초록 ▼

The invention provides a process for removing steam-volatile fluorinated emulsifiers in their free acid form, from aqueous fluoropolymer dispersions. The process comprises adding a nonionic emulsifier, to the aqueous fluoropolymer dispersion and, at a pH-value of the aqueous fluoropolymer dispersion

The invention provides a process for removing steam-volatile fluorinated emulsifiers in their free acid form, from aqueous fluoropolymer dispersions. The process comprises adding a nonionic emulsifier, to the aqueous fluoropolymer dispersion and, at a pH-value of the aqueous fluoropolymer dispersion below 5, removing steam-volatile fluorinated emulsifier by distillation until the concentration of steam-volatile fluorinated emulsifier in the dispersion reaches the desired value.

대표청구항 ▼

1. A process for removing steam-volatile fluorinated emulsifiers in their free acid form, from aqueous fluoropolymer dispersions, said process comprising adding a nonionic emulsifier to said aqueous fluoropolymer dispersion and, at a pH-value of said aqueous fluoropolymer dispersion below 5, removin

1. A process for removing steam-volatile fluorinated emulsifiers in their free acid form, from aqueous fluoropolymer dispersions, said process comprising adding a nonionic emulsifier to said aqueous fluoropolymer dispersion and, at a pH-value of said aqueous fluoropolymer dispersion below 5, removing steam-volatile fluorinated emulsifier by distillation until the concentration of steam-volatile fluorinated emulsifier in the fluoropolymer dispersion reaches the desired value. 2. The process as claimed in claim 1, wherein said pH-value of said aqueous fluoropolymer dispersion is from 1 to 3. 3. The process as claimed in claim 1 or 2, wherein a strong mineral acid is used to set said pH. 4. The process as claimed in claim 3, wherein the acid is nitric acid. 5. The process according to claim 1 or 2 wherein said pH is set through cation-exchange. 6. The process of claim 1, wherein said aqueous fluoropolymer dispersion is a crude dispersion obtained from the polymerization process producing the fluoropolymer. 7. The process of claim 1, wherein water is removed from the dispersion by distillation, thus raising the concentration of the dispersion. 8. Process according to claim 1 wherein said process further comprises increasing the pH of said aqueous fluoropolymer dispersion to more than 7 subsequent to said removal of steam-volatile fluorinated emulsifier. 9. The process of claim 1 further comprising coating a substrate with the aqueous fluoropolymer dispersion. 10. A process according to claim 1 wherein the fluoropolymer is a fluoroelastomer. 11. A process according to claim 10 wherein the fluoroelastomer has a molecular weight less than 150,000. 12. A process according to claim 11 wherein the molecular weight of the fluoroelastomer is less than 100,000. 13. An aqueous dispersion made according to the process of claim 10 wherein the dispersion contains less than 50 ppm fluorinated emulsifier after distillation. 14. A process according to claim 1 wherein the aqueous fluoropolymer dispersion has been upconcentrated prior to removal of fluorinated emulsifiers. 15. A method of treating a substrate to provide a feature thereto selected from the groups consisting of antistickiness, weatherability, and noninflammability comprising contacting the substrate with a fluoropolymer prepared according to claim 1. 16. A method according to claim 15 wherein the substrate is metal. 17. A method according to claim 15 wherein the substrate is fabric.