초록 ▼

Erosion resistant coating processes and material improvements for line-of-sight applications. The erosion resistant coating composition includes nanostructured grains of tungsten carbide (WC) and/or submicron sized grains of WC embedded into a cobalt chromium (CoCr) binder matrix. A high velocity ai

Erosion resistant coating processes and material improvements for line-of-sight applications. The erosion resistant coating composition includes nanostructured grains of tungsten carbide (WC) and/or submicron sized grains of WC embedded into a cobalt chromium (CoCr) binder matrix. A high velocity air fuel thermal spray process (HVAF) is used to create thick coatings in excess of about 500 microns with high percentages of primary carbide for longer life better erosion resistant coatings. These materials and processes are especially suited for hydroelectric turbine components.

대표청구항 ▼

The invention claimed is: 1. An erosion resistant coating, comprising: a matrix comprising cobalt chromium, wherein the cobalt is at about 4 to about 12 weight percent, and the chromium is at about 2 to about 5 weight percent, wherein the weight percents are based on a total weight of the coating;

The invention claimed is: 1. An erosion resistant coating, comprising: a matrix comprising cobalt chromium, wherein the cobalt is at about 4 to about 12 weight percent, and the chromium is at about 2 to about 5 weight percent, wherein the weight percents are based on a total weight of the coating; a plurality of tungsten carbide gains embedded in the cobalt chromium matrix, wherein the grains are less than about 2 microns in diameter; and wherein the erosion resistant coating has a thickness greater than about 500 microns and is deposited with a high velocity air fuel process. 2. The erosion resistant coating of claim 1, wherein the plurality of tungsten carbide grains have the diameter of about 0.3 microns to about 2 microns. 3. The erosion resistant coating of claim 1, wherein the plurality of tungsten carbide grains have the diameter of about 0.4 to about 1 micron. 4. The erosion resistant coating of claim 1, wherein the erosion resistant coating is formed by a high velocity air fuel process that can achieve average particle temperatures between about 1,500째 C. and about 1,700째 C. while maintaining average particle velocity above 600 meters per second. 5. The erosion resistant coating of claim 1, wherein the erosion resistant coating is formed by a high velocity air fuel process that can achieve average particle temperatures between about 1,500째 C. and about 1,600째 C. while maintaining average particle velocity above 700 meters per second. 6. The erosion resistant coating of claim 1, wherein the coating exhibits a lower level of decarburization than erosion resistant coatings formed utilizing processes other than the high velocity air fuel process.