초록 ▼

The present invention relates to a process for recovery of nickel and alumina from spent catalyst by direct leaching with sulphuric acid in presence of small amount of an additive. The invention is useful for recovery of both nickel and sources of nickel and therefore important from the view of envi

The present invention relates to a process for recovery of nickel and alumina from spent catalyst by direct leaching with sulphuric acid in presence of small amount of an additive. The invention is useful for recovery of both nickel and sources of nickel and therefore important from the view of environmental protection, resource recycling and conservation.

대표청구항 ▼

1. A process for extraction of nickel from spent nickel catalyst which comprises i) adding a persulphate-based additive along with fine sized nickel catalyst in a sulphuric acid solution and stirring by a magnetic needle/glass stirrer and maintaining the solid liquid ratio in the range of ½-{fract

1. A process for extraction of nickel from spent nickel catalyst which comprises i) adding a persulphate-based additive along with fine sized nickel catalyst in a sulphuric acid solution and stirring by a magnetic needle/glass stirrer and maintaining the solid liquid ratio in the range of ½-{fraction (1/10)} (wt. in grams/vol. in mL) to obtain a slurry, ii) keeping the temperature of the slurry obtained in step (i) in the range of 40 to 100° C. for a period of 0.5 to 6 h, iii) allowing the slurry to settle and then filtering the slurry to obtain (a) a leach liquor containing nickel and (b) an alumina as a solid residue, iv) washing the solid residue to remove entrapped liquor and drying at 110-120° C. to get a by-product containing high alumina, v) purifying the leach liquor by precipitating iron and other impurities using lime and filtering to obtain a pure nickel sulphate solution, vi) crystallizing or precipitating the leach liquors to obtain nickel sulphate crystal and nickel hydroxide, and vii) reducing nickel hydroxide to obtain nickel metal powder or nickel oxide. 2. A process as claimed in claim 1 wherein the spent nickel catalyst used is selected from nickel catalyst having particle size in the range of 38 &mgr;m-211 &mgr;m and has a composition in range Ni:5-20%, Fe 0.1-1%, Al2O3: 70-90%, and SO2: 0-6%.3. A process as claimed in claim 1 wherein the persulphate-based additive is selected from persulphate salts of sodium, potassium and ammonium and has a salt to catalyst concentration in the range of 0.25-4% (w/w).4. A process as claimed in claim 1 wherein the sulphuric acid is of commercial grade and has concentration in the range of 2-12% (v/v).5. A process as claimed in claim 1 wherein the concentration of the pulp in the slurry in step (i) is in the range of 10-100%.