A liner for a shaped charge comprising powdered heavy metal tungsten coated with a metal binder coating compressively formed into a liner body. Each of the powdered heavy metal particles are substantially uniformly coated with metal binder coating. The preferred powdered heavy metal particles are co
A liner for a shaped charge comprising powdered heavy metal tungsten coated with a metal binder coating compressively formed into a liner body. Each of the powdered heavy metal particles are substantially uniformly coated with metal binder coating. The preferred powdered heavy metal particles are comprised of tungsten. Optionally, the liner for a shaped charge includes a lubricant intermixed with the coated heavy metal particles. The metal binder coating is selected from the group consisting of copper, lead, nickel, tantalum, other malleable metals, and alloys thereof, and comprises from 40 percent to 3 percent by weight of the liner. The powdered heavy metal particles comprise from 60 percent to 97 percent by weight of the liner.
대표청구항▼
What is claimed is: 1. A liner for a shaped charge, which liner comprises: a quantity of powdered heavy metal particles substantially uniformly coated with a metal binder coating and compressively formed into a liner body by cold working, where said liner is collapsible into a penetrating jet upon
What is claimed is: 1. A liner for a shaped charge, which liner comprises: a quantity of powdered heavy metal particles substantially uniformly coated with a metal binder coating and compressively formed into a liner body by cold working, where said liner is collapsible into a penetrating jet upon application of a force to said liner outer surface, where the powdered heavy metal particles comprise an amount greater than 60% by weight to approximately 90% by weight of said liner, and the metal binder comprises from approximately 10% to less than 40% by weight of said liner. 2. The liner for a shaped charge of claim 1 wherein said metal binder coating is selected from the group consisting of copper, lead, nickel, tantalum, other malleable metals, and alloy combinations thereof. 3. The liner for a shaped charge of claim 1, wherein said powdered heavy metal particles are selected from the group consisting of tungsten, uranium, tantalum, and molybdenum. 4. A shaped charge comprising: a housing; a quantity of explosive inserted into said housing; and a liner inserted into said housing so that said quantity of explosive is positioned between said liner and said housing, said liner comprising powdered heavy metal particles coated with a metal binder coating and compressively formed into a liner body by cold working, where the powdered heavy metal particles comprise an amount greater than 60% to approximately 90% by weight of said liner and the metal binder comprises from approximately 10% to less than 40% by weight of said liner, and wherein upon detonation of said explosive said liner collapses and is formed into a jet that is ejected from the housing at a very high velocity. 5. The liner for a shaped charge of claim 4 wherein said metal binder coating is selected from the group consisting of copper, lead, nickel, tantalum, other malleable metals, and alloy combinations thereof. 6. The shaped charge of claim 4 wherein said powdered heavy metal particles are selected from the group consisting of tungsten, uranium, tantalum, and molybdenum. 7. A method of forming a shaped charge liner comprising the steps of: coating a multiplicity of powdered heavy metal particles with a metal binder; compressively forming said multiplicity of now coated heavy metal particles into a liner body by cold working, where said liner is collapsible into a penetrating jet upon application of a force to said liner outer surface, where the powdered heavy metal particles comprise an amount greater than 60% to approximately 90% by weight of said liner and the metal binder comprises from approximately 10% to less than 40% by weight of said liner. 8. The method of claim 7 wherein said metal binder coating is selected from the group consisting of copper, lead, nickel, tantalum, other malleable metals, and alloy combinations thereof. 9. The method of claim 7 wherein said powdered heavy metal particles are selected from the group consisting of tungsten, uranium, tantalum, and molybdenum.
연구과제 타임라인
LOADING...
LOADING...
LOADING...
LOADING...
LOADING...
이 특허에 인용된 특허 (15)
Leidel David J., Apparatus for discharging a high speed jet to penetrate a target.
Held Manfred (Aresing DEX) Leidig Alfred (Schrobenhausen DEX) Merl Wilhelm A. (Pforzheim DEX) Stempel Gnter (Kelkheim DEX), Hollow charge, or plate charge, lining and method of forming a lining.
Barlow, Darren Ross; Van Le, Cam; Barker, James Marshall, Perforating gun assembly and method for controlling wellbore pressure regimes during perforating.
Le, Cam Van; Barlow, Darren Ross; Nelson, Jeffrey Alan, Perforating gun assembly and method for controlling wellbore pressure regimes during perforating.
Le, Cam Van; Barlow, Darren Ross; Nelson, Jeffrey Alan, Perforating gun assembly and method for controlling wellbore pressure regimes during perforating.
Le, Cam Van; Barlow, Darren Ross; Nelson, Jeffrey Alan, Perforating gun assembly and method for controlling wellbore pressure regimes during perforating.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.