A process to make a sorbent composition said process comprising: (a) contacting (i) at least one zinc component, where said zinc component consists essentially of zinc oxide, or a compound convertible to zinc oxide, (ii) at least one silica component, where said silica component consists essentially
A process to make a sorbent composition said process comprising: (a) contacting (i) at least one zinc component, where said zinc component consists essentially of zinc oxide, or a compound convertible to zinc oxide, (ii) at least one silica component, where said silica component consists essentially of silica, or a compound convertible to silica, (iii) at least one colloidal oxide component, where said colloidal oxide component consists essentially of particles of a metal oxide where said metal oxide is selected from the group consisting of alumina, silica, titania, zirconia, tin oxide, antimony oxide, cerium oxide, yttrium oxide, copper oxide, iron oxide, manganese oxide, molybdenum oxide, tungsten oxide, chromium oxide, and mixtures thereof, (iv) at least one pore generator component, wherein the amount of pore generator is from 1 to about 15 weight percent based on the total weight of said sorbent composition, and wherein said sorbent composition consists essentially of components (a)(i) through (a)(iv) to form a moist composition, where said moist composition has a moisture content from about 22 to about 31 weight percent based on the weight of said moist composition; (b) extruding said moist composition to form an extruded, moist composition where said extruded, moist composition has a moisture content from about 22 to about 31 weight percent based on the weight of said extruded, moist composition; and (c) sphering said extruded, moist composition to form a sphered, extruded, moist composition that has a particle size from about 0.5 to about 15 millimeters.
대표청구항▼
[ That which is claimed:] [1.] A process to make a sorbent composition said process comprising:(a) contacting(i) at least one zinc component, where said zinc component consists essentially of zinc oxide, or a compound convertible to zinc oxide,(ii) at least one silica component, where said silica co
[ That which is claimed:] [1.] A process to make a sorbent composition said process comprising:(a) contacting(i) at least one zinc component, where said zinc component consists essentially of zinc oxide, or a compound convertible to zinc oxide,(ii) at least one silica component, where said silica component consists essentially of silica, or a compound convertible to silica,(iii) at least one colloidal oxide component, where said colloidal oxide component consists essentially of particles of a metal oxide where said metal oxide is selected from the group consisting of alumina silica, titania, zirconia, tin oxide ,antimony oxide, cerium oxide, yttrium oxide, copper oxide, iron oxide, manganese oxide, molybdenum oxide, tungsten oxide, chromium oxide, and mixtures thereof,(iv) at least one pore generator component, wherein the amount of pore generator is from 1 to about 15 weight percent based on the total weight of said sorbent composition, andwherein said sorbent composition consists essentially of components(a)(i) through (a)(iv) to form a moist composition, where said moist composition has a moisture content from about 22 to about 31 weight percent based on the weight of said moist composition;(b) extruding said moist composition to form an extruded, moist composition where said extruded, moist composition has a moisture content from about 22 to about 31 weight percent based on the weight of said extruded, moist composition; and(c) sphering said extruded, moist composition to form a sphered, extruded, moist composition that has a particle size from about 0.5 to about 15 millimeters.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (11)
Khare Gyanesh P. (Bartlesville OK), Absorption of hydrogen sulfide and absorbent composition therefor.
Flytzani-Stephanopoulos Maria (Winchester MA) Jothimurugesan Kandaswami (Baton Rouge LA), Preparation of extrusions of bulk mixed oxide compounds with high macroporosity and mechanical strength.
Siminski Vincent (Rockaway NJ) Gernand Martin O. (Baton Rouge LA) Mayer Francis X. (Baton Rouge LA), Process for flue gas desulfurization or nitrogen oxide removal using a magnetically stabilized fluid cross-flow contacto.
Courty ; Philippe ; Deschamps ; Andre ; Franckowiak ; Sigismond ; Sugie r ; Andre, Process for purifying a gas containing hydrogen sulfide and contact masses usable therefor.
Kidd Dennis R. (Dewey OK) Delzer Gary A. (Bartlesville OK) Kubicek Donald H. (Bartlesville OK) Schubert Paul F. (Bartlesville OK), Selective removal of hydrogen sulfide over a zinc oxide and silica absorbing composition.
Herbst, Konrad; Stern, Peter; Blom, Niels Jørgen; Starch-Hytoft, Glen; Knudsen, Kim Grøn, Process for the preparation of a paraffin isomerization catalyst.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.