A glass substrate is irradiated with a converged laser beam to thereby form a spherical or nearly spherical convex portion on a surface of the glass substrate. More preferably, there may be used a method including the steps of: sticking a glass substrate to a flat member having a predetermined spher

A glass substrate is irradiated with a converged laser beam to thereby form a spherical or nearly spherical convex portion on a surface of the glass substrate. More preferably, there may be used a method including the steps of: sticking a glass substrate to a flat member having a predetermined spherical or aspherical concave portion formed therein; and irradiating a converged laser beam onto a surface of the glass substrate just under the concave portion while making the converged laser beam penetrate through the flat member to thereby form a spherical or aspherical convex portion in the inside of the concave portion in accordance with the shape of the concave portion.

대표청구항 ▼

What is claimed is: 1. A method of producing a planar lens, comprising the steps of: attaching a glass substrate to a flat member having a predetermined spherical or aspherical concave portion formed thereon; and irradiating a converged laser beam onto a surface of said glass substrate just under s

What is claimed is: 1. A method of producing a planar lens, comprising the steps of: attaching a glass substrate to a flat member having a predetermined spherical or aspherical concave portion formed thereon; and irradiating a converged laser beam onto a surface of said glass substrate just under said concave portion while making said converged laser beam penetrate through said flat member to thereby form a spherical or aspherical convex portion in the inside of said concave portion in accordance with a shape of said concave portion. 2. A method of producing a planar lens array, comprising the steps of: sticking a glass substrate to a flat member having a plurality of predetermined spherical or aspherical concave portions formed therein; and irradiating a converged laser beam onto a surface of said glass substrate just under said plurality of concave portions while making said converged laser beam penetrate through said flat member to thereby form spherical or aspherical convex portions in the inside of said plurality of concave portions respectively in accordance with a shape of each of said plurality of concave portions. 3. A method of producing a planar lens array according to claim 1, wherein a linear expansion coefficient of said glass substrate in a region of temperature higher than a glass transition temperature of said glass substrate is not smaller than 1.1 times as large as that in a region of temperature lower than the glass transition temperature. 4. A method of producing a planar lens array according to claim 1, wherein an absorption factor of said glass substrate with respect to a wavelength of said laser beam used is from 30% to 95%, both inclusively. 5. A method of producing a planar lens array according to claim 2, wherein transmittance of said flat member with respect to a wavelength of said laser beam used is not lower than 70%. 6. The method of claim 2, wherein the glass substrate is formed of Na2O, MgO, Al2O3, SiO2, K2O and CaO.