초록 ▼

A composite crucible for pulling up monocrystalline silicon, which is superior in shape stability and suitable for a large-sized one is provided. The composite crucible is characterized in that a carbonaceous material as an outer layer and a quartz glass as an inner layer are integrally formed. Meth

A composite crucible for pulling up monocrystalline silicon, which is superior in shape stability and suitable for a large-sized one is provided. The composite crucible is characterized in that a carbonaceous material as an outer layer and a quartz glass as an inner layer are integrally formed. Methods for preparing and regenerating a composite crucible are also disclosed.

대표청구항 ▼

1. A method for preparing a composite crucible for pulling up monocrystalline silicone, the crucible comprising an outer layer made of a carbon fiber-reinforced carbonaceous material having fine gaps between fibers on an inner surface, the fibers having a gas permeability of 0.5 cm/sec or more, and

1. A method for preparing a composite crucible for pulling up monocrystalline silicone, the crucible comprising an outer layer made of a carbon fiber-reinforced carbonaceous material having fine gaps between fibers on an inner surface, the fibers having a gas permeability of 0.5 cm/sec or more, and wherein the crucible comprises an inner vitrified quartz layer which is integral with the outer layer through the fine gaps, the method comprising:using a carbon fiber crucible as an outer circumferential part,supplying quartz powders on an inner surface of the carbon crucible while rotating it to be heated and malted; andvitrifying the quartz layer up to the inner surface of the carbon crucible to integrally form the quartz glass layer and the carbon crucible layer, thereby obtaining the composite crucible having a carbon fiber outer layer integrally formed with a quartz glass inner layer. 2. A method according to claim 1, comprising:depositing quartz powders on the inner surface of the carbon crucible to be heated and melted; andsupplying quartz powders gradually under boating to deposit a melted quartz powder on the quartz layer, thereby obtaining a composite crucible having a transparent glass layer formed in the inner surface thereof. 3. A method according to claim 1, comprising:using a carbon fiber crucible having gas permeability as an outer circumferential part,depositing quartz powders on an inner surface of the carbon crucible while rotating it to be heated and fused;reducing pressure in the carbon crucible through the carbon crucible upon the heating and fusing;sucking and removing the gas contained in the quartz layer; and extruding bubbles contained in the quartz glass layer to form a transparent glass layer on an inner surface of the carbon crucible, thereby obtaining the composite crucible in which the quartz glass layer and the carbon crucible layer are integrally formed. 4. A method according to claim 1 for regenerating a composite crucible, comprising: heating the crucible from the inner surface side; and fusing again the surface of the quartz glass layer. 5. A method according to claim 1 for regenerating a composite crucible, comprising:removing a quartz glass layer composite crucible;supplying fresh quartz powders on an inner surface of the remaining carbon crucible to be heated and melted; andvitrifying the quartz powder to thereby integrally form the quartz glass layer and carbon crucible layer.