초록▼
The invention relates to absorptive, crosslinked polymers which are based on partly neutralized, monoethylenically unsaturated monomers carrying acid groups, and have improved properties, in particular in respect of their capacity for transportation of liquids in the swollen state, and which has a h
The invention relates to absorptive, crosslinked polymers which are based on partly neutralized, monoethylenically unsaturated monomers carrying acid groups, and have improved properties, in particular in respect of their capacity for transportation of liquids in the swollen state, and which has a high gel bed permeability and high centrifuge retention capacity.
대표청구항▼
What is claimed is: 1. A superabsorbent polymer composition comprising a polymer consisting essentially of: a) from about 55 to about 99.9 wt. % of polymerizable unsaturated acid group containing monomers; b) from about 0.001 to about 5.0 wt. % based on the weight of a) of internal crosslinking ag
What is claimed is: 1. A superabsorbent polymer composition comprising a polymer consisting essentially of: a) from about 55 to about 99.9 wt. % of polymerizable unsaturated acid group containing monomers; b) from about 0.001 to about 5.0 wt. % based on the weight of a) of internal crosslinking agent; said superabsorbent polymer composition further comprising c) from about 0.001 to about 5.0 wt. % based on dry polymer powder weight of surface crosslinking agent applied to the particle surface; d) from about 0.01% to about 5 wt. % based on dry polymer powder weight of a penetration modifier added immediately before, during or immediately after the surface crosslinking step; e) from 0 to about 5 wt. % based on dry polymer powder weight of a multivalent metal salt on the surface; f) from 0 to 2 wt % based on dry polymer powder weight of a surfactant on the surface; and g) from about 0.01 to about 5 wt % based on dry polymer powder weight of an insoluble, inorganic powder wherein the composition has a degree of neutralization of more than about 25%; and a gel bed permeability numeric value GBP is at least about [54000 e-0.18x+ 75]×10-9 cm2 where x is the numeric value of centrifuge retention capacity; and a shear modulus G' is less than about 9,500 dynes/cm2 and an absorption against pressure at 0.7 psi of less than about 23 g/g. 2. A superabsorbent polymer composition according to claim 1 wherein GBP is at least about [54000 e-0.175x+100]×10-9 cm2. 3. A superabsorbent polymer according to claim 1 wherein GBP is at least about [54000 e-0.17x+100]×10-9 cm2. 4. A superabsorbent polymer composition according to claim 1 wherein GBP is at least about [54000 e-0.165x+100]×10-9 cm2. 5. A superabsorbent polymer composition according to claim 1 wherein the centrifuge retention capacity is greater than about 25 g/g. 6. A superabsorbent polymer compostion according to claim 1 wherein the centrifuge retention capacity is greater than about 27 g/g. 7. A superabsorbent polymer composition according to claim 1 wherein the gel bed permeability is at least about 500×10-9 cm2. 8. A superabsorbent polymer composition according to claim 1 wherein the shear modulus is from about 4000 to about 9000 dynes/cm 2. 9. A superabsorbent polymer composition according to claim 1 having the characteristics of centrifuge retention capacity from about 27 to about 30 g/g; a shear modulus from about 6400 to 8000 dynes/cm 2, and a gel bed permeability from about 800×10-9 cm2 to about 1500×10-9 cm2. 10. A superabsorbent polymer composition according to claim 1 having the characteristics of centrifuge retention capacity of at least about 30 g/g; a shear modulus from about 4500 to 6400 dynes/cm2, and a gel bed permeability of at least about 600×10-9 cm 2. 11. A water insoluble, slightly cross-linked, partially neutralized, superabsorbent polymer composition comprising a polymer consisting essentially of a polymerizable unsaturated acid group containing monomers and an internal crosslinking agent, and the superabsorbent polymer further comprising a penetration modifier, wherein the superabsorbent polymer has a gel bed permeability numeric value, GBP, of at least about [54000 e-0.18x+75]×10-9 cm2 where x is the numeric value of the centrifuge retention capacity; and a shear modulus, G', is less than about 9,500 dynes/cm2 and an absorption against pressure at 0.7 psi of less than about 23 g/g. 12. A superabsorbent polymer composition according to claim 11 wherein GBP is at least about [54000 e-0.175x+100]×10-9 cm2. 13. A superabsorbent polymer composition according to claim 11 wherein GBP is at least about [54000 e-0.17x+100]×10-9 cm2. 14. A superabsorbent polymer composition according to claim 11 wherein GBP is at least about [54000 e-0.165x+100]×10-9 cm2. 