Substrate glass for optical interference filters with minimal wave length shift
원문보기
IPC분류정보
국가/구분
United States(US) Patent
등록
국제특허분류(IPC7판)
C03C-003/085
C03C-003/087
C03C-003/095
출원번호
US-0929688
(2001-08-14)
발명자
/ 주소
Lin, Jacob W.
출원인 / 주소
OptoElectronics International, Inc., Lin
Yeong C.
대리인 / 주소
Chapin, William L.
인용정보
피인용 횟수 :
8인용 특허 :
10
초록▼
A silicate based composition for optical glass used as a substrate for thin film optical interference filters having a stable transmission band center wavelength and bandwidth has a relatively high coefficient of thermal expansion, high Young's modulus and high optical transmittance in the near infr
A silicate based composition for optical glass used as a substrate for thin film optical interference filters having a stable transmission band center wavelength and bandwidth has a relatively high coefficient of thermal expansion, high Young's modulus and high optical transmittance in the near infrared (NIR) wavelength range of about 950 nm to about 1600 nm. The coefficient of thermal expansion of the glass composition is adjustable to particular values to result in minimal wavelength shift in filters made by depositing thin films of particular dielectric materials onto a substrate made of the glass, the composition being varied from a preferred baseline composition consisting of about 43.2% SiO2, 7% Al2O3, 12.7% CaO, 7.3% SrO, 7.8% Li2O, 13.2% Na2O, 8.0% K2O, 0.7% ZrO, and 0.1% Sb2O3, the baseline composition having a coefficient of thermal expansion of about 112×10-7/° C. over the temperature range of -30° C. to +70° C., a Young's modulus E of 88.3 Gpa, and an optical transmittance of 90.9% at 1550 nm for an 8 mm thick sample plate.
대표청구항▼
1. Silicate glass for use as a substrate for optical interference filters comprising in mole percentages the following ingredients: a. SiO2: approximately 43.2%, b. Al2O3: approximately 7.0%, c. CaO: approximately 12.7%, d. SrO: approximately 7.3%, e. Li2O: approximately 7.8%, f. Na2O: appro
1. Silicate glass for use as a substrate for optical interference filters comprising in mole percentages the following ingredients: a. SiO2: approximately 43.2%, b. Al2O3: approximately 7.0%, c. CaO: approximately 12.7%, d. SrO: approximately 7.3%, e. Li2O: approximately 7.8%, f. Na2O: approximately 13.2%, g. K2O: approximately 8.0%, h. ZnO: approximately 0.7%, i. Sb2O3,As2O3approximately 0.1 total. 2. The glass as defined in claim 1 further defined as having a coefficient of thermal expansion lying in the approximate range between about 91×10-7/° C. and about 120×10-7/° C. 3. The glass as defined in claim 1 further defined as having a Young's modulus of greater than 80 Gpa. 4. The glass as defined in claim 1 further defined as having an optical transmission at 1550 nm of greater than about 90% for a plate thickness of about 8 mm. 5. Silicate glass for use as a substrate for optical interference filters comprising in mole percentages the following ingredients: a. SiO2: approximately 52% to about 58%, b. La2O3: Approximately 3.0% to about 3.3%, c. Alkaline metal oxides: approximately 25% to about 28%, d. Alkaline earth oxides: approximately 10% to about 19%, e. Non-color generating heavier metal oxides: approximately 0% to about 20%. 6. Silicate glass for use as a substrate for optical interference filters comprising in mole percentages the following ingredients: a. SiO2: approximately 47% to about 51%, b. (Al2O3): approximately 1.0% to about 8.0%, c. Alkaline metal oxides: approximately 26% to about 29%, d. Alkaline earth oxides: approximately 18% to about 19%, e. Non-color generating heavier metal oxides: approximately 0% to about 20%. 7. Silicate glass for use as a substrate for optical interference filters comprising in mole percentages the following ingredients: a. SiO2: approximately 50%, b. (Al2O3,La2O3): approximately 3.0%, c. Alkaline metal oxides: approximately 28%, d. Alkaline earth oxides: approximately 19%, e. Non-color generating heavier metal oxides: approximately 0% to about 20%.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (10)
Speit Burkhard,DEX, Chemically prestressable aluminosilicate glass and products made therefrom.
Akihiro Koyama JP; Shoichi Kishimoto JP; Junji Kurachi JP; Nobuyuki Yamamoto JP, Glass composition and substrate for information recording media comprising the same.
Koyama Akihiro,JPX ; Kishimoto Shoichi,JPX ; Kurachi Junji,JPX ; Yamamoto Nobuyuki,JPX, Glass composition and substrate for information recording media comprising the same.
Kurachi Junji,JPX ; Koyama Akihiro,JPX ; Kishimoto Shoichi,JPX ; Yamamoto Nobuyuki,JPX, Glass composition and substrate for information recording media comprising the same.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.