초록 ▼

Construction material from granular material reclaimed from the ash of a municipal waste combustor wherein the ash is subjected to sorting and separating recovered metals, the granular material including particles having a maximum particle diameter of 5 to 40 mm, a U-coefficient of 10 or more, and i

Construction material from granular material reclaimed from the ash of a municipal waste combustor wherein the ash is subjected to sorting and separating recovered metals, the granular material including particles having a maximum particle diameter of 5 to 40 mm, a U-coefficient of 10 or more, and ignition loss of 10% or less in weight and being subjected to at least one heavy metal immobilization agent, preferably phosphoric acid; and a second heavy metal immobilization agent consisting of ferrous sulfate. The ash is further subjected to drying before subjecting the ash to the at least one heavy metal immobilization agent. The ash is further subjected to mulling the material after subjecting the ash to the at least one heavy metal immobilization agent.

대표청구항 ▼

1. Construction material consisting of granular material reclaimed from the ash of a municipal waste combustor wherein the ash is subjected to sorting and separating recovered metals, said granular material including particles having a maximum article diameter of 5 to 50 mm, a U-coefficient of 10 or

1. Construction material consisting of granular material reclaimed from the ash of a municipal waste combustor wherein the ash is subjected to sorting and separating recovered metals, said granular material including particles having a maximum article diameter of 5 to 50 mm, a U-coefficient of 10 or more, and ignition loss of 10% or less in weight and at least one heavy metal immobilization agent being added to said granular material followed by mulling the resulting material. 2. The construction material as defined in claim 1 wherein the heavy metal immobilization agent is phosphoric acid. 3. The construction material as defined in claim 2 wherein the ash is further treated by adding thereto a second heavy metal immobilization agent consisting of ferrous sulfate. 4. The construction material as defined in claim 1 wherein the ash is treated by adding thereto two heavy metal immobilization agents comprising phosphoric acid and ferrous sulfate. 5. The construction material as defined in claim 1 wherein the ash is further subjected to drying. 6. The construction material as defined in claim 5 wherein the ash is further subjected to drying before the addition of at least one heavy metal immobilization agent. 7. The construction material as defined in claim 1 wherein the ash is further subjected to drying before adding said at least one heavy metal immobilization agent. 8. The construction material as defined in claim 1 wherein the ash is sequentially subjected to (1) sorting according to particle size; (2) comminuting particles greater than 40 mm in size to a lesser size; (3) blending the particles of various sorted sizes to create a U-coefficient of 10 or greater; (4) drying; (5) the addition of at least one heavy metal immobilization agent; and (7) mulling. 9. The construction material as defined in claim 8 wherein the ash is further treated by the addition of a second heavy metal immobilization agent. 10. The construction material as defined in claim 8 wherein said at least one heavy metal immobilization agent is phosphoric acid. 11. The construction material as defined in claim 8 wherein said at least one heavy metal immobilization agent is ferrous sulfate. 12. The construction material as defined in claim 8 wherein said granular material includes non-ferrous metals.