초록 ▼

Recycled rubber products are made in a two step process. In the first step, ground rubber is treated with a polyurethane binder to make a treated rubber. In the second step, the treated rubber is mixed with additional polyurethane binder and molded into finished products. This method uses less polyu

Recycled rubber products are made in a two step process. In the first step, ground rubber is treated with a polyurethane binder to make a treated rubber. In the second step, the treated rubber is mixed with additional polyurethane binder and molded into finished products. This method uses less polyurethane binder than the conventional process, but the products have higher tensile strengths. The molding time is also reduced because of the reduced amount of polyurethane binder used.

대표청구항 ▼

1. A method of making recycled rubber products with less polyurethane binder reduced curing times, and high tensile strengths compared with equivalent products made by known polyurethane binder methods, the method comprisinga treatment step comprising mixing ground rubber with a first polyurethane b

1. A method of making recycled rubber products with less polyurethane binder reduced curing times, and high tensile strengths compared with equivalent products made by known polyurethane binder methods, the method comprisinga treatment step comprising mixing ground rubber with a first polyurethane binder until the first polyurethane binder is reacted and the rubber is free of clumps, anda forming step comprising mixing the product of the treatment step with a second polyurethane binder and molding the resulting mixture. 2. The method of claim 1 using from about 0.25% to about 1.5% by weight of the first polyurethane binder. 3. The method of claim 2 comprising about 1% by weight of the first polyurethane binder. 4. The method of claim 1 wherein the treatment step is performed at an elevated temperature. 5. The method of claim 1 wherein the treatment step is performed at about 150° F. 6. The method of claim 1 wherein the first polyurethane binder is the same as the second polyurethane binder. 7. The method of claim 1 wherein the first polyurethane binder is different from the second polyurethane binder. 8. The method of claim 1 comprising from about 1% to about 3% by weight of the second polyurethane binder. 9. The method of claim 1 wherein the molding is performed at from about 200° F. to about 400° F. 10. The method of claim 1 wherein the molding is performed at from about 75 psi to about 500 psi. 11. The method of claim 1 wherein the treatment step further comprises mixing a dye or pigment with the ground rubber and the first polyurethane binder. 12. The method of claim 1 wherein the forming step further comprises mixing a dye or pigment with the ground rubber and the second polyurethane binder. 13. The method of claim 1 wherein the ground rubber contains nylon. 14. A method of making a composite of ground rubber and polyurethane comprisingpreparing a treated rubber by mixing ground rubber with a first polyurethane binder at an elevated temperature until the first polyurethane binder is reacted and the rubber is free of clumps, andmixing the treated rubber with a second polyurethane binder and molding the resulting mixture at elevated temperature and pressure. 15. A recycled rubber product with less polyurethane binder, reduced curing time, and high tensile strength compared with equivalent products made by known polyurethane binder methods, made by a method comprisinga treatment step comprising mixing ground rubber with a first polyurethane binder until the first polyurethane binder is reacted and the rubber is free of clumps, anda forming step comprising mixing the product of the treatment step with a second polyurethane binder and molding the resulting mixture. 16. Polyurethane treated rubber particles comprising rubber particles coated with a cured polyurethane binder, wherein the treated rubber particles comprise from about 0.25% to about 1.5% by weight of the polyurethane binder. 17. The treated rubber particles of claim 16 further comprising a pigment or dye.