ether, and heating said solid poly(vinyl methyl ether) under vacuum from about 0.1 mm Hg to about 600 mm Hg to a temperature of from about 100°C. to about 200°C. to remove residual water and solvent from said solid poly(vinyl methyl ether).
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허를 인용한 특허 (3)
Kubota, Minoyuki; Suzuki, Kazuhiko; Yamazaki, Hirotaka; Yoshimoto, Tokuyuki; Ogawa, Akihisa; Kamimori, Shigeru, Process for producing a high-purity oxygenic compound and lubricating oil.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.