초록 ▼

Carbon structures, e.g. carbon nano-fibers, suitable for absorbing hydrogen at low pressures and low temperatures are produced by a selective oxidation and/or acid reflux process. The process includes heating an impure mixture containing a crystalline form of carbon in the presence of an oxidizing g

Carbon structures, e.g. carbon nano-fibers, suitable for absorbing hydrogen at low pressures and low temperatures are produced by a selective oxidation and/or acid reflux process. The process includes heating an impure mixture containing a crystalline form of carbon in the presence of an oxidizing gas at a temperature and time sufficient to selectively oxidize and remove a substantial amount of any amorphous carbon impurities from the mixture. Metal containing impurities can be removed from the mixture by exposing the desired carbon and accompanying impurities to an acid to produce a carbon fiber that is substantially free of both non-fiber carbon impurities and metal impurities. Another aspect of the present invention includes purified carbon structures that can store hydrogen at low pressures and temperatures.

대표청구항 ▼

1. A process for synthesizing a purified single-wall carbon nanotube having open ends, the process comprising the sequential steps of:a) heating a mixture comprising a single-wall carbon nanotube and accompanying impurities in the presence of an oxidizing gas at a temperature sufficient to selective

1. A process for synthesizing a purified single-wall carbon nanotube having open ends, the process comprising the sequential steps of:a) heating a mixture comprising a single-wall carbon nanotube and accompanying impurities in the presence of an oxidizing gas at a temperature sufficient to selectively remove a substantial amount of carbon impurities; b) exposing the mixture to an acid at a temperature of about 100° C. to about 130° C. to remove a substantial amount of metal impurities; and c) exposing the single-wall carbon nanotube to nitric acid at a temperature and time period sufficient to introduce openings in the single-wall carbon nanotube. 2. The process of claim 1, comprising, after step c), heating the single-wall carbon nanotube under vacuum.3. The process of claim 1, comprising heating the mixture at a temperature of about 295° C. to about 500° C. to selectively remove the substantial amount of carbon impurities.4. The process of claim 1, comprising heating the mixture at a temperature of about 350° C. to about 410° C. for a period of time of no less than 30 minutes to selectively remove the substantial amount of carbon impurities.5. A process for synthesizing a purified single-wall carbon nanotube having open ends, the process comprising the sequential steps of:a) heating a mixture comprising a single-wall carbon nanotube and accompanying impurities in the presence of an oxidizing gas at a temperature sufficient to selectively remove a substantial amount of carbon impurities; b) exposing the mixture to an acid to remove a substantial amount of metal impurities; and c) exposing the single-wall carbon nanotube to nitric acid at a temperature of about 130° C. and time period sufficient to introduce openings in the single-wall carbon nanotube. 6. The process of claim 5, comprising exposing the heated and exposed mixture to the HNO3 at a temperature of about 130° C. for a time period of about 2 hours to about 200 hours.7. A process for synthesizing a purified single-wall carbon nanotube, the process comprising the sequential steps of:a) heating a carbon soot comprising a single-wall carbon nanotube and accompanying impurities in air at a temperature of about 500° C. for a period of about 1 hour; b) exposing the single-wall carbon nanotube and any accompanying impurities to about 3 molar aqueous nitric acid at a temperature of about 120° C. for about 12 hours; c) exposing the single-wall carbon nanotube and any accompanying impurities to aqueous hydrogen peroxide at a temperature of about 80° C. for about 24 hours; and d) exposing the single-wall carbon nanotube and any accompanying impurities to about 10 molar HCl at a temperature of about 120° C. for about 12 hours. 8. The process of claim 7, wherein the carbon soot contains nickel, titanium, or salts thereof as impurities.9. The process of claim 7, wherein the carbon soot was prepared using a catalyst comprising nickel, yttrium, titanium, their salts or any combination thereof.