15. A superabsorbent polymer composition according to claim 11 wherein the gel bed permeability is at least about 500×10-9 cm2. 16. A superabsorbent polymer composition according to claim 11 having the characteristics of centrifuge retention capacity from about 27 to about 30 g/g; a shear modulus from about 6400 to 8000 dynes/cm 2, and a gel bed permeability from about 800×10-9 cm2 to about 1500×10-9 cm2. 17. A superabsorbent polymer composition according to claim 11 having the characteristics of centrifuge retention capacity of at least about 30 g/g; a shear modulus from about 4500 to 6400 dynes/cm 2, and a gel bed permeability of at least about 600×10-9 cm2. 18. A superabsorbent polymer composition comprising a polymer consisting essentially of: a) from about 55 to about 99.9 wt. % of polymerizable unsaturated acid group containing monomers; and b) from about 0.001 to about 5.0 wt. % based on the weight of a) of internal crosslinking agent; said superabsorbent polymer composition further comprising c) from about 0.001 to about 5.0 wt. % based on dry polymer powder weight of surface crosslinking agent applied to the particle surface; d) from about 0.01% to about 5 wt. % based on dry polymer powder weight of a penetration modifier added immediately before, during or immediately after the surface crosslinking step; e) from 0 to about 5 wt. % based on dry polymer powder weight of a multivalent metal salt on the surface; f) from 0 to 2 wt % based on dry polymer powder weight of a surfactant on the surface; and g) from about 0.01 to about 5 wt % based on dry polymer powder weight of an insoluble, inorganic powder wherein the composition has a degree of neutralization of more than about 25%; having the characteristics of centrifuge retention capacity from about 27 to about 30 g/g; a shear modulus from about 6400 to about 8000 dynes/cm2 and a gel bed permeability from about 800×10-9 cm2 to about 1500×10-9 cm2 and an absorption against pressure at 0.7 psi of less than about 23 g/g. 19. A superabsorbent polymer composition comprising a polymer consisting essestially of: a) from about 55 to about 99.9 wt. % of polymerizable unsaturated acid group containing monomers; b) from about 0.001 to about 5.0 wt. % based on the weight of a) of internal crosslinking agent; said superabsorbent polymer composition further comprising c) from about 0.001 to about 5.0 wt. % based on dry polymer powder weight of surface crosslinking agent applied to the particle surface; d) from about 0.01% to about 5 wt. % based on dry powder weight of a penetration modifier added immediately before, during or immediately after the surface crosslinking step; e) from 0 to about 5 wt. % based on dry polymer powder weight of a multivalent metal salt on the surface; f) from 0 to 2 wt % based on dry polymer powder weight of a surfactant on the surface; and g) from about 0.01 to about 5 wt % based on dry polymer powder of an insoluble, inorganic powder wherein the composition has, a degree of neutralization of more than about 25%; and a gel bed permeability numeric value GBP is at least about [54000 e-0.18x+ 75]×10-9 cm2 where x is the numeric value of centrifuge retention capacity; and an absorption against pressure at 0.7 psi of less than about 23 g/g. 20. A superabsorbent polymer composition according to claim 19 wherein GBP is at least about [54000 e-0.175x+100]×10-9 cm2. 21. A superabsorbent polymer composition according to claim 19 wherein GBP is at least about [54000 e-0.17x+100]×10-9 cm2. 22. A superabsorbent polymer composition according to claim 19 wherein GBP is at least about [54000 e-0.165x+100]×10-9 cm2. 23. A superabsorbent polymer composition according to claim 19 wherein the centrifuge retention capacity is greater than about 25 g/g. 24. A superabsorbent polymer composition according to claim 19 wherein the centrifuge retention capacity is greater than about 27 g/g. 25. A superabsorbent polymer composition according to claim 19 having the characteristics of centrifuge retention capacity from about 27 to about 30 g/g; and a gel bed permeability from about 800×10-9 cm2 to about 1500×10-9 cm2. 26. A superabsorbent polymer composition according to claim 19 having the characteristics of centrifuge retention capacity of at least about 30 g/g; and a gel bed permeability of at least about 600×10-9 cm2. 