초록 ▼

A process is described for the production of holes, particularly of micro-perforations, in a composite material, constituted by fibers embedded in a resinous matrix, characterized in that it consists in a preliminary step of carrying out on a specimen of the composite material, with the help of a la

A process is described for the production of holes, particularly of micro-perforations, in a composite material, constituted by fibers embedded in a resinous matrix, characterized in that it consists in a preliminary step of carrying out on a specimen of the composite material, with the help of a laser beam, tests consisting in adjusting the duration of illumination at a predetermined place on the specimen, as well as the focusing and power of said laser beam, so as to confine the temperature in the mass of the material to a range of temperatures both greater than the thermal decomposition temperature of the matrix resin and below the temperature of altering the physical properties of the fibers, so as to carry out the elimination of the resin without affecting the physical integrity of the fibers, then in reproducing on the material (8) to be treated, at each position of a perforation to be made, the operating conditions of the laser (10, 12) so as to constitute in said material a through passage, as a result of only the local burning of the resin of the matrix of the composite material.

대표청구항 ▼

1. Process for producing holes (4 to 7), particularly micro-perforations, in a composite material, constituted by mineral or organic fibers (1, 2) embedded in a resinous matrix (3), characterized in that it consists:in a preliminary step, carrying out tests on a specimen of the composite material to

1. Process for producing holes (4 to 7), particularly micro-perforations, in a composite material, constituted by mineral or organic fibers (1, 2) embedded in a resinous matrix (3), characterized in that it consists:in a preliminary step, carrying out tests on a specimen of the composite material to be perforated, with a laser beam directed substantially perpendicularly to the surface of said specimen, said tests consisting in adjusting the duration of illumination at a predetermined position on the specimen, as well as the focusing and the power of said laser beam, so as to confine the temperature within the mass of the composite material to a range of temperatures both greater than the thermal decomposition material of the resin matrix (3) and below the temperature of changing the physical properties of the fibers (1, 2), so as to carry out the elimination of the resin without affecting the physical integrity of the fibers, then, in reproducing on the material to be treated, at each position of a hole or perforation to be produced, the conditions of operation of the laser (10, 12) so as to constitute in said material, at said position, a through-hole or passage, resulting from only local burning of the resin of the matrix of the composite material. 2. Process according to claim 1, characterized in that the step of reproduction on the material to be treated of said conditions of operation of the laser (10, 12) is carried out automatically by programming, on the one hand, parameters of controlling the operation of the laser and, on the other hand, controlling the movement of the laser beam relative to the various position of perforation.3. Process according to claim 1 or 2, characterized in that during the step of reproduction on the material to be treated of said conditions of operation of the laser (10, 12), the beam of this latter is subjected to sweeping of the position where a perforation is to be produced.