초록 ▼

A new method for repairing turbine engine components is provided. The method utilizes a cold gas-dynamic spray technique to repair degradation on turbine blades, vanes and other components. In the cold gas-dynamic spray process particles at a temperature below their fusing temperature are accelerate

A new method for repairing turbine engine components is provided. The method utilizes a cold gas-dynamic spray technique to repair degradation on turbine blades, vanes and other components. In the cold gas-dynamic spray process particles at a temperature below their fusing temperature are accelerated and directed to a target surface on the turbine blade. When the particles strike the target surface, the kinetic energy of the particles is converted into plastic deformation of the particle, causing the particle to form a strong bond with the target surface. Post-spray processing is then performed to consolidate and homogenize the applied materials and restore integrity to the material properties in the repaired turbine component. Thus, the cold gas-dynamic spray process and post-spray processing can be employed to effectively repair degraded areas on gas turbine components.

대표청구항 ▼

1. A method for repairing a high pressure turbine component, the method comprising the steps of:cold gas-dynamic spraying powder material to repair degradation in at least a portion of the high pressure turbine component; vacuum sintering the high pressure turbine component after the cold gas-dynami

1. A method for repairing a high pressure turbine component, the method comprising the steps of:cold gas-dynamic spraying powder material to repair degradation in at least a portion of the high pressure turbine component; vacuum sintering the high pressure turbine component after the cold gas-dynamic spraying step; performing a hot isostatic pressing on the high pressure turbine component after the vacuum sintering step; and heat treating the high pressure turbine component after performing the hot isostatic pressing step. 2. The method of claim 1 wherein the high pressure turbine component comprises a turbine blade.3. The method of claim 2 wherein the turbine blade comprises a tip, and wherein the cold gas-dynamic spraying is performed on the tip.4. The method of claim 2 wherein the turbine blade comprises a leading edge, and wherein the cold gas-dynamic spraying is performed on the leading edge.5. The method of claim 2 wherein the turbine blade comprises a platform, and wherein the cold gas-dynamic spraying is performed on the platform.6. The method of claim 2 wherein the turbine blade comprises a z-notch shroud, and wherein the particles are sprayed on the z-notch shroud.7. The method of claim 1 wherein the step of performing a vacuum sintering comprises sintering in a vacuum for between 2 and 4 hours at temperatures of between 2050 degrees F. and 2300 degrees F.8. The method of claim 1 wherein the step of performing a hot isostatic pressing on the turbine component comprises pressing for between 2 and 4 hours at temperatures of between 2100 and 2300 degrees F. and at pressures of between 10 and 30 ksi.9. The method of claim 1 further comprising the step of performing a rapid cooling of between 45 and 60 degrees F. per minute to a desired temperature level after the hot isostatic pressing.10. The method of claim 1 wherein the step heat treating the high pressure turbine component comprises a heat treatment of between 2 to 4 hours at temperatures of between 2000 and 2200 degrees F. followed by a second beat treatment of between 16 to 24 hours at temperatures of between 1300 and 1800 degrees F.11. A method for repairing degradation on a turbine blade, the method comprising the steps of:providing repair powder material; mixing the repair powder material into a flow of gas, the gas at a temperature below a melt temperature of the repair powder material; accelerating the repair powder material mixed into the flow of gas; directing the accelerated repair powder material to a target surface on the turbine blade, wherein the repair powder material deforms on the target surface to repair degradation on the turbine blade; vacuum sintering the turbine blade for between 2 and 4 hours at temperatures of between 2050 degrees F. and 2300 degrees F.; performing a hot isostatic pressing on the turbine blade for between 2 and 4 hours at temperatures of between 2100 and 2300 degrees F. and at pressures of between 10 and 30 ksi; and heat treating the turbine blade between 2 to 4 hours at temperatures of between 2000 and 2200 degrees F. followed by a second heat treatment of between 16 to 24 hours at temperatures of between 1300 and 1800 degrees F.