27. A superabsorbent polymer composition comprising a polymer consisting essentially of: a) from about 55 to about 99.9 wt. % of polymerizable unsaturated acid group containing monomers; b) from about 0.001 to about 5.0 wt. % based on the weight of a) of internal crosslinking agent; said superabsorbent polymer composition further comprising c) from about 0.001 to about 5.0 wt. % based on dry polymer powder weight of surface crosslinking agent applied to the particle surface; d) from about 0.01% to about 5 wt. % based on dry poymer powder weight of a penetration modifier added immediately before, during or immediately after the surface crosslinking step; e) from 0 to about 5 wt. % based on dry polymer powder weight of a multivalent metal salt on the surface; f) from 0 to 2 wt % based on dry polymer powder weight of the surfactant on the surface; and g) from about 0.01 to about 5 wt % based on dry polymer powder weight of an insoluble, inorganic powder wherein the composition has, a degree of neutralization of more than about 25%; having the characteristics of centrifuge retention capacity from about 27 to about 30 g/g; a gel bed permeability from about 800×10-9 cm2 to about 1500×10-9 cm2 and an absorption against pressure at 0.7 psi of less than about 23 g/g. 28. A superabsorbent polymer composition comprising a polymer consisting essentially of: a) from about 55 to about 99.9 wt. % of polymerizable unsaturated acid group containing monomers; b) from about 0.001 to about 5.0 wt. % based on the weight of a) of internal crosslinking agent; said superabsorbent polymer composition further comprising c) from about 0.001 to about 5.0 wt. % based on dry polymer powder weight of surface crosslinking agent applied to the particle surface; d) from about 0.01% to about 5 wt. % based on dry polymer powder weight of a penetration modifier added immediately before, during or immediately after the surface crosslinking step; e) from 0 to about 5 wt. % based on dry polymer powder weight of a multivalent metal salt on the surface; f) from 0 to 2 wt % based on dry polymer powder weight of a surfactant on the surface; and g) from about 0.01 to about 5 wt % based on dry polymer weight of an insoluble, inorganic powder wherein the composition has, a degree of neutralization of more than about 25%; and a gel bed permeability is at least 300×10-9 cm2 and greater than [0.34(G')-2080]×10-9 cm2 where G' is the numeric value of shear modulus in dynes/cm2; and an absorption against pressure at 0.7 psi of less than about 23 g/g. 29. A superabsorbent polymer according to claim 28 where the GBP is at least 400×10-9 cm2. 30. A superabsorbent polymer composition according to claim 28 where the GBP is at least 500×10-9 cm2. 31. A superabsorbent polymer composition according to claim 28 having the characteristics of centrifuge retention capacity from about 27 to about 30 g/g; a shear modulus from about 6400 to 8000 dynes/cm 2. 32. A superabsorbent polymer composition according to claim 28 having the characteristics of centrifuge retention capacity of at least about 30 g/g; a shear modulus from about 4500 to 6400 dynes/cm 2. 33. A water insoluble, slightly cross-linked, partially neutralized, superabsorbent polymer composition comprising a polymer consisting essentially of a polymerizable unsaturated acid group containing monomers and an internal crosslinking agent, and the superabsorbent polymer further comprising a penetration modifier, wherein the superabsorbent polymer has a gel bed permeability numeric value, GBP, at least about [0.34(G'-(2080)]×10-9 cm2 where G' is the numeric value of the shear modulus; with a minimum GBP of 300×10-9 cm2 and an absorption against pressure at 0.7 psi of less than about 23 g/g. 34. A superabsorbent polymer composition according to claim 33 where the GBP is at least 400×10-9 cm2. 35. A superabsorbent polymer composition according to claim 33 where the GBP is at least 500×10-9 cm2. 36. A superabsorbent polymer composition according to claim 33 having the characteristics of centrifuge retention capacity from about 27 to about 30 g/g; a shear modulus from about 6400 to 8000 dynes/cm 2. 37. A superabsorbent polymer composition according to claim 33 having the characteristics of centrifuge retention capacity of at least about 30 g/g; a shear modulus from about 4500 to 6400 dynes/cm 2. 38. A superabsorbent polymer composition comprising a polymer consisting essentially of: a) from about 55 to about 99.9 wt. % of polymerizable unsaturated acid group containing monomers; b) from about 0.001 to about 5.0 wt. % based on the weight of a) of internal crosslinking agent; said superabsorbent polymer composition further comprising c) from about 0.001 to about 5.0 wt. % based on dry polymer powder weight of surface crosslinking agent applied to the particle surface; d) from about 0.01% to about 5 wt. % based on dry polymer powder weight of a penetration modifier added immediately before, during or immediately after the surface crosslinking step; e) from 0 to about 5 wt. % based on dry polymer powder weight of a multivalent metal salt on the surface; f) from 0 to 2 wt % based on dry polymer powder weight of a surfactant on the surface; and g) from about 0.01 to about 5 wt % based on dry polymer powder weight of an insoluble, inorganic powder wherein the composition has a degree of neutralization of more than about 25%; and a gel bed permeability numeric value GBP is at least about [54000 e-0.18x+ 75]×10-9 cm2 where x is the numeric value of centrifuge retention capacity; and a shear modulus G' is less than about 9,500 dynes/cm2. 