초록 ▼

The invention provides a monolithic catalyst support for hydrogenation and hydrotreating and in particular for selective hydrogenation of pyrolysis gasoline. The monolithic catalyst includes (i) a multicellular monolith body, preferably having a honeycomb structure, most preferably a honeycomb struc

The invention provides a monolithic catalyst support for hydrogenation and hydrotreating and in particular for selective hydrogenation of pyrolysis gasoline. The monolithic catalyst includes (i) a multicellular monolith body, preferably having a honeycomb structure, most preferably a honeycomb structure made of cordierite, the honeycomb structure having an inlet end, an outlet end, and a multiplicity of mutually adjoining cells extending along the length of the body from the inlet end to the outlet end, the cells being separated from one another by porous walls, and, (ii) a coating consisting of theta alumina synthesized in situ on the multicellular monolith body. The in situ theta alumina is strongly bonded with the multicellular monolith body and comprises at least 50% by weight of the washcoat layer, and preferably greater than 90% by weight.

대표청구항 ▼

1. A monolithic catalyst support comprising a multicellular monolith body and a coating layer of in situ synthesized theta alumina strongly bonded to the multicellular monolith body, wherein the theta alumina is greater than 50% by weight of the coating layer.2. A monolithic catalyst support accordi

1. A monolithic catalyst support comprising a multicellular monolith body and a coating layer of in situ synthesized theta alumina strongly bonded to the multicellular monolith body, wherein the theta alumina is greater than 50% by weight of the coating layer.2. A monolithic catalyst support according to claim 1 wherein the theta alumina is greater than 90% by weight of the coating layer.3. A monolithic catalyst support according to claim 2 wherein the multicellular monolith body is composed of a material selected from the group consisting of ceramic, glass, glass-ceramic, metal and combinations thereof.4. A monolithic catalyst support according to claim 3 wherein the multicellular monolith body is a honeycomb structure.5. A monolithic catalyst support according to claim 4 wherein the honeycomb structure has an inlet end, an outlet end, and a multiplicity of mutually adjoining cells extending along the length of the honeycomb structure from the inlet end to the outlet end, the cells being separated by from one another by porous walls.6. A monolithic catalyst support according to claim 5 wherein the honeycomb structure is composed of cordierite.7. A monolithic catalyst support according to claim 6 wherein the honeycomb structure is further characterized by:a cell density of 10 to 1200 cells per square inch; a cell wall thickness of 0.1 to 50 mil; a cell wall porosity of 10% to 75% by volume; and, a cell wall median pore size of 1 to 50 micrometers. 8. A monolithic catalyst support according to claim 7 wherein the honeycomb structure is further characterized by:a cell density of 100 to 600 cells per square inch; a cell wall thickness of 2 to 35 mil; a cell wall porosity of 25% to 65% by volume; and, a cell wall median pore size of 10 to 35 micrometers. 9. A method of producing an in situ synthesized theta alumina monolith catalyst support, the method comprising:a. providing a multicellular monolith body; b. applying a washcoat of an alumina precursor to the multicellular monolith body; c. drying the resulting coated multicellular monolith body; and, d. calcining the dried coated multicellular monolith body at a temperature of 800° to 1200° C. for at least 0.5 hours to in situ synthesize and strongly bond theta alumina in a proportion greater than 50% by weight of the calcined coating to the multicellular monolith body. 10. The method of claim 9 wherein the calcining step is carried out at a temperature of between 900° to 1050° C. for 2 to 4 hours to in situ synthesize and strongly bond theta alumina in a proportion greater than 90% by weight of the calcined coating to the multicellular monolith body.11. The method of claim 10 wherein the calcining step is carried out at a temperature of 1000° C. for 3 hours.12. The method of claim 9 wherein the multicellular monolith body is a honeycomb structure.13. The method of claim 12 wherein the honeycomb structure is characterized by an inlet end, an outlet end, and a multiplicity of mutually adjoining cells extending along the length of the honeycomb structure from the inlet end to the outlet end, the cells being separated by from one another by porous walls.14. The method of claim 13 wherein the alumina precursor is selected from the group consisting of inorganic and organic salts of aluminum.15. The method of claim 14 wherein the alumina precursor is selected from the group consisting of aluminum oxide hydroxide (AlOOH.xH2O), aluminum hydroxide, aluminum nitrate, aluminum isopropoxide, lactate, and triethoxide.16. The method of claim 15 wherein the alumina precursor is aluminum oxide hydroxide or boehmite.