초록 ▼

A faster and more efficient method for applying ultra thin films to substrate surfaces is disclosed. The method comprises heating a film forming composition comprising amphiphilic molecules to a liquid state, immersing the substrate surface in the heated liquid composition to heat the surface, and w

A faster and more efficient method for applying ultra thin films to substrate surfaces is disclosed. The method comprises heating a film forming composition comprising amphiphilic molecules to a liquid state, immersing the substrate surface in the heated liquid composition to heat the surface, and washing away the excess composition. For surfaces that ordinarily have insufficient or no chemical moieties reactive with the amphiphilic molecules, the immersion in the heated composition causes the substrate to become porous and expose previously unavailable chemically reactive moieties in the surface matrix. The amphiphilic molecules then self-assemble, chemically bond to the surface matrix and self-polymerize with each other and with other surface matrix-bound and/or surface-bound molecules to form the ultra thin surface film. The method is also faster and more efficient for coating non porous and metal surfaces.

대표청구항 ▼

[ We claim:] [1.] A method for applying an ultra thin film comprising amphiphilic molecules to a substrate surface that is chemically unreactive with or inadequately chemically reactive with said molecules, comprising the steps of:(a) providing a substrate having a surface that has an inadequate num

[ We claim:] [1.] A method for applying an ultra thin film comprising amphiphilic molecules to a substrate surface that is chemically unreactive with or inadequately chemically reactive with said molecules, comprising the steps of:(a) providing a substrate having a surface that has an inadequate number of or no available surface groups that are chemically reactive with amphiphilic molecules, wherein said substrate surface becomes porous when heated to a temperature in the range of 30.degree. C. to 120.degree. C. and newly exposes a surface matrix comprising moieties that are chemically reactive with the amphiphilic molecules;(b) providing a composition that comprises a film forming substance dispersed in a carrier that has a gel state at a temperature below 25.degree. C. and a liquid state at a temperature of 30.degree. C. to 120.degree. C., the film forming substance comprising amphiphilic molecules that are chemically reactive with the chemically reactive moieties of the surface matrix and are capable of automatically separating from the composition and of self-assembly and self-polymerization in the surface matrix, the carrier having a consistency in the gel state and the liquid state sufficient to inhibit diffusion of moisture and oxygen into the composition and to hold the molecules in suspension so that agglomeration of the molecules is minimized,wherein the film forming substance consists essentially of RmSiXn, where R is apolar and is selected from the group of compounds having 6 to 30 carbon atoms consisting essentially of alkyls, alkyl ethers, fluorinated alkyls, fluorinated alkyl ethers, diacetylenes, vinyl unsaturated groups, fused linear aromatic moieties, and branched aromatic moieties, where X is selected from the group consisting essentially of halogens, hydroxy, alkoxy and acetoxy, and where m=0-3 and n=1-4 and m plus n equals four;(c) heating the composition to a temperature of 30.degree. C. to 120.degree. C. to form a heated liquid composition;(d) immersing the substrate in the heated liquid composition for a period of time sufficient to heat the substrate surface to a temperature at which it forms pores in which the chemically reactive moieties within the surface matrix are exposed, wherein during said period of time the amphiphilic molecules automatically separate from the heated liquid compositions impregnate the surface matrix, chemically bond to the exposed chemically reactive moieties within the surface matrix, self-assemble and self-polymerize within the surface matrix, and further self-polymerize to bridge the surface area between the pores to form a substantially continuous thin film on the substrate surface, wherein the film has a substantially uniform thickness not greater than about 0.5 microns;(e) washing an excess of said composition from the substrate surface and the surface matrix with a heated liquid having a temperature of 30.degree. C. to 80.degree. C.; and(f) cooling the substrate surface to a temperature sufficient to secure the polymerized amphiphilic molecules in-situ.