초록 ▼

A rail for a linear motion guide bearing is fabricated by using a steel which contains C in a range of from 0.56 to 1.0% by weight, Si in a range of up to 0.15% by weight, Mn in a range from 0.20 to 0.40% by weight, Cr in a range of from 0.30 to 0.70% by weight, and B in a range of from 0.0005 to 0.

A rail for a linear motion guide bearing is fabricated by using a steel which contains C in a range of from 0.56 to 1.0% by weight, Si in a range of up to 0.15% by weight, Mn in a range from 0.20 to 0.40% by weight, Cr in a range of from 0.30 to 0.70% by weight, and B in a range of from 0.0005 to 0.0035% by weight, whereby the hardness of the track surface of the resultant rail is higher than a Vickers hardness of 700, and the die is not decreased in service 1 life by the cold-drawing of the steel.

대표청구항 ▼

A rail for a linear motion guide bearing, the rail being fabricated into a required shape with a track surface, by using steel which is cold-drawn and induction-hardened, said steel comprising: carbon in a range of from 0.56 to 1.0% by weight; silicon in a range of 0.05 to 0.15% by weight; manganese

A rail for a linear motion guide bearing, the rail being fabricated into a required shape with a track surface, by using steel which is cold-drawn and induction-hardened, said steel comprising: carbon in a range of from 0.56 to 1.0% by weight; silicon in a range of 0.05 to 0.15% by weight; manganese in a range of from 0.20 to 0.40% by weight; chromium in a range of from 0.30 to 0.70% by weight; and boron in a range of from 0.0005 to 0.0035% by weight, the rail comprising a hardened surface layer having a hardness of a range from 700 to 800 in Vickers hardness (Hv) in a surface portion of the rail from the track surface to substantially 1.4 mm in depth.