초록 ▼

Applicant has developed an improved adsorbent useful in removing contaminants from various hydrocarbon streams. The adsorbent contains a zeolite, an alumina and a metal component. The metal component (Madd) is present in an amount at least 10 mole % the stoichiometric amount of metal (M) (expressed

Applicant has developed an improved adsorbent useful in removing contaminants from various hydrocarbon streams. The adsorbent contains a zeolite, an alumina and a metal component. The metal component (Madd) is present in an amount at least 10 mole % the stoichiometric amount of metal (M) (expressed as the oxide) needed to balance the negative charge of the zeolite lattice. In a specific application an adsorbent comprising zeolite X, alumina and sodium is used to purify an ethylene stream in order to remove CO2,H2S, methanol, and other S-- and O-- containing compounds.

대표청구항 ▼

1. A solid shaped adsorbent for purifying hydrocarbon streams comprising an alumina component, a zeolite component and a metal component (Madd), the metal component present in an amount from about 0.015 to 0.08 moles of the metal as the oxide per 100 g of adsorbent and where the alumina is present i

1. A solid shaped adsorbent for purifying hydrocarbon streams comprising an alumina component, a zeolite component and a metal component (Madd), the metal component present in an amount from about 0.015 to 0.08 moles of the metal as the oxide per 100 g of adsorbent and where the alumina is present in an amount from about 40 to about 90 wt. % of the adsorbent. 2. The adsorbent of claim 1 where the zeolite is selected from the group consisting of zeolite X, zeolite Y, zeolite A and mixtures thereof. 3. The adsorbent of claim 2 where the zeolite is zeolite X. 4. The adsorbent of claim 1 where the metal component (Madd) is an alkali metal selected from the group consisting of sodium, potassium, lithium, rubidium, cesium and mixtures thereof. 5. The adsorbent of claim 4 where the metal component is sodium. 6. The adsorbent of claim 1 where the zeolite is present in an amount from about 5 to about 55 wt. % of the adsorbent. 7. A process for preparing a solid shaped adsorbent for purifying hydrocarbon streams comprising an alumina component, a zeolite component and a metal component (Madd) selected from the group consisting of sodium, potassium, lithium, rubidium, cesium and mixtures thereof the metal component present in an amount from about 0.015 to about 0.08 moles of metal as the oxide per 100 g of adsorbent and where the alumina is present in an amount from about 40 to about 90 wt. % of the adsorbent; the process comprising forming a shaped article by combining an alumina component, a zeolite component and a metal component precursor in any order to form a shaped article, curing the shaped article at curing conditions to give a cured shaped article and activating the cured article at activation conditions to give the solid shaped adsorbent. 8. The process of claim 7 where the zeolite component is selected from the group consisting of zeolite X, zeolite Y, zeolite A and mixtures thereof. 9. The process of claim 7 where the metal component precursor is selected from the carboxylate, carbonate and hydroxide compound of the metal component. 10. The process of claim 9 where the carboxylate is an acetate compound of the metal component. 11. The process of claim 7 where the shaped article is selected from the group consisting of extrudes, pills, tablets, spheres and irregular shaped particles. 12. The process of claim 7 where the curing conditions include a temperature of about ambient to about 200° C. and a time of about 5 minutes to about 25 hours. 13. The process of claim 7 where the activation conditions include a temperature of about 275° C. to about 600° C. and a time of about 5 to about 70 minutes. 14. The process of claim 7 where the alumina, zeolite and an aqueous solution of the metal precursor are mixed and formed into a shaped article. 15. The process of claim 7 where the alumina and zeolite components are formed into a shaped article and then contacted with an aqueous solution containing a metal precursor. 16. The process of claim 7 where alumina powder, zeolite powder and metal precursor powder are combined and formed into a shaped article.