초록 ▼

A water soluble mask is formed on a substrate. Thereafter, a coating (e.g., low-E coating) is formed on the substrate in at least one select area over the mask and in at least one area where the mask is not provided. After the coating has been formed, water is used to remove the mask and a portion

A water soluble mask is formed on a substrate. Thereafter, a coating (e.g., low-E coating) is formed on the substrate in at least one select area over the mask and in at least one area where the mask is not provided. After the coating has been formed, water is used to remove the mask and a portion of the coating formed thereon in order to form a partially coated substrate. The technique may be used in applications such as in the making of vehicle windshields, or the like.

대표청구항 ▼

The invention claimed is: 1. A method of making a vehicle windshield, the method comprising: providing a glass substrate; silk-screen printing a water soluble ceramic paste mask onto at least one select area of the glass substrate in liquid and/or slurry form, the water soluble ceramic paste mask c

The invention claimed is: 1. A method of making a vehicle windshield, the method comprising: providing a glass substrate; silk-screen printing a water soluble ceramic paste mask onto at least one select area of the glass substrate in liquid and/or slurry form, the water soluble ceramic paste mask comprising an organic portion and a ceramic portion wherein an organic:ceramic ratio of the respective portions by weight is from about 3:1 to 1:1 when the ceramic paste mask is initially silk-screen printed onto the substrate, wherein the organic portion comprises a synthetic resin and propylenoxyd; drying the water soluble ceramic paste mask when the mask is on the glass substrate; after drying the water soluble ceramic paste mask on the glass substrate, sputtering a multi-layer low-E coating onto the substrate so that the low-E coating is provided over the mask in the at least one select area where the mask is provided and directly on the substrate in an area where the mask is not provided; removing the mask and a portion of the low-E coating provided thereon from the select area of the substrate, but not from the area of the substrate where the mask was not provided, using at least water at a temperature of no greater than 60 degrees C. thereby forming a partially coated substrate; and laminating the partially coated substrate to another substrate in forming the vehicle windshield. 2. The method of claim 1, wherein the removing is carried out using at least water at a temperature of from about 20 to 50 degrees C. 3. The method of claim 2, wherein the removing is carried out using at least water at a temperature of from about 20 to 40 degrees C. 4. The method of claim 1, wherein at the time when the water soluble ceramic paste mask is initially deposited on the substrate, the organic portion makes up by weight from about 50 to 75% of the ceramic paste mask and the ceramic portion makes up by weight from about 25 to 50% of the ceramic paste mask. 5. The method of claim 4, wherein at the time when the water soluble ceramic paste mask is initially deposited on the substrate, the organic portion makes up by weight from about 60 to 70% of the ceramic paste mask and the ceramic portion makes up by weight from about 30 to 40% of the ceramic paste mask. 6. The method of claim 1, wherein at a time when the silk-screening begins, the ceramic paste has a weight of from about 800 to 2, 000 gm/liter. 7. The method of claim 6, wherein at the time when the silk-screening begins, the ceramic paste has a weight of from about 1,100 to 1, 650 gm/liter. 8. The method of claim 7, wherein at the time when the silk-screening begins, the ceramic paste has a weight of from about 1,300 to 1, 550 gm/liter.