초록 ▼

A method for producing a metallic honeycomb configuration is described. The method includes forming a honeycomb body by stacking and/or winding layers of steel sheet containing chromium and aluminum resulting in the honeycomb body having channels through which a fluid can flow. The honeycomb body is

A method for producing a metallic honeycomb configuration is described. The method includes forming a honeycomb body by stacking and/or winding layers of steel sheet containing chromium and aluminum resulting in the honeycomb body having channels through which a fluid can flow. The honeycomb body is introduced into a tubular jacket. Connections are formed between neighboring layers of steel sheet by thermal treatment. The honeycomb body is then cooled down. It is preferred for the layers of steel sheet to be provided with a rolling oil having a high carbon content before the forming of the honeycomb body, with the effect that a layer of carbon enhancing the sintering process is formed in the thermal treatment. The number of connections produced in individual regions can be further influenced by selective introduction of stresses or by stress relief.

대표청구항 ▼

1. A method for producing a metallic honeycomb configuration, which comprises the following steps: providing layers of steel sheet each having a thickness being at most equal to 35 &mgr;m and containing chromium and aluminum with a rolling oil during a cold rolling of the layers of steel sheet and

1. A method for producing a metallic honeycomb configuration, which comprises the following steps: providing layers of steel sheet each having a thickness being at most equal to 35 &mgr;m and containing chromium and aluminum with a rolling oil during a cold rolling of the layers of steel sheet and, as a result of a composition and additives added to the layers of steel sheet, a carbon-rich layer forming on a surface of the layers of steel sheet if heated, at least some of the layers of steel sheet being structured layers of steel sheet; forming a honeycomb body by at least one of stacking and winding the layers of steel sheet for forming channels in the honeycomb body through which a fluid can flow; introducing the honeycomb body into a tubular jacket; forming connections between neighboring layers of steel sheet by a thermal treatment in which the honeycomb body is heated up to over 1100° C.; and cooling down the honeycomb body, with an average temperature transient of at least 25 K/min. 2. The method according to claim 1, which comprises carrying out the thermal treatment in one of a partial vacuum and a vacuum.3. The method according to claim 1, which comprises mixing in a fine powdered graphite with the rolling oil as an additive, in order to increase a carbon content.4. The method according to claim 1, which comprises selectively stress relieving the honeycomb body, at least in subregions, by one of flexing and hammering, before performing the thermal treatment, in order to achieve a high and uniform connecting quality of touching locations in the subregions.5. The method according to claim 4, which comprises forming the honeycomb body as a body with a multiplicity of the layers of steel sheet running outward in one of a spiral and an involute form, the body undergoing selective introduction of at least one of stresses and flexing in an outer region to give the body a stress profile in which more connections are produced in the outer region between touching locations of the layers of steel sheet than in an inner region of a cross section of the body.6. The method according to claim 1, which comprises performing the thermal treatment by annealing the layers of steel sheet of the honeycomb body.7. The method according to claim 1, which comprises heating the honeycomb body in the range of 1150° C. to 1190° C. during the thermal treatment.8. The method according to claim 1, which comprises performing the cooling step at the average temperature transient of 30 K/min.