초록 ▼

A part is manufactured from a composite material containing an aluminum alloy as a metal matrix. Blanks are prepared from a billet of the composite material, and worked on in a press, while they are held at a temperature ranging from the solidus temperature, Ta, of the aluminum alloy minus 50 (Ta-50

A part is manufactured from a composite material containing an aluminum alloy as a metal matrix. Blanks are prepared from a billet of the composite material, and worked on in a press, while they are held at a temperature ranging from the solidus temperature, Ta, of the aluminum alloy minus 50 (Ta-50) deg. C. to Ta deg. C. At a temperature below (Ta-50), the blanks have too high a resistance to plastic deformation to be easily worked on. At a temperature over Ta, a liquid phase is produced and makes the blanks likely to crack easily during plastic deformation.

대표청구항 ▼

1. A process for manufacturing a part of an aluminum-based composite material comprising the steps of: preparing an aluminum-based composite material containing an aluminum alloy and having an appropriate diameter; cutting the material into a plurality of blanks each having an appropriate thickn

1. A process for manufacturing a part of an aluminum-based composite material comprising the steps of: preparing an aluminum-based composite material containing an aluminum alloy and having an appropriate diameter; cutting the material into a plurality of blanks each having an appropriate thickness; heating the blanks to an appropriate temperature ranging from (Ta-40)° C. to (Ta-33)° C. wherein Ta is the solidus temperature; and press forming each blank, while holding the blank at the appropriate temperature wherein each blank is press formed at a compressibility not less than 30%. 2. The process according to claim 1, wherein the composite material is prepared by reducing a porous reinforcing material composed of a metal oxide in the presence of magnesium nitride to expose a metal on at least a part of the reinforcing material and impregnating the reinforcing material with a molten aluminum alloy. 3. The process according to claim 1, wherein the blanks are heated by a heater embedded in a die.