초록 ▼

An alkali-free accelerator for sprayed concrete is prepared by dissolving aluminium sulphate and amorphous aluminium hydroxide in water which optionally contains one amine, and optionally adding at least one stabiliser, selected from hydroxycarboxylic acid and phosphoric acids and non-alkaline salts

An alkali-free accelerator for sprayed concrete is prepared by dissolving aluminium sulphate and amorphous aluminium hydroxide in water which optionally contains one amine, and optionally adding at least one stabiliser, selected from hydroxycarboxylic acid and phosphoric acids and non-alkaline salts thereof, and at least one defoaming agent.

대표청구항 ▼

1. A method of preparing an accelerator for sprayed concrete, consisting essentially of the steps of: (i) dissolving aluminum sulphate and aluminum hydroxide in water, containing at least one amine dissolved therein, to give a clear solution; and (ii) optionally adding at least one of at least s

1. A method of preparing an accelerator for sprayed concrete, consisting essentially of the steps of: (i) dissolving aluminum sulphate and aluminum hydroxide in water, containing at least one amine dissolved therein, to give a clear solution; and (ii) optionally adding at least one of at least stabilizer and at least one defoaming agent; wherein the proportions of ingredients present being such that the final product contains from 3%-12% by weight of aluminum sulphate (measured as Al2O3), up to 30% by weight of amorphous aluminum hydroxide, 4-7% by weight amine, up to 3% by weight defoaming agent and up to 0.06 mol/kg, stabilizer, being selected from the group consisting of hydroxycarboxylic acids, phosphoric acids and non-alkaline salts of phosphoric acids. 2. A method according to claim 1, wherein there is added at least one of an at least one stabilizer and at least one defoaming agent. 3. A method according to claim 2, wherein there is added at least one stabilizer. 4. A method according to claim 2, wherein there is added at least one defoaming agent. 5. A method according to claim 4, wherein the defoaming agent contains no silicone and is present to a maximum extent of 3%. 6. A method according to claim 1, wherein the stabilizer is at least one hydroxycarboxylic acid. 7. A method according to claim 1, wherein a clear solution is prepared by the steps of (i) dissolving aluminum sulphate in water, containing at least one amine dissolved therein; and (ii) dissolving amorphous aluminum hydroxide in the solution of (i) until a clear solution is obtained. 8. A method according to claim 7, wherein there is added to the clear solution at least one of (a) at least one defoaming agent, and (b) at least one stabilizer selected from the group consisting of hydroxycarboxylic acids, phosphoric acids and non-alkaline salts of phosphoric acids, and hydroxycarboxylic acids. 9. An accelerator for use with sprayed concrete, prepared by a process according to claim 1. 10. The method of claim 1, wherein the at least one amine is an alkanolamine. 11. The method of claim 10, wherein the alkanolamine is selected from the group consisting of diglycolamine, diethanolamine and triethanolamine. 12. The method of claim 11, wherein the alkanolamine is diethanolamine. 13. An accelerator for use with sprayed concrete, prepared by a process according to claim 12.