초록 ▼

A powder injection molding and infiltration process. A powder of a skeleton material having a relatively high melting point is mixed with a composite binder to form a mold mixture. The composite binder is comprised of at least two binder materials. The mold mixture is molded into a desired shape in

A powder injection molding and infiltration process. A powder of a skeleton material having a relatively high melting point is mixed with a composite binder to form a mold mixture. The composite binder is comprised of at least two binder materials. The mold mixture is molded into a desired shape in a mold device to produce a molded part. The composite binder is then removed to produce voids in the molded part and the voids are filled by infiltrating an infiltrant comprised of an infiltrant material having a relatively low melting point to produce a composite molded part. In a preferred embodiment the skeleton material is TiB.sub.2 and the infiltrant material is aluminum and the composite binder is comprised of a plastic and a wax. In this embodiment the wax portion of the composite binder is removed using a solvent and the plastic is removed during the infiltration step. The resulting composite part has a TiB.sub.2 skeleton with voids substantially filled with aluminum. This process is especially useful for making light and strong parts with complex shapes such as golf club heads, tools, cutting implements, thermal management products, rocket motor components and bicycle parts. In another preferred embodiment, a golf club head is comprised of three parts: an non-sintered TiB.sub.2 part for the body of the head, a sintered TiB.sub.2 part for the striking surface of the head, and a heavy tungsten part to provide weight for the head. In this embodiment, the aluminum infiltrant substantially fills the voids in all three parts to create a golf club head with optimum characteristics.

대표청구항 ▼

[ We claim:] [1.]1. A powder injection and infiltration process comprising the steps of:A) making a sintered pail comprising interconnected voids, the steps for making said sintered part comprising:i) mixing powder of a first skeleton material with a composite binder comprised of at least two binder

[ We claim:] [1.]1. A powder injection and infiltration process comprising the steps of:A) making a sintered pail comprising interconnected voids, the steps for making said sintered part comprising:i) mixing powder of a first skeleton material with a composite binder comprised of at least two binder materials to form a first mold mixture,ii) molding the mold mixture into a desired shape in a mold device to produce a first molded part,iii) sintering the first molded part to produce said sintered part, andiv) removing the composite binder to produce interconnected voids in said sintered part,B) making a heavy part comprising interconnected voids, the steps for making said heavy part comprising:i) mixing powder of a second skeleton material with a composite binder comprised of at least two binder materials to form a second mold mixture, wherein said second skeleton material is heavier in relation to said first skeleton material,ii) molding the mold mixture into a desired shape in a mold device to produce said heavy part, andiii) removing the composite binder to produce interconnected voids in said heavy part,C) inserting said sintered part and said heavy part into a mold cavity, andD) molding around said sintered part and said heavy part, said steps for said molding comprising:i) mixing powder of a third skeleton material with a composite binder comprised of at least two binder materials to form third mold mixture, wherein said second skeleton material is heavier in relation to said third skeleton material,ii) molding said third mold mixture into a desired shape by inserting said third mold mixture into a mold device comprising said mold cavity to produce a final molded part comprising said third mold mixture, said sintered part and said heavy part,iii) removing the composite binder in said third mold mixture to produce interconnected voids in said third mold mixture, andiv) at least substantially filling the interconnected voids in said final molded part with an infiltrant comprised of an infiltrant material having a relatively low melting point to produce a composite molded part.