초록 ▼

A glass-ceramic composition which is is crystallized in situ from a thermally crystallizable mixture containing from about 40 to about 80 weight percent of electric arc furnace dust and from about 10 to about 40 weight percent of glass. The composition has a Vickers hardness of at least about 5.5 gi

A glass-ceramic composition which is is crystallized in situ from a thermally crystallizable mixture containing from about 40 to about 80 weight percent of electric arc furnace dust and from about 10 to about 40 weight percent of glass. The composition has a Vickers hardness of at least about 5.5 gigaPascals, a Vickers fracture toughness of from about 0.6 to about 1.5 megaPascals.meters.sup.0.5, and a density of from about 2.8 to about 4.1 grams per cubic centimeter; and it contains from about 20 to about 40 weight percent of an iron oxide. When the composition is tested in accordance with the Environmental Protection Agency's Toxicity Characteristic Leaching Procedure, it produces a leachate which contains no detectable mercury, no detectable barium, no detectable selenium, less than 0.2 parts per million of detectable lead, less than 0.5 parts per million of detectable chromium, less than 0.1 parts per million of detectable cadmium, less than 0.005 parts per million of detectable arsenic, and less than 0.04 parts per million of detectable silver.

대표청구항 ▼

[ I claim:] [1.] A glass-ceramic composition, wherein said glass-ceramic composition is crystallized in situ from a thermally crystallizable mixture comprising from about 40 to about 80 weight percent of electric arc furnace dust, and from about 10 to about 40 weight percent of glass, wherein:(a) fr

[ I claim:] [1.] A glass-ceramic composition, wherein said glass-ceramic composition is crystallized in situ from a thermally crystallizable mixture comprising from about 40 to about 80 weight percent of electric arc furnace dust, and from about 10 to about 40 weight percent of glass, wherein:(a) from about 2 to about 4.5 parts, by weight, of said electric arc furnace dust are present for each part of said glass present in said mixture,(b) said electric arc furnace dust has a particle size distribution such that at least about 70 weight percent of its particles are smaller than about 20 microns,(c) said electric arc furnace dust comprises from about 25 to about 35 weight percent of at least one iron oxide compound,(d) said glass-ceramic composition has a Vickers hardness of at least about 5.5 gigaPascals, a Vickers fracture toughness of from about 0.6 to about 1.5 megaPascals.meters.sup.0.5, and a density of from about 2.8 to about 4.1 grams per cubic centimeter,(e) said glass-ceramic composition contains from about 20 to about 40 weight percent of an iron oxide selected from the group consisting of ferrous oxide, ferric oxide, and mixtures thereof, and(f) said composition, when it is tested in accordance with the Environmental Protection Agency's toxicity characteristic leaching procedure published at 40 Code of Federal Regulations 268.7(a), produces a leachate which contains no detectable mercury, less than about 0.2 parts per million of detectable barium, no detectable selenium, less than 0.2 parts per million of detectable lead, less than 0.5 parts per million of detectable chromium, less than 0.1 parts per million of detectable cadmium, less than 0.005 parts per million of detectable arsenic, and less than 0.04 parts per million of detectable silver.