초록 ▼

Monazite or xenotime-based blanket coatings that stiffen ceramic fabrics without causing embrittlement at temperatures of at least as high as 2400° F. are provided. Methods for making the coatings are also provided. The methods comprise the synthesis of high purity, monazite and xenotime powders wit

Monazite or xenotime-based blanket coatings that stiffen ceramic fabrics without causing embrittlement at temperatures of at least as high as 2400° F. are provided. Methods for making the coatings are also provided. The methods comprise the synthesis of high purity, monazite and xenotime powders with the stoichiometric ratio of metal to phosphorous of about 1:1.

대표청구항 ▼

1. A method for producing a monazite or xenotime comprising: (a) forming a precipitate from an aqueous solution comprising a lanthanide salt and a phosphate; (b) washing the precipitate with water; and (c) washing the precipitate with an organic base with a pH greater than about 12. 2. The me

1. A method for producing a monazite or xenotime comprising: (a) forming a precipitate from an aqueous solution comprising a lanthanide salt and a phosphate; (b) washing the precipitate with water; and (c) washing the precipitate with an organic base with a pH greater than about 12. 2. The method of claim 1 wherein the lanthanide salt is a lanthanum salt, cerium salt, yttrium salt or combinations thereof. 3. The method of claim 1 wherein the organic base is tetramethylammonium hydroxide. 4. A monazite or xenotime produced by the method of claim 1, wherein the monazite or xenotime has a stoichiometric ratio between a metal of the monazite or xenotime and a phosphate of the monazite or xenotime of about 1:1. 5. The method of claim 1 wherein the step of washing the precipitate with the organic base further comprises washing at a temperature from about 80° C. to about 100° C. 6. A method for producing a monazite- or xenotime-based coating, comprising: (a) forming a precipitate from an aqueous solution comprising a lanthanide salt and a phosphate; (b) washing the precipitate with water; (c) washing the precipitate with an organic base with a pH greater than about 12; (d) calcining the precipitate of step (c); (e) milling the calcined precipitate of step (d) to form a powder; and (f) forming an aqueous slurry comprising the powder of step (e) and inert powder. 7. The method of claim 6 wherein the lanthanide salt is a lanthanum salt, cerium salt, yttrium salt, or combinations thereof. 8. The method of claim 6 wherein the organic base is tetramethylammonium hydroxide. 9. The method of claim 6 wherein the inert powder is alumina, zirconia, YAG, mullite, or combinations thereof. 10. The method of claim 6 wherein the aqueous slurry of step (f) further comprises an SiC additive. 11. The method of claim 6 further comprising: (g) applying the aqueous slurry onto a fabric of woven ceramic fibers. 12. The method of claim 6 wherein the step of washing the precipitate with the organic base further comprises washing at a temperature from about 80° C. to about 100° C. 13. A monazite- or xenotime coating composition comprising a high purity monazite or xenotime, wherein the monazite or xenotime is synthesized by forming a precipitate from an aqueous solution comprising a lanthanide salt and a phosphate, washing the precipitate with water, and washing the precipitate with an organic base with a pH of greater than about 12, the coating composition further comprising an Inert powder. 14. The coating composition of claim 13 wherein the inert powder is Al2O3,zirconia, YAG, mullite, or compositions thereof. 15. A monazite- or xenotime coating composition comprising a high purity monazite or xenotime, wherein the monazite or xenotime is synthesized by forming a precipitate from an aqueous solution comprising a lanthanide salt and a phosphate, washing the precipitate with water, and washing the precipitate with an organic base with a pH of greater than about 12, the coating composition further comprising SiC additives. 16. The coating composition of claims 13 or 15 wherein the lanthanide salt is a lanthanum salt, cerium salt, yttrium salt, or combinations thereof. 17. The coating composition of claims 13 or 15 wherein the organic base is tetramethylammonium hydroxide. 18. The coating composition of claims 13 or 15 wherein the step of washing the precipitate with the organic base further comprises washing at a temperature from about 80° C. to 100° C.