39. A superabsorbent polymer composition according to claim 38 wherein GBP is at least about [54000 e-0.175x+100]×10-9 cm2. 40. A superabsorbent polymer composition according to claim 38 wherein GBP is at least about [54000 e-0.17x+100]×10-9 cm2. 41. A superabsorbent polymer compositon according to claim 38 wherein GBP is at least about [54000 e-0.165x+100]×10-9 cm2. 42. A superabsorbent polymer composition according to claim 38 wherein the centrifuge retention capacity is greater than about 25 g/g. 43. A superabsorbent polymer compositon according to claim 38 wherein the centrifuge retention capacity is greater than about 27 g/g. 44. A superabsorbent polymer composition according to claim 38 wherein the gel bed permeability is at least about 500×10-9 cm2. 45. A superabsorbent polymer composition according to claim 38 wherein the shear modulus is from about 4000 to about 9000 dynes/cm 2. 46. A superabsorbent polymer composition according to claim 38 having the characteristics of centrifuge retention capacity from about 27 to about 30 g/g; a shear modulus from about 6400 to 8000 dynes/cm 2, and a gel bed permeability from about 800×10-9 cm2 to about 1500×10-9 cm2. 47. A superabsorbent polymer composition according to claim 38 having the characteristics of centrifuge retention capacity of at least about 30 g/g; a shear modulus from about 4500 to 6400 dynes/cm 2, and a gel bed permeability of at least about 600×10-9 cm2. 48. A water insoluble, slightly cross-linked, partially neutralized, superabsorbent polymer composition comprising a polymer consisting essentially of a polymerizable unsaturated acid group containing monomers and an internal crosslinking agent, and the superabsorbent polymer further comprising a penetration modifier, wherein the superabsorbent polymer has a gel bed permeability numeric value, GBP, of at least about [54000 e-0.18x+75]×10-9 cm2 where x is the numeric value of the centrifuge retention capacity; and a shear modulus, G', is less than about 9,500 dynes/cm2. 49. A superabsorbent polymer composition according to claim 48 wherein GBP is at least about [54000 e-0.175x+100]×10-9 cm2. 50. A superabsorbent polymer composition according to claim 48 wherein GBP is at least about [54000 e-0.17x+100]×10-9 cm2. 51. A superabsorbent polymer composition according to claim 48 wherein GBP is at least about [54000 e-0.165x+100]×10-9 cm2. 52. A superabsorbent polymer composition according to claim 48 wherein the gel bed permeability is at least about 500×10-9 cm2. 53. A superabsorbent polymer composition according to claim 48 having the characteristics of centrifuge retention capacity from about 27 to about 30 g/g; a shear modulus from about 6400 to 8000 dynes/cm 2, and a gel bed permeability from about 800×10-9 cm2 to about 1500×10-9 cm2. 54. A superabsorbent polymer composition according to claim 48 having the characteristics of centrifuge retention capacity of at least about 30 g/g; a shear modulus from about 4500 to 6400 dynes/cm 2, and a gel bed permeability of at least about 600×10-9 cm2. 55. A superabsorbent polymer composition comprising a polymer consisting essentially of: a) from about 55 to about 99.9 wt. % of polymerizable unsaturated acid group containing monomers; b) from about 0.001 to about 5.0 wt. % based on the weight of a) of internal crosslinking agent; said superabsorbent polymer composition further comprising c) from about 0.001 to about 5.0 wt. % based on dry polymer powder weight of surface crosslinking agent applied to the particle surface; d) from about 0.01% to about 5 wt. % based on dry polymer powder weight of a penetration modifier added immediately before, during or immediately after the surface crosslinking step; e) from 0 to about 5 wt. % based on dry polymer powder weight of a multivalent metal salt on the surface; f) from 0 to 2 wt % based on dry polymer powder weight of a surfactant on the surface; and g) from about 0.01 to about 5 wt % based on dry polymer powder of an insoluble, inorganic powder wherein the composition has a degree of neutralization of more than about 25%; having the characteristics of centrifuge retention capacity from about 27 to about 30 g/g; a shear modulus from about 6400 to about 8000 dynes/cm2 and a gel bed permeability from about 800×10-9 cm2 to about 1500×10-9 cm2. 