Carbon composite components (1, 11, 22, 30), which may be aircraft brake discs, heat exchanger cores, and so on, are covered by protective coating 32. Component (1, 11, 22, 30) is immersed in liquid bath precursor of fluidized glass (step 55). After immersion step, glass-coated component (1, 11, 22,
Carbon composite components (1, 11, 22, 30), which may be aircraft brake discs, heat exchanger cores, and so on, are covered by protective coating 32. Component (1, 11, 22, 30) is immersed in liquid bath precursor of fluidized glass (step 55). After immersion step, glass-coated component (1, 11, 22, 30) is removed and annealed. Heat treatment gradually increases temperature to 250-350° C. at the rate of 1-2° C. per minute (step 60). Heat treatment is followed by soak at temperature of 250-350° C. for 1-10 hours (step 65). Temperature is then increased to 550-650° C. (step 70). Temperature is maintained at 550-650° C. for 1-10 hours (step 75). After completion of second prolonged heat treatment, the component is cooled until reaching room temperature (step 80). Upon completion of the annealing step, the fluidized glass coating converts to solid glass coating (32) enveloping and forming a protective barrier against undesirable oxidation of the C?C component (1, 11, 22, 30). For application to thin-gauge composites, the glass precursor components contain 20-60 weight-% water, 25-50 weight-% phosphoric acid, 2-20 weight-% alkali metal hydroxide, 1-10 weight-% manganese phosphate, 1-10 weight-% boron nitride, 0-5 weight-% elemental boron, and 10-28 weight-% boron carbide.
대표청구항▼
1. A method of protecting a carbon fiber or carbon-carbon (C?C) composite component against high temperature oxidation, said method comprising the steps of:applying a coating of fluidized borophosphate glass precursor over the component by immersing the component in a bath containing glass precursor
1. A method of protecting a carbon fiber or carbon-carbon (C?C) composite component against high temperature oxidation, said method comprising the steps of:applying a coating of fluidized borophosphate glass precursor over the component by immersing the component in a bath containing glass precursor components including 25-50 weight-% phosphoric acid, 1-10 weight-% manganese phosphate, 2-20 weight-% potassium hydroxide, 1-10 weight-% boron nitride, 0-30 weight-% boron carbide, and 20-60 weight-% waters; gradially heating the glass precursor-coated component to a temperature range at which the glass transition temperature of a glass formed from the glass precursor is thermally matched to the oxidation temperature range of the carbon in the component, thereby forming a glass-coated component; continuing to heat the glass-coated component to anneal the glass-coated component; and gradually cooling the glass-coated component, thereby enveloping said component in a solid glass coating which protects it against high temperatures oxidation. 2. The method of claim 1, wherein said component is configured as an aircraft landing system brake disc.3. The method of claim 1, wherein said component is protected against oxidation at a temperature of about 1600° F.4. The method of claim 1, comprising the steps of:preparing a liquid glass precursor including 25-50 weight-% phosphoric acid, 1-10 weight-% manganese phosphate, 2-20 weight-% potassium hydroxide, 1-10 weight-% boron nitride, 0-30 weight-% boron carbide, and 20-60 weight-% water; maintaining the precursor at a temperature in the range of between about 20-90° C.; applying a coating of the liquid precursor to an outer surface of the component; and annealing the coated component at a temperature in the range of about 250-650° C., thereby creating a solid glass protective coating of about 1-10 mils thickness around the component for protecting the component from oxidizing species. 