초록 ▼

An improved method for manufacturing poly(hexamethylene adipamide), i.e. nylon 6,6, by reacting monomethyl adipate with hexamethylenediamine in an approximately equimolar ratio in the presence of water at a temperature of 100 to 165.degree. C. while simultaneous distilling off of a stoichiometric am

An improved method for manufacturing poly(hexamethylene adipamide), i.e. nylon 6,6, by reacting monomethyl adipate with hexamethylenediamine in an approximately equimolar ratio in the presence of water at a temperature of 100 to 165.degree. C. while simultaneous distilling off of a stoichiometric amount of methanol. The resulting aqueous intermediate product is then heated to 200 to 260.degree. C. while distilling off substantially all water at a pressure of 150 to 250 psig (1.03 .times.10.sup.6 to 1.72 .times.10.sup.6 Pa) followed by reducing the pressure to atmospheric pressure and increasing the temperature to 270 to 280.degree. C. to polycondense the distillate residue. Such a process is useful in producing high purity commercial grade poly(hexamethylene adipamide) that advantageously avoids problems caused by N-methylation of the polyamide.

대표청구항 ▼

[ We claim:] [1.] A method for preparing poly(hexamethylene adipamide) comprising the steps of:(a) reacting monomethyl adipate and hexamethylenediamine in an approximately equimolar ratio in the presence of water at a temperature of 100 to 165.degree. C. while simultaneous distilling off methanol an

[ We claim:] [1.] A method for preparing poly(hexamethylene adipamide) comprising the steps of:(a) reacting monomethyl adipate and hexamethylenediamine in an approximately equimolar ratio in the presence of water at a temperature of 100 to 165.degree. C. while simultaneous distilling off methanol and water for a time sufficient to remove at least 90 mole % of the theoretical stoichiometric amount of methanol;(b) heating the aqueous reaction product of step (a) to 200 to 260.degree. C. while distilling off substantially all water at a pressure of 100 to 250 psig (6.89 .times.10.sup.5 to 1.72 .times.10.sup.6 Pa) followed by reducing the pressure to atmospheric pressure and increasing the temperature to 270 to 280.degree. C. to polycondense the distillate residue; and(c) recovering poly(hexamethylene adipamide) having a relative viscosity of 20 to 100, measured at 8.4 wt % polyamide in 90/10 wt % formic acid/water @ 25.degree. C., and a concentration of N-methylated groups in the polyamide, analyzed as N-methylhexamethylenediamine, of less than 50 moles per million grams of polyamide.