초록 ▼

Carbon-silicon carbide brake preforms are manufactured by carbonizing a blend of carbon (e.g., polyacrylonitrile) fibers and thermosetting pitch resin, optionally along with a lubricant such as graphite, to provide an intermediate product having open porosity and subsequently filling the pores of th

Carbon-silicon carbide brake preforms are manufactured by carbonizing a blend of carbon (e.g., polyacrylonitrile) fibers and thermosetting pitch resin, optionally along with a lubricant such as graphite, to provide an intermediate product having open porosity and subsequently filling the pores of the intermediate product with silicon by a melt infiltration process. Molded articles that consist principally of carbon, that have relatively high strength and resistance to decomposition by frictional heat, and that are suitable for melt infiltration with silicon, are produced by, e.g.: coating randomly oriented polyacrylonitrile-derived carbon fibers, optionally mixed with finely divided carbon powder, with a thermosetting blend of (a) pitch and (b) an organic medium, at an elevated temperature to form a viscous molding compound; molding the compound at a low pressure and elevated temperature so that a solid compact is obtained; stripping a molded article made of said compound from the mold; optionally heating the molded article at gradually increasing temperatures to insure complete condensation within the article; and carbonizing the condensed molded article in an inert atmosphere at gradually increasing temperatures to produce a molded C/C intermediate article suitable for melt-infiltration with silicon. The preforms may be configured in the form of a disc brake rotor or a disc brake pad.

대표청구항 ▼

1. A friction article comprising a compressed and charred mixture of 30-70 parts by weight of a C/SiC friction material and 30-70 parts by weight of carbonized organic fibers protected by pitch-based resin char. 2. A friction article comprising a compressed and charred mixture of 30-70 parts by weig

1. A friction article comprising a compressed and charred mixture of 30-70 parts by weight of a C/SiC friction material and 30-70 parts by weight of carbonized organic fibers protected by pitch-based resin char. 2. A friction article comprising a compressed and charred mixture of 30-70 parts by weight of a C/SiC friction material, 0-30 parts by weight of a friction-modifying constituent, and 20-45 parts by weight of carbonized organic fibers protected by pitch-based resin char. 3. The friction article of claim 2, wherein said friction-modifying constituent is a graphite powder.4. The friction article of one of claims 1-3, wherein said carbonized organic fibers are selected from the group consisting of carbonized cellulose, rayon, and polyacrylonitrile fibers.5. The friction article of claim 4, wherein said carbonized organic fibers are carbonized polyacrylonitrile fibers.6. A C/SiC preform comprising a porous matrix of carbonized polyacrylonitrile fibers and pitch-based resin char, wherein the pores of the matrix are filled and reacted with metallic silicon. 7. The C/SiC preform of claim 6, comprising a porous matrix of carbonized, randomly oriented polyacrylonitrile fibers, graphite powder, and pitch-based resin char, wherein the pores of the matrix are filled and reacted with metallic silicon.8. The C/SiC preform of one of claims 6 or7, wherein pitch-resin char forms a continuous layer around carbon fibers resulting from carbonization of polyacrylonitrile fibers and wherein said layer is impermeable to molten silicon.9. A C/SiC preform manufactured by carbonizing a blend of polyacrylonitrile fibers and a pitch tar solution to provide an intermediate product having open porosity and subsequently filling the pores with silicon in a melt infiltration process. 10. The C/SiC friction article of claim 1 or2, configured in the form of a disc brake rotor or a disc brake pad.11. A disc braking system comprising a C/SIC rotor or C/SiC pad manufactured from a friction article of claim 1 or2.