초록 ▼

The methods of manufacturing molds from shape memory materials and molds made thereby, in accordance with the present invention, provide numerous advantages for molding castable composite parts. The initial mold cost is low enough to accommodate economical production of as few as a single part incor

The methods of manufacturing molds from shape memory materials and molds made thereby, in accordance with the present invention, provide numerous advantages for molding castable composite parts. The initial mold cost is low enough to accommodate economical production of as few as a single part incorporating high surface definition and intricate three dimensional detail. The preferred methods and molds made thereby are transparent, thereby, curing of the corresponding part by ultra-violet and infra-red light is made possible, as well as, visual inspection during injection and curing of the given resin. Removal of the cured part from within the mold is simplified.

대표청구항 ▼

What is claimed is: 1. A method of making a mold from shape memory materials for manufacturing castable composite parts with resins which are solidified within said mold by application of a curing temperature, said method comprising the steps: a) providing said shape memory material with a glass tr

What is claimed is: 1. A method of making a mold from shape memory materials for manufacturing castable composite parts with resins which are solidified within said mold by application of a curing temperature, said method comprising the steps: a) providing said shape memory material with a glass transition temperature which exceeds said curing temperature, wherein said shape memory material comprises an embedded thermal energy generation means; b) processing said shape memory material into a memorized shape; and c) deforming said shape memory material from said memorized shape into a desired mold shape. 2. The method of claim 1 wherein said thermal energy generation means comprises an electrical conductor. 3. The method of claim 1 wherein said thermal energy generation means comprises thermally conductive fibers. 4. The method of claim 1 wherein the shape memory material is processed into a memorized shape that is in the form of a flat sheet. 5. The method of claim 1 wherein the shape memory material is processed into a memorized shape that is an inverted image of the desired mold shape. 6. The method of claim 1 wherein the shape memory material is transparent. 7. The method of claim 1 wherein said shape memory material is a shape memory polymer. 8. A method of making a mold for use in manufacturing castable composite parts, said parts being cast with resins that solidify within said mold upon application of a curing temperature, said method comprising the steps: a) providing a mold material of shape memory polymer having a glass transition temperature which exceeds the curing temperature of the castable composite part to be formed in the mold; b) processing said shape memory material into a memorized shape; and c) deforming said shape memory material from said memorized shape into a desired mold shape, wherein said desired mold shape is different from said memorized shape such that the mold expels the cast composite part therefrom when the shape memory polymer is caused to revert to its memorized shape. 9. The method of claim 8 further comprising embedding a thermal energy generation means in the shape memory polymer. 10. The method of claim 9 wherein said thermal energy generation means comprises thermally conductive fibers. 11. The method of claim 9 wherein the shaped memory material is processed into a memorized shape that is in the form of a flat sheet. 12. The method of claim 9 wherein the shaped memory material is processed into a memorized shape that is an inverted image of the desired mold shape. 13. The method of claim 9 wherein the shaped memory material is transparent. 14. The method of claim 9 wherein said thermal energy generation means comprises an electrical conductor. 15. The method of claim 8 wherein said processing of said shape memory material is by die casting. 16. The method of claim 8 wherein said processing of shape memory material is by extrusion. 17. The method of claim 8 wherein said processing of said shape memory material is by molding and annealing. 18. The method of claim 8 wherein said deforming of said shape memory material is by draping. 19. The method of claim 8 wherein said deforming of said shape memory material is by vacuum forming. 20. The method of claim 8 wherein said deforming of said shape memory material is by computer aided mechanical technology. 21. The method of claim 8 wherein said deforming of said shape memory material is by stamping. 22. The method of claim 21 wherein said stamping of said shape memory material is performed with said shape memory material below said glass transition temperature. 23. The method of claim 21 wherein said stamping of said shape memory material is performed with said shape memory material above said glass transition temperature. 24. The method of claim 8 wherein said shape memory material is a shape memory polymer.