초록 ▼

The invention relates to a method for the hydrolytic polymerisation of ε-caprolactam to polyamide-6, comprising a step (a) in which ring opening of part of the ε-caprolactam to the corresponding amino caproic acid is effected in the presence of water and a step (b) in which polyaddition and polycond

The invention relates to a method for the hydrolytic polymerisation of ε-caprolactam to polyamide-6, comprising a step (a) in which ring opening of part of the ε-caprolactam to the corresponding amino caproic acid is effected in the presence of water and a step (b) in which polyaddition and polycondensation are effected under preferably anhydrous reaction conditions, in which at least one of the steps (a) and (b) is carried out in a reactor in which a self-renewing interface between the molten phase and the gas phase with a large surface/volume ratio of the molten phase is effected. The method is preferably effected in an horizontal scraped-surface reactor, since relatively strong mixing of the molten phase can be achieved in these and the molten phase is present in a thin layer, a large gas volume is present having a relatively high partial pressure of the water vapour and the thin layer is constantly renewed by shear forces. The method can be carried out in one reactor, preferably with several reaction zones, or with several reactors in series.

대표청구항 ▼

1. Method for the hydrolytic polymerisation of molten ε-caprolactam to polyamide-6 comprising: (a) reacting at least a portion of the ε-caprolactam with water to form the corresponding amino caproic acid; and (b) performing polyaddition and polycondensation to form polyamide-6; wherein at lea

1. Method for the hydrolytic polymerisation of molten ε-caprolactam to polyamide-6 comprising: (a) reacting at least a portion of the ε-caprolactam with water to form the corresponding amino caproic acid; and (b) performing polyaddition and polycondensation to form polyamide-6; wherein at least one of steps (a) and (b) comprises creating a self-renewing interface between the molten phase and the gas phase, with a surface/volume ratio of the molten phase greater than 10 m-1. 2. Method according to claim 1 wherein the surface/volume ratio of the molten phase is greater than 40 m-1. 3. Method for the hydrolytic polymerisation of molten ε-caprolactam to polyamide-6 comprising: (a) reacting at least a portion of the ε-caprolactam with water to form the corresponding amino caproic acid; and (b) performing polyaddition and polycondensation to form polyamide-6; wherein either step (a) or (b) is performed in a reactor chosen from stirred gas bubble scrubbers, horizontal scraped-surface reactors or packed column reactors. 4. Method according to claim 3 wherein the reactor is an horizontal scraped-surface reactor. 5. Method according to claim 1, wherein a self-renewing interface between the molten phase and the gas phase is created in step (a), with a surface/volume ratio of the molten phase greater than 10 m-1. 6. Method according to claim 5 wherein step (a) further comprises supplying water via the gas phase. 7. Method according to claim 5, wherein step (a) is performed at a gas pressure greater than atmospheric pressure. 8. Method according to claim 5, wherein the gas phase comprises an inert gas and steam. 9. Method according to claim 5, wherein steam is continuously added to the gas phase. 10. Method according to claim 1, wherein a self-renewing interface between the molten phase and the gas phase is created in step (b), with a surface/volume ratio of the molten phase greater than 10 m-1. 11. Method according to claim 10 wherein water is continuously removed from the reactor. 12. Method according to claim 1, wherein a self-renewing interface between the molten phase and the gas phase is created in steps (a) and (b), with a surface/volume ratio of the molten phase greater than 10 m-1. 13. Method according to claim 3, wherein the method is carried out in at least two reactors in series. 14. Method according to claim 1, wherein the method is carried out in one reactor with at least two reaction zones. 15. Method for storing a polyamide melt at a constant viscosity comprising storing the melt in a reactor which creates a self-renewing interface between the melt and a gas phase, with a surface/volume ratio of the molten phase greater than 10 m-1. 16. The method of claim 1, wherein step (b) is performed under anhydrous reaction conditions.