초록 ▼

A method for manufacturing valve seats using a laser cladding process is provided that includes forming a casting material on which the valve seats are to be formed; fabricating a valve seat target position on which laser cladding will be performed, the valve seat target position being provided at a

A method for manufacturing valve seats using a laser cladding process is provided that includes forming a casting material on which the valve seats are to be formed; fabricating a valve seat target position on which laser cladding will be performed, the valve seat target position being provided at a location on the casting material where a valve seat is to be formed; removing an oxidation film formed on the valve seat target position; injecting a metal powder mixture on the valve seat target position, the metal powder mixture being realized through a mixture of two or more metal powders at a predetermined ratio by weight %; and irradiating a laser beam on the metal powder mixture to clad the metal powder mixture on the valve seat target position to thereby form the valve seat.

대표청구항 ▼

1. A method for manufacturing valve seats using a laser cladding process, comprising:forming a casting material on which at least one valve seat is to be formed; fabricating a valve seat target position at a location on the casting material where a valve seat is to be formed; removing an oxidation f

1. A method for manufacturing valve seats using a laser cladding process, comprising:forming a casting material on which at least one valve seat is to be formed; fabricating a valve seat target position at a location on the casting material where a valve seat is to be formed; removing an oxidation film formed on the valve seat target position by injecting a mixture including two or more elements that react chemically at a predetermined temperature onto the valve seat target position, and irradiating a laser beam onto the mixture to raise the temperature of the mixture to at or above the predetermined temperature needed for chemical reaction; injecting a metal powder mixture onto the valve seat target position wherein the metal powder mixture includes copper (Cu) particles and nickel (Ni) particles mixed at a predetermined ratio by weight; and irradiating a laser beam on the metal powder mixture to clad the metal powder mixture on the valve seat target position. 2. The method of claim 1, wherein the mixture includes silicon (Si) particles and boron (B) particles, which are mixed at a predetermined ratio by weight.3. The method of claim 1, wherein the oxidation film is removed by varying an intensity of the laser beam irradiated on the valve seat target position.4. The method of claim 3, wherein the intensity of the laser beam is varied within a range in which a fusing temperature of the valve seat target position is not exceeded.5. The method of claim 1, wherein the metal powder mixture is injected with a shield gas mixed with the metal powder mixture, the shield gas allowing for the smooth supply of the metal powder mixture and shielding of the metal powder mixture from surrounding air.6. The method of claim 5, wherein the shield gas is a gas selected from the group consisting of argon and helium.7. A method for manufacturing a valve seat, comprising:removing oxidation film from a valve seat target position on a valve seat receiving structure wherein said removing oxidation film comprises irradiating said valve seat target position with a laser beam, injecting onto said valve seat target position a mixture including components that react at a predetermined temperature to remove the oxidation film, and directing said laser beam onto said mixture to raise the temperature above said predetermined temperature; injecting a metal powder mixture in an inert shielding gas onto the valve seat target position wherein said metal powder mixture comprises copper and nickel particles; and directing a laser beam on the metal powder mixture at said target position to clad the metal powder to said structure forming a valve seat. 8. The method of claim 7, wherein said removing oxidation film further comprises varying intensity of said laser beam within a range not exceeding a fusing temperature of the valve seat target position.