초록 ▼

A coating formulation for application to surfaces associated with combustion, such as fuel injectors, and surfaces subjected to elevated temperatures, such as fuel supply components, to prevent the deposition at high temperatures of carbon or graphite on such surfaces, such as stainless steel and al

A coating formulation for application to surfaces associated with combustion, such as fuel injectors, and surfaces subjected to elevated temperatures, such as fuel supply components, to prevent the deposition at high temperatures of carbon or graphite on such surfaces, such as stainless steel and alloyed steel compositions. The coating formulation forms a thin layer of polymer coating on the surface by chemical grafting involving the use of a graft initiator to create active bonding sites, on the metal surface, for the silicone-based prepolymer to undergo polymerization on the metal surface. The bonding and polymerization are completed in a single application process without using complex equipment. The coating and process helps surfaces associated with combustion and surfaces subjected to elevated temperature reduce carbon or coke formation at temperatures up to 700° F. and thereby improves the durability and performance of those surfaces.

대표청구항 ▼

1. A deposit-resistant fuel-supply or injection component, comprising said component having a coating on at least one surface thereof to prevent carbon or coke formation at high temperatures, said coating comprising a polysiloxane polymer which is applied to the surface as a solution and is graft po

1. A deposit-resistant fuel-supply or injection component, comprising said component having a coating on at least one surface thereof to prevent carbon or coke formation at high temperatures, said coating comprising a polysiloxane polymer which is applied to the surface as a solution and is graft polymerized to the surface of the component to thereby resist deposit of carbon or coke. 2. The component of claim 1 wherein the polysiloxane polymer is a methylphenylpolysiloxane polymer. 3. The component of claim 1 wherein the polysiloxane polymer is applied to the surface as a solution of a polysiloxane prepolymer, a silane monomer and a vinyl monomer. 4. The component of claim 3 wherein the vinyl monomer is selected from the group consisting of hexafluoro butyl methacrylate monomer and trifluoro ethyl methacrylate monomer. 5. The component of claim 1 wherein the polysiloxane polymer is applied to the surface as a liquid formulation containing a mixture of siloxane prepolymer, a graft initiator, and a catalyst. 6. The component of claim 1 wherein the surface is a stainless steel or a stainless steel alloy. 7. The component of claim 1 wherein the coating is effective at temperatures from about 300° F. to about 700° F. 8. The component of claim 1 wherein the polymer coating is about 0.0005 to about 0.003 inch thick. 9. The component of claim 1 wherein the graft polymerization is initiated by a metal ion selected from the group consisting of Fe+++,Fe++,Ag+,Co++,Ni++,Ce+++,and Cu++. 10. The component of claim 1 wherein the polysiloxane polymer is applied to the surface as a liquid formulation containing a mixture of siloxane prepolymer, a silane, a vinyl monomer, a graft initiator, a catalyst, a solvent, and additives. 11. The component of claim 1 wherein said polysiloxane polymer is obtained by polymerizing a polysiloxane prepolymer with minor amounts of a silane monomer and a vinyl monomer.