초록 ▼

A method of forming a metal product. A metal alloy workpiece substrate is provided have pre-process dimensions. The dimensional differences are determined between the pre-process dimensions of the workpiece substrate and desired post-process dimensions of a post-process metal product formed from the

A method of forming a metal product. A metal alloy workpiece substrate is provided have pre-process dimensions. The dimensional differences are determined between the pre-process dimensions of the workpiece substrate and desired post-process dimensions of a post-process metal product formed from the workpiece substrate. A build-up thickness is determined of coating material required to obtain the desired post-process dimensions of the post-process metal product. A high-density coating process is performed to coat the workpiece substrate with a coating material to build-up a thickness of coating material effective to obtain desired finished dimensions after performing a sintering heat treatment process and/or a hot isostatic pressing treatment. The sintering heat treatment is performed on the coated workpiece substrate to densify the coating material. Then, the hot isostatic pressing treatment is performed to obtain the post-process metal product having the desired post-process dimensions and having diffusion bonding between the coating material and the workpiece substrate.

대표청구항 ▼

What is claimed is: 1. A method of forming a metal product having an edge area comprising a cutting edge having a wear resistant surface, comprising the steps of: forming a workpiece substrate having an edge area comprising a cutting edge portion; performing a high-density coating process to coat a

What is claimed is: 1. A method of forming a metal product having an edge area comprising a cutting edge having a wear resistant surface, comprising the steps of: forming a workpiece substrate having an edge area comprising a cutting edge portion; performing a high-density coating process to coat at least the cutting edge portion of the workpiece substrate with a wear resistant coating material; performing a hot isostatic pressing treatment on the coated workpiece substrate to obtain a metal product having a wear resistant surface comprised of the coating material, the hot isostatic pressing treatment comprising disposing the coated workpiece substrate within a chamber, filling the chamber with an inert gas, and heating and pressurizing the inert gas so that the wear resistant surface is formed at the cutting edge portion and having a diffusion bonding between the coating material and the workpiece substrate; and sharpening the cutting edge portion so that the diffusion bonding between the coating material and the workpiece substrate retains the wear resistant coating material on the cutting edge portion during the sharpening process of the cutting edge portion and during use of the cutting edge portion of the formed metal product. 2. A method of forming a metal product having a cutting edge according to claim 1 wherein the step of performing the high-density coating process comprises performing a hyper velocity oxy-fuel thermal spray process. 3. A method of forming a metal product having a cutting edge according to claim 2 wherein the step of hot isostatic pressing treating comprises the step of heating the coated cutting tool substrate to a temperature that is substantially 80% of the melting point of the coating material; and pressurizing the coated cutting tool substrate to a pressure substantially between 20 and 50 percent of the yield strength of the [metal alloy] coating material in an inert gas atmosphere. 4. A method of forming a metal product having a cutting edge according to claim 3 further comprising the step of performing a sintering heat treatment on the coated workpiece substrate to remove entrapped gas in the coating material before performing the hot isostatic pressing treatment so that the formed metal product has a relatively smooth surface texture. 5. A method of forming a metal product having a cutting edge according to claim 1 wherein the workpiece substrate comprises a high speed steel substrate composition. 6. A method of forming a metal product having a cutting edge according to claim 1 wherein the coating material comprises a hard and durable metal such as Cobalt, Carbide and TiN. 7. A method of forming a metal product having a cutting edge according to claim 1 wherein the workpeice substrate comprises a nickel or cobalt-base superalloy; and the step of performing the high-density coating process comprises performing a high-density coating process such as a hyper velocity oxy-fuel thermal spray process or a detonation gun process to apply the coating material as a high-density coating. 8. A method of forming a metal product having a cutting edge according to claim 1 wherein the cutting tool comprises one of a drill bit, end mill, lathe tool bit, saw blade, planer knife, and cutting tool insert. 