초록 ▼

The present invention relates to a process for the preparation of a large-pore molecular sieve, comprising crystallizing the molecular sieve from a starting mixture at a pH in the range of from 3 to 8, and recovering a large-pore molecular sieve, the said starting mixture having a molar composition

The present invention relates to a process for the preparation of a large-pore molecular sieve, comprising crystallizing the molecular sieve from a starting mixture at a pH in the range of from 3 to 8, and recovering a large-pore molecular sieve, the said starting mixture having a molar composition satisfying the following molar ratio\s: (0.01-2)R2/nO):(0-1.5)M2/mO:(0-0.5)X2O3:1YO2:(5-1000)H2O:(0.01-3)F-, wherein n and m are the weighted average valences of R and M respectively, M is an alkali- or alkaline earth metal, X is a trivalent metal and Y is a tetravalent element, wherein R comprises at least one main organic template Rm having the formula R1R2R3R4Q+wherein Q is nitrogen or phosphorus and wherein at least one and at most three of R1, R2, R3 and R4 is an aryl or alkyl group having 6 to 36 carbon atoms and each of the remainder of R1, R2, R3 and R4 is selected from hydrogen and an alkyl group having 1 to 5 carbon atoms.

대표청구항 ▼

A process for the preparation of a large-pore molecular sieve having in its calcined state an X-ray diffraction pattern with at least one peak at a d-spacing of at least 1.8 nanometers, comprising crystallizing the molecular sieve from a starting mixture at a pH in the range of from 3 to 8, and reco

A process for the preparation of a large-pore molecular sieve having in its calcined state an X-ray diffraction pattern with at least one peak at a d-spacing of at least 1.8 nanometers, comprising crystallizing the molecular sieve from a starting mixture at a pH in the range of from 3 to 8, and recovering a large-pore molecular sieve, the said starting mixture having a molar composition satisfying the following molar ratios: (0.01-2)R2/nO):(0-1.5)M2/mO :(0-0.5)X2O3:1YO2:(5-1000)H2O:(0.01-3)F-, wherein n and m are the weighted average valences of R and M respectively, M is an alkali- or alkaline earth metal, X is a trivalent metal and Y is a tetravalent element, wherein R comprises at least one main organic template Rm having the formula R1R2R3R4Q+wherein Q is nitrogen or phosphorus, wherein at least one and at most three of R1, R2, R3 and R4 is an aryl or alkyl group having 6 to 36 carbon atoms and each of the remainder of R1, R2, R3 and R4 is selected from hydrogen and an alkyl group having 1 to 5 carbon atoms, and wherein the fluorine source is selected from the group consisting of HF, NH4F and mixtures thereof.