초록 ▼

A process produces a glass overcladding tube from a silica gel body. The process includes passing the gel body through a hot zone under conditions that cause partial sintering of the gel body and repassing the gel body through the hot zone under conditions that further sinter the gel body into a gla

A process produces a glass overcladding tube from a silica gel body. The process includes passing the gel body through a hot zone under conditions that cause partial sintering of the gel body and repassing the gel body through the hot zone under conditions that further sinter the gel body into a glass overcladding tube.

대표청구항 ▼

1. A process, comprising: passing a silica gel body through a hot zone under conditions that cause partial sintering of the gel body such that pore closure in the gel body and shrinkage of a linear dimension of the gel body by at least one percent are produced; and then, repassing the gel body

1. A process, comprising: passing a silica gel body through a hot zone under conditions that cause partial sintering of the gel body such that pore closure in the gel body and shrinkage of a linear dimension of the gel body by at least one percent are produced; and then, repassing the gel body through the hot zone under conditions that further sinter the gel body such that further pore closure in the gel body and further shrinkage of a linear dimension of the gel body by at least one percent are produced. 2. The process of claim 1, wherein each of the passing and the repassing comprises: vertically moving the gel body through the hot zone in a direction of gravity or in a direction opposite to gravity. 3. The process of claim 1, further comprising: passing the gel body through the hot zone under conditions that significantly purify the gel body without shrinking the gel body. 4. The process of claim 3, further comprising: treating the silica gel body to cause dehydroxylation prior to performing the passing a silica gel body through a hot zone under conditions that cause partial sintering of the gel body. 5. The process of claim 1, wherein the gel body has a tubular shape; the passing causes at least a 1 percent shrinkage in a diameter of the gel body; and the repassing causes at least another 1 percent shrinkage in the diameter of the gel body. 6. The process of claim 5, wherein one of the passing and the repassing causes at least a 5 percent shrinkage of the diameter of the gel body.7. The process of claim 1, further comprising: forming a sol comprising silica particles; and casting the gel body from the sol. 8. The process of claim 1, wherein both the passing and repassing include vertically moving the hot zone along the gel body in a direction, the direction being along or opposite to a direction of gravity.9. The process of claim 8, wherein the passing and repassing include regulating a temperature of the hot zone to be at least 1300° C.10. The process of claim 9, wherein the passing and repassing produce a preform having a level of [OH] impurities of less than 2 parts per million.11. The process of claim 8, further comprising: inserting a core-cladding rod into the further sintered gel body; and heat collapsing the further sintered gel body onto the rod to produce a preform. 12. The process of claim 1, wherein the repassing includes producing a transparent silica-glass overcladding tube.13. A process, comprising: subjecting one end of a cylindrical silica gel body to a hot zone until the end is at least partially sintered in a manner that produces both pore closure in the end and shrinkage of a linear dimension of the end by at least 1%; and then, vertically passing the whole gel body through the hot zone to sinter in a manner that produces pore closure in the gel body and shrinkage of a linear dimension in the gel body, the vertically passing causing the end to enter the hot zone last. 14. The process of claim 13, wherein the subjecting causes the end to have a diameter at least 1 percent smaller than the diameter of the end prior to the subjecting.15. The process of claim 14, wherein the vertically passing includes raising the gel body through the hot zone in a direction opposite to the direction of gravity.16. The process of claim 13, further comprising: producing the silica gel body from a sol comprising silica particles; and wherein the gel body has a tubular form. 17. The process of claim 13, wherein the passing produces a silica glass tube.