초록 ▼

A method for making a polymeric blast media, and a product of this method. The first step involves blending a melamine compound with a cellulosic material and compression molding said first blend to produce a compression molded first blend. This first blend is then cooled and then ground. In the nex

A method for making a polymeric blast media, and a product of this method. The first step involves blending a melamine compound with a cellulosic material and compression molding said first blend to produce a compression molded first blend. This first blend is then cooled and then ground. In the next step of this method, a urea compound is blended with a nano-clay material to produce a second blend and compression molded. This compression molded second blend is then ground to produce a particulate second blend. The particulate first blend is then blended with the particulate second blend. A blast media product of this method is also disclosed.

대표청구항 ▼

What is claimed is: 1. A method for making a polymeric blast media comprising the steps of: (a) blending a melamine compound with a cellulosic material to form a first blend; (b) compression molding said first blend to produce a compression molded first blend; (c) cooling said compression molded fi

What is claimed is: 1. A method for making a polymeric blast media comprising the steps of: (a) blending a melamine compound with a cellulosic material to form a first blend; (b) compression molding said first blend to produce a compression molded first blend; (c) cooling said compression molded first blend to produce a cooled first blend; (d) grinding said cooled first blend to produce a particulate first blend; (e) blending a urea compound with a nano-clay material to produce a second blend; (f) compression molding said second blend to produce a compression molded second blend; (g) cooling said compression molded second blend to produce a cooled second blend; (h) grinding said cooled second blend to produce a particulate second blend; (i) blending the particulate first blend with the particulate second blend to form a third blend. 2. The method of claim 1 wherein in step (a) the cellulosic material is alpha cellulose. 3. The method of claim 1 wherein in step (b) the first blend is compression molded at a temperature of from about 280째 F. to about 330째 F. and under a pressure of from about 300 tons per square inch to about 500 tons per square inch. 4. The method of claim 1 wherein in step (d) the cooled first blend is ground to from about 20/30 mesh to about 30/40 mesh. 5. The method of claim 1 wherein in step (e) the nano-clay is montmorillonite. 6. The method of claim 1 wherein in step (f) the second blend is compression molded at a temperature of from about 280째 F. to about 330째 F. and under a pressure of from about 300 tons per square inch to about 500 tons per square inch. 7. The method of claim 1 wherein in step (h) the cooled second blend is ground to from about 16/20 mesh size to about 40/60 mesh particulate size. 8. The method of claim 1 wherein in step (i) the first blend and second blend are blended in a ratio of about 1:1 by weight. 9. The method of claim 1 wherein in step (i) the third blend has a mesh particulate size from about 10/40 mesh to about 30/60 mesh. 10. The method of claim 1 wherein an acrylic polymer is ground and then added to the blend in step (i). 11. The method of claim 10 wherein the acrylic polymer is a cross-linked cast polymer. 12. The method of claim 10 wherein the acrylic polymer is ground to from about a 20/30 mesh size to about a 30/40 mesh size. 13. The method of claim 10 wherein the acrylic polymer is blended in about equal proportion with the first blend and the second blend. 14. The method of claim 1 wherein after step (c) wherein the blast media is comprised of a plurality of individual particles which a polyurethane coating is applied. 15. The method of claim 1 wherein a dense particulate material selected from a glass oxide and a metal oxide is added to the first blend. 16. The method of claim 15 wherein the dense particulate material is a glass oxide material having a size of at least about-80 mesh. 17. The method of claim 15 wherein the dense particulate material is an aluminum oxide material having a grit size of from about 230 to 320. 18. The method of claim 1 wherein an about 30/40 mesh size melamine compound material and an about 20/30 mesh size allyldiglycol carbonate material are added to the first blend. 19. A product of a method of making a polymeric blast media comprising the steps of: (a) blending a melamine compound with a cellulosic material to form a first blend; (b) compression molding said first blend to produce a compression molded first blend; (c) cooling said compression molded first blend to produce a cooled first blend; (d) grinding said cooled first blend to produce a particulate first blend; (e) blending a urea compound with a nano-clay material to produce a second blend; (f) compression molding said second blend to produce a compression molded second blend; (g) cooling said molded second blend to produce a cooled second blend; (h) grinding said cooled second blend to produce a particulate second blend; (i) blending the particulate first blend with the particulate second blend to form a third blend. 20. The product of the method of claim 19 wherein in step (a) the cellulosic material is alpha cellulose. 21. The product of the method of claim 19 wherein step (b) the first blend if compression molded at a temperature of from about 280째 F. to about 300째 F. and under a pressure of from about 300 tons per square inch to about 500 tons per square inch. 22. The product of the method of claim 19 wherein in step (c) the cooled first blend is ground to from about 20/30 mesh to about 30/40 mesh. 23. The product of the method of claim 19 wherein in step (e) the nano-clay is montmorillonite. 24. The product of the method of claim 19 wherein in step (h) the second blend is compression molded at a temperature of from about 280째 F. to about 330째 F. and under a pressure of from about 300 tons per square inch to about 500 tons per square inch. 25. The product of the method of claim 19 wherein in step (i) the first blend and second blend are blended in a ratio of about 1:1 by weight. 26. The product of the method of claim 19 wherein in step (i) the third blend has a mesh particulate size from about 10/40 to about 30/60. 27. The product of the method of claim 19 wherein an acrylic polymer is ground and then added to the blend in step (i).