초록 ▼

A water vapor-permeable waterproof fabric free from an environmental pollution problem upon being discarded is formed by coating a substrate fiber fabric with a composite coating layer including a lower layer (A) directly formed on the substrate fabric and an upper layer (B) formed on the lower laye

A water vapor-permeable waterproof fabric free from an environmental pollution problem upon being discarded is formed by coating a substrate fiber fabric with a composite coating layer including a lower layer (A) directly formed on the substrate fabric and an upper layer (B) formed on the lower layer (B), wherein the lower and upper layers are formed from one of polyetherester elastomers different from each other and each containing polyalkylene glycol (PAG) residues, and satisfy the following requirements: (a) in the polyetherester elastomer (PEEA), the polyalkylene glycol residues contain 90% by weight or more of polytetramethylene glycol residues; (b) in the polyetherester elastomer (PEEB), the polyalkylene glycol residues contain 50% by weight or more of polyethylene glycol residues; (c) the thickness of the composite coating layer is 5 to 50 μm; and (d) the lower layer (A) is in an amount of 5 to 40% by weight based on the total weight of the composite coating layer.

대표청구항 ▼

1. A water vapor-permeable waterproof fabric comprising: a substrate fabric comprising a fiber material; and a composite coating layer formed on at least a portion of the surfaces of the substrate fabric and containing (A) a lower layer directly bonded to the substrate fabric and (B) an upper la

1. A water vapor-permeable waterproof fabric comprising: a substrate fabric comprising a fiber material; and a composite coating layer formed on at least a portion of the surfaces of the substrate fabric and containing (A) a lower layer directly bonded to the substrate fabric and (B) an upper layer formed on the lower layer, wherein the lower and upper layers (A) and (B) comprise one of two polyetherester elastomers (PEE) different in coating layer-forming property from each other, and each comprising polyalkylene glycol (PAG) residues, alkylene glycol (AG) residues and dicarboxylic acid (DC) residues, and satisfy the following requirements: (a) in the polyetherester elastomer (PEAA) for the lower layer (A), the polyalkylene glycol (PAG) residues contain polytetramethylene glycol residues in a content of 90% by weight or more; (b) in the polyetherester elastomer (PEEB) for the upper layer (B), the polyalkylene glycol (PAG) residues contain polyethylene glycol residues in a content of 50% by weight or more; (c) the thickness of the composite coating layer is in the range of from 5 to 50 μm; and (d) the lower layer (A) is in an amount of 5 to 40% by weight based on the total weight of the composite coating layer including the lower and upper layers (A) and (B), wherein in the cross-section of the water vapor-permeable waterproof fabric at right angles to the surface of the fabric, and in the interface portion between the composite coating layer and the substrate fabric, some of the individual fibers in the substrate fabric are completely coated in an amount of 20 to 1000 fibers per cm along a boundary line between the substrate fabric and the lower layer (A) and appearing in the cross-section, with the polyetherester elastomer (PEAA) for the lower layer (A) to serve as anchor fibers for fixing between the substrate fabric and the lower layer (A) and 20 to 90% of the anchor fibers have peripheral surfaces of which 90% or more in area are spaced from the polyetherester elastomer (PEAA) of the lower layer (A) and are movable from the polyetherester elastomer (PEAA) of the lower layer (A).