초록 ▼

The present invention describes a process for manufacture of high iron hydraulic cement clinker in production of cement and cementation binder for application in construction activity and in metallurgical industry for sintering of iron ore fines and making cold bonded briquettes and pellets. The pro

The present invention describes a process for manufacture of high iron hydraulic cement clinker in production of cement and cementation binder for application in construction activity and in metallurgical industry for sintering of iron ore fines and making cold bonded briquettes and pellets. The process is cost effective and flexible for utilization of wide varieties of raw material consisting of lime and iron in production of high iron cements for different applications.

대표청구항 ▼

1. A process for the manufacture of high iron hydraulic cement clinker wherein Fe 2 O 3 is at least 33% using a down draft sintering technique which comprises:preparing a homogenous raw mixture of raw materials selected from limestone, lime, lime sludge, lime bearing solid wastes, iron ore, slime

1. A process for the manufacture of high iron hydraulic cement clinker wherein Fe 2 O 3 is at least 33% using a down draft sintering technique which comprises:preparing a homogenous raw mixture of raw materials selected from limestone, lime, lime sludge, lime bearing solid wastes, iron ore, slime red mud, ferruginuous bauxite, laterite, clay, iron oxide containing metallurgical and chemical wastes, slag, coke breeze, coal char, carbonaceous sludge, carbon bearing solid wastes and any mixture thereof, wherein the chemical ratio of CaO/(Al 2 O 3 +Fe 2 O 3 ), SiO 2 /(Al 2 O 3 +Fe 2 O 3 ) and (Al 2 O 3 +Fe 2 O 3 ) in the homogenized raw mixture is between 1.3 to 2.5, 0.2 to 0.5 and 0.25 to 0.8 respectively, with the content of Fe 2 O 3 in the homogenized raw mixture being in the range of less than 40% and the content of solid carbon in the homogenized raw mixture being in the range of between 4 to 12%,pelleting the resultant homogenized raw mixture in the presence of water to prepare granulated particles,sintering and cooling the pelletized granulated particles by down draft sintering technique to convert into clinker,grinding the clinker particles with and without gypsum to make high iron hydraulic cements and binders for different applications. 2. A process according to claim 1 wherein the homogeneous raw mixture is prepared in semi-wet or dry form by blending or grinding depending on the particle fineness of the raw materials. 3. A process according to claim 1 wherein the particle fineness of the homogenized raw mixture is below 150 mesh (100 micron) size. 4. A process according to claim 1 wherein pelleting of the homogenized mixture is done in the in presence of water to make granulated particles below 15 mm in size and to consist 8 to 15% water. 5. A process according to claim 1 wherein the sintering of the granulated particles is done at a temperature in the range of 1050 to 1450° C. for conversion into clinker by down draft sintering, wherein an operating condition consisting of 300 to 600 mm bed height of the granulated particle, 200 to 800 mm water gauge (WG) air suction pressure below the bed, and 15 to 20 mm vertical sintering speed from top to bottom of the bed is maintained. 6. A process according to claim 1 wherein the product obtained is cooled between 200 to 1000° C. and 400 to 600° C. depending on the granulated particle size. 7. A process according to claim 1 wherein the both sintering and cooling operation in cement clinker formation is within the bed itself and is done in a period of 15 to 30 minutes. 8. A process according to claim 1 wherein the sintering hearth is free of refractory lining and attached to the sintering hearth are scrubbers for removal of hot gas carrying dust particles to control pollution during the sintering operation. 9. A process according to claim 1 wherein the clinkerised lumpy aggregates are crushed and then ground with or without gypsum and other additives to make cements and binders for different applications. 10. A process according to claim 1 wherein a mineralizing agent is added to the homogenized raw mixture and is selected from the group consisting of sulphate, fluorine, chlorine bearing minerals and chemical wastes. 11. A process according to claim 1 wherein the iron (Fe 2 O 3 ) content of the homogenized raw mixture is less than 40%. 12. A process according to claim 1 wherein the rate of sintering and cooling respectively varies between 200 to 1000° C. and 400 to 600° C. per minute.