5. An article comprising:a component, made of carbon fiber or carbon-carbon (C?C) composite having a thickness of about 0.5 to 1.5 inches, annealed at a temperature in the range of about 2200-2600° C., and a glass coating of about 1-10 mils, made with a mixture containing 20-60 weight-% water, 25-50 weight-% phosphoric acid, 2-20 weight-% alkali metal hydroxide, 1-10 weight-% manganese phosphate, 0-10 weight-% boron nitride, 0-13 weight-% elemental boron, and 2-50 weight-% boron carbide, wherein said glass coating covers and protects said component against oxidizing species when the article is subjected to temperatures of up to about 900° C. 6. The article of claim 5, wherein said component is configured as an aircraft landing system brake disc.7. A method of protecting a thin-gauge carbon fiber or carbon-carbon (C?C) composite component against oxidation, the method comprising the steps of:applying a coating of fluidized borophosphate glass precursor over the component by immersing the component in a bath containing glass precursor components including at least 2 weight-% boron carbide and no more than 13 weight-% elemental boron; qradually heating the glass precursor-coated component to a temperature range at which the glass transition temperature of a glass formed from the glass precursor is thermally matched to the oxidation temperature range of the carbon in the component, thereby forming a glass-coated component; continuing to heat the glass-coated component to anneal the glass-coated component; and gradually cooling the glass-coated component, thereby enveloping said component in a solid glass coating which protects it against high temperatures oxidation. 8. The method of claim 7, wherein said bath contains glass precursor components including at least 10 weight-% boron carbide and no more than 5 weight-% elemental boron.9. The method of claim 7, wherein the glass precursor components comprise 20-60 weight-% water, 25-50 weight-% phosphoric acid, 2-20 weight-% alkali metal hydroxide, 1-10 weight-% manganese phosphate, 0-10 weight-% boron nitride, 0-13 weight-% elemental boron, and 2-50 weight-% boron carbide.10. The method of claim 9, wherein the glass precursor components comprise 20-60 weight-% water, 25-50 weight-% phosphoric acid, 2-20 weight-% alkali metal hydroxide, 1-10 weight-% manganese phosphate, 1-10 weight-% boron nitride, 0-5 weight-% elemental boron, and 10-28 weight-% boron carbide.11. The method of claim 7, wherein the coating of fluidized glass precursor is applied by rotating either the component or the bath relative to one another when the component is immersed in the fluidized glass precursor to completely and uniformly cover the component with the fluidized glass precursor.12. The method of claim 7, wherein the component is immersed in the precursor bath for more than one minute.13. The method of claim 7, wherein the step of heating the glass precursor coated component is conducted at a rate of about 1-2° C. per minute to a temperature of between about 250-350° C. and wherein the temperature is then maintained at about 250-350° C. for a period of between 1-10 hours.14. The method of claim 7, wherein the step of continuing to heat the coated component is conducted at a temperature of between about 550-650° C. for a period of between 1-10 hours.15. A method of protecting a thin-gauge carbon fiber or carbon-carbon (C?C) composite component against oxidation, the method comprising the steps of:preparing a liquid glass precursor including 25-50 weight-% phosphoric acid, 1-10 weight-% manganese phosphate, 2-20 weight-% potassium hydroxide, 0-10 weight-% boron nitride, 2-28 weight-% boron carbide, and 20-60 weight-% water; maintaining the liquid glass precursor at a temperature in the range of between about 20-90° C.; applying a coating of the liquid glass precursor to an outer surface of the component; and annealing the coated component at a temperature in the range of about 250-650° C., thereby creating a solid glass protective coating of about 1-10 mils thickness around the component for protecting the component from oxidizing species. 16. The method of claim 15, wherein the liquid precursor components comprise 20-60 weight-% water, 25-50 weight-% phosphoric acid, 2-20 weight-% potassium hydroxide, 1-10 weight-% manganese phosphate, 1-10 weight-% boron nitride, 0-5 weight-% elemental boron, and 10-28 weight-% boron carbide.17. The method of claim 15, comprising the step of gradually heating the precursor-coated component at a rate of 1-2° C. per minute until reaching a temperature in the range of about 250-350° C. and maintaining this temperature for between 1-10 hours to further anneal the coated component.18. The method of claim 15, comprising the step of gradually heating the precursor-coated component from a temperature in the range of about 250-350° C. to a temperature in the range of about 550-650° C. and maintaining this temperature for between 1-10 hours to further anneal the coated component.19. The method of claim 15, wherein the component has a thickness of about 3-30 mils.20. The method of claim 15, wherein said