초록 ▼

Mixed matrix membranes are prepared from zeolites and polymers, such as polyimides, in a void free fashion where either no voids or voids of less than several Angstroms are present at the interface of the polymer and the zeolite by bonding (hydrogen, ionic, or covalent) functional groups on the zeol

Mixed matrix membranes are prepared from zeolites and polymers, such as polyimides, in a void free fashion where either no voids or voids of less than several Angstroms are present at the interface of the polymer and the zeolite by bonding (hydrogen, ionic, or covalent) functional groups on the zeolite with functional groups on the polymer. The mixed matrix membranes may be cast or formed by ISAM processes, and may be present on a variety of supports including hollow fibers.

대표청구항 ▼

We claim: 1. A mixed matrix membrane, comprising zeolite; a surface active agent adhered by silanation to a surface of said zeolite and the zeolite surface is functionalized; and polyimide, said zeolite and said polyimide being bonded to each other by at least covalent bonds between said surface ag

We claim: 1. A mixed matrix membrane, comprising zeolite; a surface active agent adhered by silanation to a surface of said zeolite and the zeolite surface is functionalized; and polyimide, said zeolite and said polyimide being bonded to each other by at least covalent bonds between said surface agent on said zeolite and said polyimide. 2. The mixed matrix membrane as recited in claim 1 wherein said zeolite is selected from the group consisting of ZSM-2, ETS-4, LTL and MFI. 3. The mixed matrix membrane as recited in claim 1 wherein said zeolite has a diameter of not greater than 500 nanometers. 4. A mixed matrix membrane comprising a faujasite; a surface active agent adhered to said faujasite; and polyimide, said faujasite and said polyimide being bonded to each other by at least one of hydrogen, covalent, and ionic bonds between said surface agent on said faujasite and said polyimide. 5. The mixed matrix membrane as recited in claim 1 wherein said polyimide is 6FDA-6FpDA-DABA. 6. The mixed matrix membrane as recited in claim 1 wherein said polyimide is a glassy polymer. 7. A mixed matrix membrane comprising: zeolite; a surface active agent adhered to said zeolite; polyimide functionalized with carboxilic acid moieties; said zeolite and said polyimide being bonded to each other by at least one of hydrogen, covalent, and ionic bonds between said surface agent on said zeolite and said polyimide. 8. The mixed matrix membrane as recited in claim 1 wherein said surface active agent is a polyelectrolyte. 9. A mixed matrix membrane comprising: zeolite; a polyelectrolyte adhered to said zeolite, wherein said polyelectrolyte is selected from the group consisting of poly(allylamine hydrochloride), polyldiallyl dimethylammonium chloride, and aminopropyltriethoxysilane; and polyimide, said zeolite and said polyimide being bonded to each other by at least one of hydrogen, covalent, and ionic bonds between said surface agent on said zeolite and said polyimide. 10. The mixed matrix membrane as recited in claim 1 wherein said surface active agent includes multiple amine groups per coupling entity. 11. The mixed matrix membrane as recited in claim 1 wherein said surface active agent includes a siloxane coupling entity coupled to said zeolite. 12. The mixed matrix membrane of claim 5 wherein said zeolite is ZSM-2, and said surface active agent is aminopropyltriethoxysilane. 13. The mixed matrix membrane as recited in claim 1 further comprising a hollow fiber, wherein said zeolite, said surface active agent and said polyimide are disposed within said hollow fiber. 14. The mixed matrix membrane as recited in claim 13 wherein a longitudinal axis of said zeolite is parallel with a longitudinal axis of said hollow fiber. 15. The mixed matrix membrane as recited in claim 13 wherein said zeolite and said polyimide are in one or more defined longitudinal planes which are parallel to a longitudinal axis of said hollow fiber. 16. The mixed matrix membrane as recited in claim 15 wherein said zeolite is present as several defined segments. 17. The mixed matrix membrane as recited in claim 13 wherein said hollow fiber has a diameter ranging from 100 nm to 100 microns. 18. A mixed matrix membrane comprising: zeolite; a surface active agent adhered to said zeolite; and polyimide, said zeolite and said polyimide being bonded to each other by at least one of hydrogen, covalent, and ionic bonds between said surface agent on said zeolite and said polyimide; wherein said zeolite and said polyimide are each present as multiple layers with layers of zeolite sandwiched between layers of polyimide. 19. The mixed matrix membrane as recited in claim 1 wherein an interface between said zeolite and said polyimide has voids no bigger than 100 nanometers. 20. The mixed matrix membrane as recited in claim 1 wherein an interface between said zeolite and said polyimide is substantially void free. 21. A method of making a mixed matrix membrane comprising the steps of: functionalizing a zeolite to include first functional groups; wherein the functionalizing step includes heating a mixture comprising zeolite and toluene at a temperature in a range of 100째 C. to 110째 C.; combining a polymer having second functional groups with said zeolite to form a mixture; casting the mixture onto a support; removing solvent from the mixture; and annealing the mixture. 22. The method of claim 21 further comprising the step of functionalizing said polymer with said second functional groups. 23. The method of claim 22 wherein functionalizing the zeolite includes silanating polyelectrolytes onto the zeolite. 24. The method of claim 22 wherein functionalizing the zeolite includes introducing an amine group onto a surface of the zeolite. 25. A method of making a mixed matrix membrane comprising the steps of: functionalizing a zeolite to include first functional groups; wherein the functionalizing includes silanating with aminopropyl-triethoxysilane (APTES) combining a polymer having second functional groups with said zeolite to form a mixture; casting the mixture onto a support; removing solvent from the mixture; and annealing the mixture.