초록 ▼

This invention relates to preparation and use of a rubber/carbon black composite comprised of at least one elastomer which contains a dispersion therein of carbon black aggregates. Such carbon black is formed by preparing a pre-blend comprised of uncompacted carbon black aggregates and oil and/or aq

This invention relates to preparation and use of a rubber/carbon black composite comprised of at least one elastomer which contains a dispersion therein of carbon black aggregates. Such carbon black is formed by preparing a pre-blend comprised of uncompacted carbon black aggregates and oil and/or aqueous latex of, preferably, a low molecular weight diene-based elastomer particles, followed by blending said pre-blend with an aqueous emulsion of diene-based elastomer particles and/or with an organic solution of a diene-based elastomer, and/or with solid diene-based elastomers, and recovery therefrom of a solid rubber/carbon black composite comprised of said diene-based elastomer, (which may include butyl rubber, EPDM rubber and thermoplastic polymers), which contains a dispersion therein of said carbon black aggregates having an apparent density significantly lower than the specific gravity of said carbon black aggregates and significantly lower than compacted carbon black aggregates. Such carbon black aggregates may be optionally in a form of silica treated carbon black which contains silica domains on its surface. A rubber composition is further provided which is comprised of said rubber/carbon black composite. An article of manufacture is also provided, such as a tire, having at least component comprised of said rubber/carbon black composite or said rubber composition.

대표청구항 ▼

1. A process of preparing a rubber composition which comprises:(A) blending non-compacted carbon black aggregates with rubber processing oil to form a pre-formed oil/carbon black aggregate composite comprised of said oil and said carbon black aggregates,wherein said rubber processing oil is selected

1. A process of preparing a rubber composition which comprises:(A) blending non-compacted carbon black aggregates with rubber processing oil to form a pre-formed oil/carbon black aggregate composite comprised of said oil and said carbon black aggregates,wherein said rubber processing oil is selected from rubber processing oils comprised of aromatic, paraffinic and/or naphthenic containing rubber processing oils,wherein said rubber processing oil is in a form of:(1) neat oil, or(2) emulsified oil comprised of:(a) water, surfactant and particles of emulsified oil, or(b) aqueous latex of particles of diene-based elastomer(s) and particles of emulsified oil, followed by:(B) blending said pre-formed oil/carbon black aggregate composite with(1) an aqueous emulsion of diene-based elastomer particles, and/or(2) an organic solvent solution of at least one diene-based elastomer, and/or(3) at least one diene-based elastomer, followed by(C) recovering therefrom a pre-formed elastomer composite comprised of said pre-formed carbon black/oil composite and said blended diene-based elastomer by removing said water and/or solvent therefrom, as the case may be, and wherein said recovered elastomer composite is comprised of said blended diene-based elastomer having a dispersion therein of said non-compacted carbon black aggregates. 2. The process of claim 1 wherein the weight ratio of said oil to said non-compacted carbon black aggregates is in a range of about 10/90 to about 50/50. 3. The process of claim 1 wherein the weight ratio of said pre-formed carbon black/oil composite to said emulsion and/or solvent solution of diene-based elastomer to form said pre-formed elastomer composite (a masterbatch) is in a range of about 30/70 to about 70/30 of said pre-formed carbon black/oil composite to said elastomer contained in said emulsion and/or solvent solution thereof. 4. The process of claim 1 wherein said pre-formed carbon black/oil composite contains at least one particulating agent selected from fatty acids, and particles of zinc oxide and compacted carbon black and their mixtures. 5. The process of claim 4 where said fatty acids are comprised of oleic acid, palmitic, linoleic and stearic acid and their mixtures. 6. The process of claim 1 wherein said pre-formed carbon black/oil composite is blended with a tapered styrene/butadiene elastomer that contains hard polystyrene segments and soft polybutadiene segments with a gradient of increasing polybutadiene content along the elastomer chain. 7. The process of claim 4 wherein said pre-formed carbon black/oil composite is blended with a tapered styrene/butadiene elastomer that contains hard polystyrene segments and soft polybutadiene segments with a gradient of increasing polybutadiene content along the elastomer chain. 8. A pre-formed carbon black/oil composite prepared according to the process of claim 1. 9. A pre-formed carbon black/oil composite prepared according to claim 4. 10. A pre-formed carbon black/oil composite prepared according to claim 6. 11. A pre-formed elastomer composite prepared by blending said pre-formed carbon black/oil composite of claim 8 with a solvent solution of a diene based elastomer and/or emulsion of diene-based elastomer particles and recovering a pre-formed elastomer composite therefrom. 12. A pre-formed elastomer composite prepared by blending said pre-formed carbon black/oil composite of claim 9 with a solvent solution of a diene based elastomer and/or emulsion of diene-based elastomer particles and recovering a pre-formed elastomer composite therefrom. 13. A pre-formed elastomer composite prepared by blending said pre-formed carbon black/oil composite of claim 10 with a solvent solution of a diene based elastomer and/or emulsion of diene-based elastomer particles and recovering a pre-formed elastomer composite therefrom. 14. A rubber composition prepared by blending said pre-formed elastomer composite of claim 11 with one or more additional diene-based elastomer s. 15. A rubber composition prepared by blending said pre-formed elastomer composite of claim 12 with one or more additional diene-based elastomers. 16. A rubber composition prepared by blending said pre-formed elastomer composite of claim 13 with one or more additional diene-based elastomers. 17. A article of manufacture having at least one component comprised of the rubber composition of claim 14. 18. A tire having at least one component comprised of the rubber composition of claim 14. 19. A tire having at least one component comprised of the rubber composition of claim 15. 20. A tire having at least one component comprised of the rubber composition of claim 16. 21. A tire having a tread comprised of the rubber composition of claim 14.