초록

The present invention provides a heat-treated plastic pressurized container that is resistant to polar liquids and impact stresses and the process for making such container.

대표청구항 ▼

1. A plastic pressurized bottle produced by the process of:a) forming a material into a plastic bottle; b) heating said bottle to a temperature about 5° C. to about 15° C. below the Tg of the material; c) holding said bottle at said temperature for a period of time; d) cooling said bottle in a contr

1. A plastic pressurized bottle produced by the process of:a) forming a material into a plastic bottle; b) heating said bottle to a temperature about 5° C. to about 15° C. below the Tg of the material; c) holding said bottle at said temperature for a period of time; d) cooling said bottle in a controlled manner to a lower temperature; e) filling said bottle with a product; f) pressurizing sad bottle with a propellant; g) closing said filled and pressurized bottle with a valve; and wherein said filled and pressurized bottle is resistant to polar liquids, resistant to impact stresses, and the combinations thereof. 2. The bottle of claim 1 wherein said material is selected from the group consisting of polyamides, polyesters, polycarbonates, polyacrylates and mixtures thereof.3. The bottle of claim 2 wherein the polyester is selected from the group consisting of polyethylene terephthalate (PET), polyethylene naphthalate (PEN), and mixtures thereof.4. The bottle of claim 3 wherein the polyester is polyethylene terephthalate (PET).5. The bottle of claim 2 wherein the polyester comprises copolymers selected from the group consisting of polyethylene terephthalate glycol-modified (PETG), polycyclohexanedimethanol terephthalate (PCT), polycyclohexanedimethanol terephthalate isophthalate (PCTA), polycyclohexanedimethanol terephthalate glycol (PCTG), and mixtures thereof.6. The bottle of claim 5 wherein the polyester copolymer comprises monomers selected from the group consisting of isophthalic acid (IPA), terephthalic acid (TPA), butane diol (BD), cyclohexanedimethanol (CHDM), ethylene glycol (EG), diethylene glycol (DEG) and mixtures thereof.7. The bottle of claim 1 wherein the material is an amorphous polyamide.8. The bottle of claim 7 wherein the material is heated about 5° C. to about 15° C. below about 93° C. and 192° C.9. The bottle of claim 1 wherein the bottle is pressurized from about 10 psi to about 100 psi at 25° C.10. The bottle of claim 1 wherein the forming of a said plastic bottle is accomplished using Injection Stretch Blow Molding (ISBM).11. The bottle of claim 1 wherein the forming of a said plastic bottle is accomplished using Injection Blow Molding (IBM).12. The bottle of claim 1 wherein the forming of said plastic bottle is accomplished using Injection Molding (IM).13. The bottle of claim 1 wherein the product is selected from the group consisting of antiperspirants, deodorants, hairsprays, cooking sprays, liquids, perfumes, shaving cream/gels and drug products.14. The bottle of claim 1 wherein the bottle is clear.15. The bottle of claim 1 wherein the bottle is frosted.16. The bottle of claim 1 wherein the bottle is tinted.17. A process of making a filled and pressurized plastic bottle, the process comprising the steps of:a) forming a material into a plastic bottle; b) heating said bottle to a temperature about 5° C. to about 15° C. below the Tg of the material; c) holding said bottle at said temperature for a period of time; d) cooling said bottle in a controlled manner to a lower temperature; e) filling said bottle with a product; f) pressurizing said bottle with a propellant; g) closing said filled and pressurized bottle with a valve; and wherein said filled and pressurized bottle is resistant to polar liquids, resistant to impact stresses, and the combinations thereof. 18. The process of claim 17 wherein the product is selected from the group consisting of antiperspirants, deodorants, hairsprays, cooking sprays, liquids, perfumes, shaving creams/gels and drug products.