초록 ▼

A film of a polymer or polymer precursor such as an epoxy resin is autodeposited on an active metal surface and then used to form an adhesive bond directly between the metal surface and the surface of a rubber substrate. Excellent adhesion of the metal to the rubber is obtained without the need to e

A film of a polymer or polymer precursor such as an epoxy resin is autodeposited on an active metal surface and then used to form an adhesive bond directly between the metal surface and the surface of a rubber substrate. Excellent adhesion of the metal to the rubber is obtained without the need to either phosphate the metal surface or use a primer or adhesive other than the autodeposited coating.

대표청구항 ▼

1. A method of forming a rubber-metal composite comprising autodepositing a coating comprised of a resin reactive with an uncured thermosettable rubber formulation onto a metallic substrate surface, substantially completely curing said autodeposited coating, bringing the cured autodeposited coating

1. A method of forming a rubber-metal composite comprising autodepositing a coating comprised of a resin reactive with an uncured thermosettable rubber formulation onto a metallic substrate surface, substantially completely curing said autodeposited coating, bringing the cured autodeposited coating into direct contact with the uncured thermosettable rubber formulation, and curing the thermosettable rubber formulation, said rubber-metal composite being characterized by the absence of a separate adhesive layer. 2. The method of claim 1 wherein the coating is comprised of epoxy resin comprising at least one diglycidyl ether of bisphenol A having an epoxide equivalent weight of about 150 to about 300 and at least one flexibilizing epoxy resin derived from cardanol, wherein the ratio of flexibilizing epoxy resin:bisphenol A diglycidyl ether is from about 0.05 to about 0.40, as calculated from the epoxide equivalent weight of each component. 3. The method of claim 1 wherein said autodepositing is accomplished by contacting the metallic substrate surface with an autodeposition bath composition comprisinga) at least one epoxy resin;b) at least one accelerator; andc) at least one cross-linker. 4. The method of claim 3 wherein the autodeposition bath composition is additionally comprised of at least one coalescing agent. 5. The method of claim 3 wherein the autodeposition bath composition is additionally comprised of at least one flow control additive. 6. The method of claim 3 wherein the at least one epoxy resin comprises at least one glycidyl ether of a polyhydric phenol. 7. The method of claim 3 wherein the at least one epoxy resin comprises at least one diglycidyl ether of bisphenol A and at least one flexibilizing epoxy resin. 8. The method of claim 3 wherein the at least one accelerator is selected from the group consisting of acids, oxidizing agents and complexing agents which are capable of causing the dissolution of active metals from the metallic substrate surface. 9. The method of claim 3 wherein the at least one cross-linker comprises a molecule containing at least two blocked isocyanate groups. 10. The method of claim 3 wherein said at least one epoxy resin and said at least one cross-linker are present in emulsified form. 11. The method of claim 1 wherein said thermosettable rubber formulation is cured in a mold. 12. The method of claim 1 wherein said reactive-resin is selected from the group consisting of phenolic resins, phenolic novolak resins, and mixtures thereof. 13. The method of claim 1 wherein the coating is additionally comprised of at least one adhesion promoter. 14. The method of claim 1 wherein the coating is additionally comprised of at least one adhesion promoter selected from the group consisting of chlorinated rubbers and chlorinated polyolefins. 15. The method of claim 1 wherein the cured autodeposited coating has a thickness of from about 20 to about 25 microns. 16. The method of claim 1 wherein the thermosettable rubber composition is comprised of at least one rubber selected from the group consisting of natural rubber, nitrile rubber, alkylated chlorosulfonated polyethylene, polybutadiene, neoprene, styrenebutadiene rubber, butyl rubber and ethylene-propylene-diene monomer (EPDM). 17. A method of forming a rubber-metal composite comprising autodepositing a coating comprised of a reactive resin directly onto a metallic substrate surface, said resin comprising functional groups reactive with functional groups of an uncured thermosettable rubber formulation, substantially completely curing said autodeposited coating, bringing the cured autodeposited coating into direct contact with said uncured thermosettable rubber formulation, and curing the uncured thermosettable rubber formulation, said rubber-metal composite being characterized by the absence of: a separate adhesive layer and a phosphate layer. 18. A method of forming a rubber-metal composite comprising:a) autodepositing a coating comprised of a res in reactive with a thermosettable rubber formulation onto a metallic substrate surface, said resin being selected from the group consisting of phenolic resins, phenolic novolak resins, styrene/butadiene-copolymers, polyacrylates, acrylic co-polymers, polyvinyl chloride, vinyl chloride/vinylidene chloride-copolymers and mixtures of phenolic resins and phenolic novolak resins;b) substantially completely curing said autodeposited coating,c) bringing the cured autodeposited coating into direct contact with the thermosettable rubber formulation, andd) curing the thermosettable rubber formulation, said rubber-metal composite being characterized by the absence of a separate adhesive layer.