초록 ▼

This invention relates to a pneumatic tire with puncture sealing property and a method for preparing such tire. Such tire is prepared by building an uncured butyl rubber-based layer, which contains a peroxide and a dispersion therein of a particulate precured rubber selected from pre resin-cured but

This invention relates to a pneumatic tire with puncture sealing property and a method for preparing such tire. Such tire is prepared by building an uncured butyl rubber-based layer, which contains a peroxide and a dispersion therein of a particulate precured rubber selected from pre resin-cured butyl rubber and/or pre sulfur-cured diene-based elastomer, into an uncured tire and between an innerliner layer and the tire carcass. Upon curing the prepared tire under conditions of elevated temperature, a major portion of the uncured butyl rubber composition is depolymerized to form a tacky material, which contains said dispersion therein of said particulate precured rubber, which has puncture sealant properties. Such layer of depolymerized butyl rubber and dispersed precured rubber particles may be collectively referred to as the sealant layer.

대표청구항 ▼

1. A method of manufacturing a pneumatic rubber tire having an outer circumferential tread, a supporting carcass therefore, and an inner liner disposed inwardly from said supporting carcass, containing a puncture sealant layer positioned between said inner liner and said carcass, the steps of which

1. A method of manufacturing a pneumatic rubber tire having an outer circumferential tread, a supporting carcass therefore, and an inner liner disposed inwardly from said supporting carcass, containing a puncture sealant layer positioned between said inner liner and said carcass, the steps of which comprise, based upon parts by weight per 100 parts by weight uncured butyl rubber (phr):(A) providing a butyl rubber-based rubber composition comprised of: (1) 100 phr of uncured star branched butyl rubber, (2) about 1 to about 35 phr of a particulate precured rubber, selected from resin-cured butyl rubber and/or sulfur-cured diene-based rubber, homogeneously dispersed in said uncured butyl rubber, and (3) about 1 to about 16 phr of organoperoxide; (B) assembling said butyl rubber based rubber composition as a layer into an unvulcanized rubber tire between said carcass and said innerliner during the tire building process; and (C) shaping and curing said rubber tire at a temperature in a range of about 130° C. to about 170° C. for a sufficient period time to partially depolymerize said uncured butyl rubber in said butyl rubber-based rubber composition layer, wherein said particulate precured rubber substantially remains in its precured condition as a particulate dispersion within said partially depolymerized butyl rubber. 2. The method of claim 1 wherein said precured rubber is a resin-cured butyl rubber cured with a phenol formaldehyde curative and zinc oxide resin cure promoter.3. The method of claim 1 wherein said precured rubber is a sulfur-cured diene-based rubber.4. The method of claim 1 wherein said organoperoxide is selected from at least one of tertbutyl perbenzoate, dialkylbenzene peroxides, 2,5-bis(t-butyl peroxy)-2,5-dimethyl hexane; 1,1-di-t-butyl peroxi-3,3,5-trimethyl cyclohexane; 2,5-dimethyl-2,5-di(t-butyl peroxy) hexyne-3; p-chlorobenzyl peroxide; 2,4-dichlorobenzyl peroxide; 2,2-bis-(t-butyl peroxi)-butane; di-t-butyl peroxide; benzyl peroxide; 2,5-bis(t-butyl peroxy)-2,5-dimethyl hexane, dicumyl peroxide; and 2,5-dimethyl-2,5-di(t-butyl peroxy) hexane.5. The method of claim 1 wherein said organoperoxide is comprised of dicumylperoxide.6. A tire prepared by the method of claim 1.7. A pneumatic tire comprising an outer circumferential tread, a supporting carcass therefore and an inner rubber liner disposed inwardly from said supporting carcass, and a puncture sealant layer which is disposed between said carcass and said innerliner, wherein said puncture sealant layer comprises a partially depolymerized star branched butyl rubber layer which contains a dispersion of particulate precured resin-cured butyl rubber and/or sulfur-cured diene-based rubber.8. The tire of claim 7 wherein said particulate precured rubber is a resin-cured butyl rubber.9. The tire of claim 7 wherein said particulate precured rubber is a sulfur-cured diene-based rubber.10. The tire of claim 7 wherein said star branched butyl rubber of said sealant layer is depolymerized within the tire with an organoperoxide during the curing of the tire.11. The tire of claim 10 wherein said organoperoxide is selected from at least one of tertbutyl perbenzoate, dialkylbenzene peroxides, 2,5-bis(t-butyl peroxy)-2,5-dimethyl hexane; 1,1-di-t-butyl peroxi-3,3,5-trimethyl cyclohexane; 2,5-dimethyl-2,5-di(t-butyl peroxy) hexyne-3; p-chlorobenzyl peroxide; 2,4-dichlorobenzyl peroxide; 2,2-bis-(t-butyl peroxi)-butane; di-t-butyl peroxide; benzyl peroxide; 2,5-bis(t-butyl peroxy)-2,5-dimethyl hexane, dicumyl peroxide; and 2,5-dimethyl-2,5-di(t-butyl peroxy) hexane.12. The tire of claim 10 wherein said organoperoxide is comprised of dicumyl peroxide.13. The tire of claim 11 wherein said particulate precured rubber is a resin-cured butyl rubber.14. The tire of claim 11 wherein said particulate precured rubber is a sulfur-cured diene-based rubber.