초록 ▼

The present invention provides a method for preparing a rhenium-tantalum alloy with improved strength and ductility characteristics. The method includes mixing powders of rhenium and tantalum with a weight ration of approximately 97% rhenium to approximately 3% tantalum. The powdered blend is then c

The present invention provides a method for preparing a rhenium-tantalum alloy with improved strength and ductility characteristics. The method includes mixing powders of rhenium and tantalum with a weight ration of approximately 97% rhenium to approximately 3% tantalum. The powdered blend is then compressed to a green state. The green compress of rhenium and tantalum is then sintered such that tantalum goes into solid solution with rhenium. The sintered material is then cold rolled. The cold rolling disperses oxides away from concentrations in the alloy grain boundaries. If desired, the alloy may then be annealed. The result is a rhenium-tantalum alloy that displays improved high temperature strength and ductility over pure rhenium materials. The present alloy is particularly suited to fabrication of rocketry components such as valve bodies, poppets, seats, and nozzles.

대표청구항 ▼

1. A method of forming a rhenium-tantalum alloy comprising the steps of:mixing a blend of rhenium and tantalum wherein the amount of tantalum is within the solid solubility limits for rhenium; compressing the mixture of rhenium and tantalum to a green state; sintering the green compress of rhenium a

1. A method of forming a rhenium-tantalum alloy comprising the steps of:mixing a blend of rhenium and tantalum wherein the amount of tantalum is within the solid solubility limits for rhenium; compressing the mixture of rhenium and tantalum to a green state; sintering the green compress of rhenium and tantalum so that the tantalum goes into solid solution with the rhenium; and cold rolling the sintered rhenium-tantalum alloy. 2. The method according to claim 1 further comprising the step of annealing the cold rolled rhenium-tantalum alloy.3. The method according to claim 1 wherein the step of mixing further comprises a blend of approximately 97 weight percent rhenium with approximately 3 weight percent tantalum.4. The method according to claim 1 wherein the weight ratio of rhenium and tantalum is between approximately 99.9% Re/0.1% Ta to approximately 94.9% Re/5.1% Ta.5. The method according to claim 1 wherein the step of compressing further comprises compressing at a pressure sufficient to compress the powders to a green compact.6. The method according to claim 1 wherein the step of sintering further comprises sintering at a temperature of between approximately 1800° C. and approximately 2200° C. for up to 4 hours.7. The method according to claim 1 wherein the step of cold rolling further comprises cold rolling.8. The method according to claim 1 wherein the step of annealing further comprises annealing at a temperature of between approximately 1450° C. to approximately 1800° C. for up to 4 hours.9. A method for making a rhenium-tantalum alloy with improved high temperature ductility comprising the steps of:providing a rhenium powder and a tantalum powder wherein the weight ratio of rhenium and tantalum is between approximately 96.5% Re/3.5% Ta and approximately 97.5% Re/2.5% Ta; mixing the rhenium and tantalum powders to form a homogenous blend; compressing the mixture of rhenium and tantalum powders to form a green compact; sintering the green compact of rhenium and tantalum powder so that the tantalum goes into solid solution with the rhenium; and cold rolling the sintered rhenium-tantalum alloy so as to distribute tantalum oxides from a grain boundary location. 10. The method according to claim 9 wherein the step of cold rolling further comprises cold rolling sufficient to disperse tantalum oxide impurities away from the grain boundaries of the alloy.11. The method according to claim 9 wherein the step of cold rolling further comprises cold rolling that affects a reduction in the concentration of a tantalum oxide impurity.12. The method according to claim 9 wherein the step of cold rolling further comprises a cold rolling that decreases the level of tantalum oxide impurities from a grain boundary by more than 10%.13. The method according to claim 9 wherein the step of cold rolling further comprises cold rolling that increases the homogeneity of the alloy with respect to the location of tantalum oxide impurities within the grain structure.14. A rocket thrust vector control component subject to high stress comprising a carbon substrate and a rhenium-tantalum alloy protective layer disposed on the carbon substrate, wherein the rhenium-tantalum alloy has received a cold rolling treatment.15. The component according to claim 14 wherein said component comprises a valve seat.16. The component according to claim 14 wherein said component comprises a valve poppet.17. The component according to claim 14 wherein said component comprises a valve body.18. The component according to claim 14 wherein said component comprises a nozzle.19. The component according to claim 14 wherein the rhenium-tantalum alloy protective layer comprises an alloy with rhenium and an amount of tantalum that is within the solid solubility limits for rhenium.20. The component according to claim 14 wherein the rhenium-tantalum alloy protective layer comprises an alloy with approximately 97 weight percent rhenium and approximately 3 weight percent tantalum.21. The component according to claim 14 wherein the rhenium-tantalum alloy protective layer comprises an alloy wherein the weight ratio of rhenium and tantalum is between approximately 99.9% Re/0.1% Ta to approximately 94.9% Re/5.1% Ta.