초록 ▼

Silicon carbide fibers are produced by mixing discontinuous isotropic carbon fibers with a silica source and exposing the mixture to a temperature of from about 1450째 C. to about 1800째 C. The silicon carbide fibers are essentially devoid of whiskers have excellent resistance to oxidation and excelle

Silicon carbide fibers are produced by mixing discontinuous isotropic carbon fibers with a silica source and exposing the mixture to a temperature of from about 1450째 C. to about 1800째 C. The silicon carbide fibers are essentially devoid of whiskers have excellent resistance to oxidation and excellent response to microwave energy, and can readily be formed into a ceramic medium employing conventional ceramic technology. The fibers also may be used for plastic and metal reinforcement.

대표청구항 ▼

We claim: 1. Discontinuous silicon carbide fiber essentially devoid of whiskers, essentially devoid of boron, and having less than about 1.25 wt percent nitrogen and an apparent density of greater than about 1.65 g/cc. 2. Silicon carbide fiber of claim 1, wherein the silicon carbide fiber has le

We claim: 1. Discontinuous silicon carbide fiber essentially devoid of whiskers, essentially devoid of boron, and having less than about 1.25 wt percent nitrogen and an apparent density of greater than about 1.65 g/cc. 2. Silicon carbide fiber of claim 1, wherein the silicon carbide fiber has less than about 1.1 wt percent nitrogen. 3. Silicon carbide fiber of claim 2, wherein the silicon carbide fiber has less than about 0.9 wt percent nitrogen. 4. Silicon carbide fiber of claim 1, wherein the silicon carbide fiber has an apparent density of at least about 1.85 g/cc. 5. Silicon carbide fiber of claim 4, wherein the silicon carbide fiber has an apparent density of at least about 2.0 g/cc. 6. Silicon carbide fiber of claim 5, wherein the silicon carbide fiber has an apparent density of at least about 2.2 g/cc. 7. Silicon carbide fiber of claim 2, wherein the silicon carbide fiber has an apparent density of at least about 1.85 g/cc. 8. Silicon carbide fiber of claim 7, wherein the silicon carbide fiber has an apparent density of at least about 2.0 g/cc. 9. Silicon carbide fiber of claim 8, wherein the silicon carbide fiber has an apparent density of at least about 2.2 g/cc. 10. Silicon carbide fiber of claim 3, wherein the silicon carbide fiber has an apparent density of at least about 1.85 g/cc. 11. Silicon carbide fiber of claim 10, wherein the silicon carbide fiber has an apparent density of at least about 2.0 g/cc. 12. Silicon carbide fiber of claim 10, wherein the silicon carbide fiber has an apparent density of at least about 2.2 g/cc. 13. Silicon carbide fiber of claim 4, wherein the silicon carbide fiber has less than about 0.9 wt percent oxygen. 14. Silicon carbide fiber of claim 7, wherein the silicon carbide fiber has less than about 0.9 wt percent oxygen. 15. Silicon carbide fiber of claim 10, wherein the silicon carbide fiber has less than about 0.9 wt percent oxygen. 16. Silicon carbide fiber of claim 12, wherein the silicon carbide fiber has less than about 0.9 wt percent oxygen. 17. Silicon carbide fiber of claim 1 wherein the silicon carbide fiber has a true density of at least 3.0 g/cc. 18. A regenerable medium for filtering combustible carbonaceous compounds from fluids comprising silicon carbide fiber of claim 1. 19. A fibrous web comprising silicon carbide fiber of claim 1. 20. The web of claim 19, wherein the web is non-woven. 21. The web of claim 20, wherein the web is wet laid.