thin-gauge carbon fiber or carbon-carbon composite component is a heat exchanger core.21. A method of forming an oxidation protected carbon-carbon (C?C) composite component, the method comprising:forming thin-gauge two-dimensional woven fabric panels; rigidizing the panels with a small percentage of carbon-containing resin; carbonizing the panels at a temperature in the range of about 800-1000° C.; densifying by chemical vapor deposition; annealing the component at a temperature in the range of about 2200-2600° C.; and applying a coating of fluidized glass precursor over the component, by immersing the component in a bath containing glass precursor components including at least 2 weight-% boron carbide and no more than 13 weight-% elemental boron, to cover the component, thereby protecting the component against oxidizing species. 22. The method of claim 21, wherein said bath contains glass precursor components including at least 10 weight-% boron carbide and no more than 5 weight-% elemental boron.23. An article comprising:a thin-gauge component, made of carbon fiber or carbon-carbon (C?C) composite having a thickness of about 3-30 mils, annealed at a temperature in the range of about 2200-2600° C.; and a glass coating of about 1-10 mil, made with a mixture containing 20-60 weight-% water, 25-50 weight-% phosphoric acid, 2-20 weight-% alkali metal hydroxide, 1-10 weight-% manganese phosphate, 0-10 weight-% boron nitride, 0-13 weight-% elemental boron, and 2-50 weight-% boron carbide, wherein said glass coating covers and protects said component against oxidizing species when the article is subjected to temperatures of up to 800° C. 24. The article of claim 24, wherein the glass coating is annealed to the component at a temperature in the range of about 250-650° C.25. The article of claim 23, wherein the glass components comprise 20-60 weight-% water, 25-50 weight-% phosphoric acid, 2-20 weight-% alkali metal hydroxide, 1-10 weight-% manganese phosphate, 1-10 weight-% boron nitride, 0-5 weight-% elemental boron, and 10-28 weight-% boron carbide.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (30)
Prochazka Svante (Ballston Lake NY), Amorphous silicon oxycarbide coated silicon carbide or carbon fibers.
McAllister Lawrence E. (Granger IN) Jannasch Norman E. (South Bend IN), Barrier coating and penetrant providing oxidation protection for carbon-carbon materials.
Dyer Paul N. (Allentown PA) Magnotta Vincent L. (Wescosville PA) Stevens Robert E. (Emmaus PA), Coated carbonaceous articles and method for making same.
Dewar Douglas M. (Rolling Hills Estates CA) Anderson Alexander F. (Rolling Hills Estates CA) Duncan Christopher K. (Long Beach CA), Composite continuous sheet fin heat exchanger.
Giannetti William B. (Fall River MA) Hess David G. (Atkinson NH) McCord Stuart J. (Westford MA) Rudd ; III Robert E. (Vergennes VT) Shih Wei-Tei (Yorba Linda CA), Composite enclosure for electronic hardware.
Dewar Douglas M. (Rolling Hills Estates CA) Anderson Alexander F. (Rolling Hills Estates CA) Duncan Christopher K. (Long Beach CA), Composite machined fin heat exchanger.
Leggett ; deceased Hyman (late of Chatsworth CA by Sally S. Leggett ; Administrator) Brown Kenneth M. (Los Angeles CA), Graphite fiber reinforced silica matrix composite.
Thebault Jacques (Bordeaux FRX) Laxague Michel (Bordeaux FRX) Rey Jacques (Merignac FRX) Delaval Rodolphe (St. Martin au Laert FRX) Palavit Gerard (Douai FRX), Method for applying an anti-oxidative coating on brake disks of a carbon-containing composite material.
Delaval Rodolphe,FRX ; Palavit Gerard,FRX ; Rey Jacques,FRX ; Laxague Michel,FRX ; Thebault Jacques,FRX, Method for protecting a porous carbon-containing material from oxidation, and material obtained thereby.
Balhadere Aline,FRX ; Thebault Jacques,FRX ; Bernard Bruno,FRX, Method of protecting a part made of a carbon-containing composite material against oxidation.
Bentson Larry D. (Brecksville OH) Price Robert J. (Hudson OH) Purdy Mark J. (Akron OH) Stover Edward R. (Akron OH), Moisture and oxidation resistant carbon/carbon composites.
Holzl Robert A. (LaCanada CA) Tilley Benjamin H. (Eugene OR) Benander Robert E. (Sylmar CA) Magnotta Vincent L. (Coopersburg PA) Dyer Paul N. (Allentown PA), Oxidation resistant carbon and method for making same.
Tawil Henri,FRX ; Bernard Xavier,FRX ; Cavalier jean-Claude,FRX, Process for protecting products made of composite material containing carbon against oxidation, and products obtained b.