9. A method of forming a metal product having a cutting edge according to claim 1 wherein the metal product formed comprises one of an ice skate blade, snow ski edge, pen tip and fishing hook. 10. A method of forming a kitchen knife having an edge area comprising a cutting edge having a wear resistant surface, comprising the steps of: forming a knife substrate having an edge area comprising a cutting edge portion; performing a high-density coating process to coat at least the cutting edge portion of the knife substrate with a wear resistant coating material; performing a hot isostatic pressing treatment on the coated knife substrate to obtain a kitchen knife having a wear resistant surface comprised of the coating material, the hot isostatic pressing treatment comprising disposing the coated workpiece substrate within a chamber, filling the chamber with an inert gas, and heating and pressurizing the inert gas so that the wear resistant surface is formed at the cutting edge portion and having a diffusion bonding between the coating material and the knife substrate; and sharpening the cutting edge portion so that the diffusion bonding between the coating material and the knife substrate retains the wear resistant coating material on the cutting edge portion during an edge sharpening process of the cutting edge portion and during use of the cutting edge portion of the formed kitchen knife. 11. A method of forming a kitchen knife having a cutting edge according to claim 10 wherein the step of performing the high-density coating process comprises performing a hyper velocity oxy-fuel thermal spray process. 12. A method of forming a kitchen knife having a cutting edge according to claim 11 wherein the step of hot isostatic pressing treating comprises the step of heating the coated cutting tool substrate to a temperature that is substantially 80% of the melting point of the coating material; and pressurizing the coated cutting tool substrate to a pressure substantially between 20 and 50 percent of the yield strength of the coating material in an inert gas atmosphere. 13. A method of forming a kitchen knife having a cutting edge according to claim 12 further comprising the step of performing a sintering heat treatment on the coated knife substrate to remove entrapped gas in the coating material before performing the hot isostatic pressing treatment so that the formed kitchen knife has a relatively smooth surface texture. 14. A method of forming a kitchen knife having a cutting edge according to claim 10 wherein the coating material comprises a hard and durable metal such as Cobalt, Carbide and TiN. 15. A method of forming a cutting tool having a cutting edge having a wear resistant surface, comprising the steps of: forming a cutting tool substrate having a cutting edge portion; performing a high-density coating process to coat at least the cutting edge portion of the cutting tool substrate with a wear resistant coating material; and performing a hot isostatic pressing treatment on the coated cutting tool substrate to obtain a cutting tool having a wear resistant surface comprised of the coating material, the hot isostatic pressing treatment comprising disposing the coated workpiece substrate within a chamber, filling the chamber with an inert gas, and heating and pressurizing the inert gas so that the wear resistant surface is formed at the cutting edge portion and having a diffusion bonding between the coating material and the cutting tool substrate, the diffusion bonding between the coating material and the cutting tool substrate being effective for retaining the wear resistant coating material on the cutting edge portion during an edge sharpening process of the cutting edge portion and during use of the cutting edge portion of the formed cutting tool. 16. A method of forming a cutting tool having a cutting edge according to claim 15 wherein the step of performing the high-density coating process comprises performing a hyper velocity oxy-fuel thermal spray process. 17. A method of forming a cutting tool having a cutting edge according to claim 16 wherein the step of hot isostatic pressing treating comprises the step of heating the coated cutting tool substrate to a temperature that is substantially 80% of the melting point of the coating material; and pressurizing the coated cutting tool substrate to a pressure substantially between 20 and 50 percent of the yield strength of the coating material in an inert gas atmosphere. 18. A method of forming a cutting tool having a cutting edge according to claim 17 further comprising the step of performing a sintering heat treatment on the coated cutting tool substrate to remove entrapped gas in the coating material before performing the hot isostatic pressing treatment so that the formed cutting tool has a relatively smooth surface texture. 19. A method of forming a cutting tool having a cutting edge according to claim 15 wherein the coating material comprises a hard and durable metal such as Cobalt, Carbide and TiN.