초록 ▼

A welding method that enables the joining of at least two dissimilar, metallic alloys to form a weld that is free of cracks is disclosed. The method incorporates a pure (99.00% minimum by weight) nickel fill-wire, integrally assembled into the joint between the two alloyed metals to be joined. The a

A welding method that enables the joining of at least two dissimilar, metallic alloys to form a weld that is free of cracks is disclosed. The method incorporates a pure (99.00% minimum by weight) nickel fill-wire, integrally assembled into the joint between the two alloyed metals to be joined. The alloys joined by this method are an iron-based, low expansivity, gamma-prime strengthened superalloy (i.e., Incoloy.RTM.) and a high carbon, powder metallurgical tool steel high in refractory metal alloying agents (i.e., CPM REX 20). Welding of the joint results in the formation of a nickel rich region within the weld, thus "inoculating" the weld against cracks. The weld joint formed by the method of the present invention can be used in the fabrication of a rotating anode bearing shaft assembly for use in an x-ray generating device.

대표청구항 ▼

1. A bearing shaft assembly, comprising a bearing shaft, a hub, and commercially pure nickel incorporated into the joint formed between the bearing shaft and the hub; wherein the desired amount of the commercially pure nickel in the joint comprises approximately 25 wt % of the joint as determined

1. A bearing shaft assembly, comprising a bearing shaft, a hub, and commercially pure nickel incorporated into the joint formed between the bearing shaft and the hub; wherein the desired amount of the commercially pure nickel in the joint comprises approximately 25 wt % of the joint as determined by Energy Dispersive X-ray Spectrometry (EDS) analysis. 2. The bearing shaft assembly in accordance with claim 1, wherein the hub comprises an iron-based, low expansivity, gamma-prime strengthened superalloy. 3. The bearing shaft assembly in accordance with claim 1, wherein the bearing shaft comprises a high carbon, powder metallurgical, cobalt free tool steel. 4. The bearing shaft assembly in accordance with claim 1, wherein the nickel comprises a formed wire. 5. The bearing shaft assembly in accordance with claim 1, wherein the nickel comprises a preformed washer. 6. The bearing shaft assembly in accordance with claim 1, wherein a sufficient quantity of the commercially pure nickel is present in the joint to obtain an iron-to-nickel-ratio (Fe/Ni) of approximately 2 or less for systems that have a combined wt % of iron and nickel equal to or greater than 75 wt % of the joint as determined by EDS analysis. 7. A bearing shaft assembly, comprising a high carbon, powder metallurgical, cobalt free tool steel bearing shaft, an iron-based, low expansivity, gamma-prime strengthened superalloy hub, and commercially pure nickel incorporated into the joint formed between the shaft and the hub; wherein the desired amount of the commercially pure nickel in the joint comprises approximately 25 wt % of the joint as determined by Energy Dispersive X-ray Spectrometry (EDS) analysis. 8. The bearing shaft assembly in accordance with claim 7, wherein the nickel comprises a formed wire. 9. The bearing shaft assembly in accordance with claim 7, wherein the nickel comprises a preformed washer. 10. The bearing shaft assembly in accordance with claim 7, wherein a sufficient quantity of the commercially pure nickel is present in the joint to obtain an iron-to-nickel-ratio (Fe/Ni) of approximately 2 or less for systems that have a combined wt % of iron and nickel equal to or greater than 75 wt % of the joint as determined by EDS analysis.