초록 ▼

A method of controlling the amount of firing shrinkage of a ceramic green body prepared by molding a ceramic powder (A) to a desired value A.sub.1 by heat treating the powder at a temperature T.sub.1 that provides the firing shrinkage A.sub.1 at a predetermined firing temperature. The temperature T.

A method of controlling the amount of firing shrinkage of a ceramic green body prepared by molding a ceramic powder (A) to a desired value A.sub.1 by heat treating the powder at a temperature T.sub.1 that provides the firing shrinkage A.sub.1 at a predetermined firing temperature. The temperature T.sub.1 is determined based on an established correlation between an amount of firing shrinkage at the predetermined firing temperature and a heat-treatment temperature of a powder (B) having a composition similar to that of the powder (A) in such an extent that a total amount of a greatest common content of an individual component common between the powders (A) and (B) in terms of percent is 90% by weight or more, and satisfying such a relation that the spherical diameter of powder (A) is within a range of .+-. 30% relative to the spherical diameter (Rs) of the powder (B) and that its average degree of aggregation (x) is within the range from 1/2 fold to 2 fold relative to the average degree of aggregation (x) of the powder (B).

대표청구항 ▼

[ What is claimed is:] [1.] A method of preparing a fired ceramic powder body, comprising the steps of:(i) molding a ceramic powder (A) having a spherical diameter (Rs) of 1 .mu.m or less wherein said spherical diameter (Rs) is expressed by an equationEQU Rs (.mu.m)=6/.rho.s which .rho. is a true de

[ What is claimed is:] [1.] A method of preparing a fired ceramic powder body, comprising the steps of:(i) molding a ceramic powder (A) having a spherical diameter (Rs) of 1 .mu.m or less wherein said spherical diameter (Rs) is expressed by an equationEQU Rs (.mu.m)=6/.rho.s which .rho. is a true density (g/cm.sup.3) of a powder, and S is a BET specific surface area of a powder, and an average degree of aggregation (x) of 2 to 10 wherein said average degree of aggregation (x) is expressed by an equationEQU x=Rm/Rs which Rm is a radian diameter observed by a laser scattering method and Rs is a spherical diameter as defined above;(ii) firing the green body at a predetermined firing temperature; said method further comprising controlling the amount of firing shrinkage during the firing step (ii) to a desired value A.sub.1 by heat treating said powder at a temperature T.sub.1 that provides said firing shrinkage A.sub.1 at said predetermined firing temperature, said temperature T.sub.1 being determined based on an established correlation between an amount of firing shrinkage at said predetermined firing temperature and a heat-treatment temperature,said correlation being obtained by the steps ob (a) subjecting samples of a powder (B) having a spherical diameter (Rs) of 1 .mu.m or less and an average degree of aggregation (x) of 2 to 10 to heat treatment before molding respectively at least two different temperatures; said powder (A) having a composition similar to a composition of said powder (B) in such an extent that a total amount of a greatest common content of an individual component common between said powders (A) and (B) in terms of percent is 90% by weight or more, and satisfying such a relation that its spherical diameter is within a range of .+-.30% relative to said spherical diameter (Rs) of said powder (B) and that its average degree of aggregation (x) is within the range from 1/2 fold to 2 fold relative to said average degree of aggregation (x) of said powder (B), and then molding the samples and firing them at said predetermined firing temperatures to obtain firing shrinkage values corresponding to said at least two heat-treatment temperatures, and thereby obtaining a regression line for the correlation between the heat-treatment temperature and the firing shrinkage, (b) subjecting a portion of said powder (A) to be molded in step (i), to heat-treatment before molding at one temperature and molding it and firing it as said predetermined firing temperature to obtain a firing shrinkage value corresponding to said one heat-treatment temperature, and (c) on the basis of the firing shrinkage value obtained in step (b) and the regression line obtained in step (a), establishing said correlation for said powder to be molded in step (i) by assuming that its regression line for the relationship between heat-treatment temperature and firing shrinkage in a graph plotting the regression lines, with respect to the regression line obtained in step (a).