초록 ▼

This invention provides a new catalyst for purification of diesel engine exhaust gas comprising a carrier of at least one sulfur-resistant refractory oxide and at least one catalytic metal, wherein at least one solid acid and/or sulfuric acid is carried on the carrier by adding at least one precurso

This invention provides a new catalyst for purification of diesel engine exhaust gas comprising a carrier of at least one sulfur-resistant refractory oxide and at least one catalytic metal, wherein at least one solid acid and/or sulfuric acid is carried on the carrier by adding at least one precursor of said solid acid and/or sulfuric acid during the preparation of the carrier, and preparation thereof. The catalyst of this invention is thermally and chemically durable and can effectively remove particulate matters, hydrocarbons and nitrogen oxides contained in the diesel engine exhaust gas at low temperatures.

대표청구항 ▼

1. A catalyst for the purification of diesel engine exhaust gas comprising at least a catalytic metal and a carrier, wherein said catalytic metal is selected from a group consisting of platinum, palladium, rhodium, ruthenium, rhenium, and their mixtures, wherein said carrier is a zirconia-titania co

1. A catalyst for the purification of diesel engine exhaust gas comprising at least a catalytic metal and a carrier, wherein said catalytic metal is selected from a group consisting of platinum, palladium, rhodium, ruthenium, rhenium, and their mixtures, wherein said carrier is a zirconia-titania composite oxide which comprises sulfuric acid and at least one additional solid acid selected from a group consisting of oxides of tungsten and oxides of molybdenum, and said zirconia-titania composite oxide has a ratio of zirconia to titania between 10:90 and 90:10.2. The catalyst according to claim 1, wherein said solid acid is present in an amount of 1?90% by weight based on the total amount of said composite oxide and said solid acid.3. The catalyst according to claim 1, wherein said sulfuric acid is present in an amount of 0.1?90% by weight based on the amount of said composite oxide.4. The catalyst according to claim 1, wherein said catalytic metal is present in an amount of 0.01?10% by weight based on the total amount of the carrier.5. The catalyst according to claim 1, wherein said zirconia-titania composite oxide further comprises at least one oxide selected from the group consisting of oxides of silicon, aluminum, iron, tin and cerium, in the form of a composite oxide or a mixture of oxides.6. A process for the preparation of a catalyst for the purification of exhaust gas comprising at least a catalytic metal and a carrier as defined in claim 1, said process comprises the steps of:(1) preparing a solution of precursors of a zirconia-titania composite oxide, (2) adding an alkali solution to co-precipitate said solution to form a mixed gel thereof, (3) drying, shaping and calcining the resulting mixed gel to form a composite oxide, (4) depositing at least one catalytic metal selected from a group consisting of platinum, palladium, rhodium, ruthenium, and rhenium; wherein (a) at least one precursor of said additional solid acid selected from a group consisting of oxides of tungsten and oxides of molybdenum or its solution is added before or after the co-precipitation of said step (2), and (b) sulfuric acid is added after the co-precipitation of said step (2). 7. The process according to claim 6, wherein said precursor of the additional solid acid is added before the co-precipitation of step (2) to the solution of precursors of a zirconia-titania composite oxide.8. The process according to claim 6, wherein said precursor of the additional solid acid is dissolved in sulfuric acid and the resulting mixture is added after the co-precipitation of step (2).9. The process according to clam 6, wherein at least one precursor of oxides of silicon, aluminum, iron, tin and/or cerium is added to the solution of precursors of a zirconia-titania composite oxide before the co-precipitation of step (2).10. The process according to claim 6, wherein said alkali solution is an aqueous ammonia solution.