56. A superabsorbent polymer composition comprising a polymer consisting essentially of: a) from about 55 to about 99.9 wt. % of polymerizable unsaturated acid group containing monomers; b) from about 0.001 to about 5.0 wt. % based on the weight of a) of internal crosslinking agent; said superabsorbent polymer composition further comprising c) from about 0.001 to about 5.0 wt. % based on dry polymer powder weight of surface crosslinking agent applied to the particle surface; d) from about 0.01% to about 5 wt. % based on dry polymer powder of a penetration modifier added immediately before, during or immediately after the surface crosslinking step; e) from 0 to about 5 wt. % based on dry polymer powder weight of a multivalent metal salt on the surface; f) from 0 to 2 wt % based on dry polymer powder weight of a surfactant on the surface; and g) from about 0.01 to about 5 wt % based on dry polymer powder weight of an insoluble, inorganic powder wherein the composition has a degree of neutralization of more than about 25%; and a gel bed permeability is at least 300×10-9 cm2 and greater than [0.34(G')-2080]×10-9 cm2 where G' is the numeric value of shear modulus in dynes/cm2. 57. A superabsorbent polymer composition according to claim 56 where the GBP is at least 400×10-9 cm2. 58. A superabsorbent polymer composition according to claim 56 where the GBP is at least 500×10-9 cm2. 59. A superabsorbent polymer composition according to claim 56 having the characteristics of centrifuge retention capacity from about 27 to about 30 g/g; a shear modulus from about 6400 to 8000 dynes/cm 2. 60. A superabsorbent polymer composition according to claim 56 having the characteristics of centrifuge retention capacity of at least about 30 g/g; a shear modulus from about 4500 to 6400 dynes/cm 2. 61. A water insoluble, slightly cross-linked, partially neutralized, superabsorbent polymer composition comprising a polymer consisting essentially of a polymerizable unsaturated acid group containing monomers and an internal crosslinking agent, and the superabsorbent polymer further comprising a penetration modifier, wherein the superabsorbent polymer has a gel bed permeability numeric value, GBP, at least about [0.34(G'-(2080)]×10-9 cm2 where G' is the numeric value of the shear modulus; with a minimum GBP of 300×10-9 cm2. 62. A superabsorbent polymer composition according to claim 61 where the GBP is at least 400×10-9 cm2. 63. A superabsorbent polymer composition according to claim 61 where the GBP is at least 500×10-9 cm2. 64. A superabsorbent polymer composition according to claim 61 having the characteristics of centrifuge retention capacity from about 27 to about 30 g/g; a shear modulus from about 6400 to 8000 dynes/cm 2. 65. A superabsorbent polymer composition according to claim 61 having the characteristics of centrifuge retention capacity of at least about 30 g/g; a shear modulus from about 4500 to 6400 dynes/cm 2. 66. A superabsorbent polymer composition according to claim 1 comprising from about 0.01 % to about 5 wt. % of a multivalent metal salt. 67. A superabsorbent polymer composition according to claim 66 wherein the multivalent salt is aluminum sulfate. 68. A superabsorbent polymer composition according to claim 11 comprising for about 0.01 % to about 5 wt. % of a pretration modifier. 69. A superabsorbent polymer composition according to claim 11 comprising from about 0.01 % to about 5 wt. % of a multivalent metal salt. 70. A superabsorbent polymer composition according to claim 69 wherein the multivalent said is aluminum sulfate. 71. A superabsorbent polymer composition according to claim 18 comprising from about 0.01 % to about 5 wt. % of a multivalent metal salt. 72. A superabsorbent polymer composition according to claim 71 wherein the multivalent salt is aluminum sulfate. 73. A superabsorbent polymer composition according to claim 27 comprising from about 0.01 % to about 5 wt. % of a multivalent metal salt. 74. A superabsorbent polymer composition according 73 wherein the multivalent salt is aluminum sulfate.
Wang Lin,JPX ; Rezai Ebrahim,JPX ; Hayashi Yumiko,JPX ; Cho Eui-Boo,JPX, Absorbent material having improved absorbent permeability and methods for making the same.
Goldman Stephen A. (Cincinnati OH) Retzsch Herbert L. (Cincinnati OH) Mansfield Todd L. (Cincinnati OH), Absorbent members for body fluids having good wet integrity and relatively high concentrations of hydrogel-forming absor.
Goldman Stephen A. (Wyoming OH) Haynes Nancy A. (Okeana OH) Mansfield Todd L. (Cincinnati OH) Plischke Manfred (Steinbach DEX) Retzsch Herbert L. (Cincinnati OH) Walker Trevor (Cincinnati OH) Young G, Absorbent members for body fluids having good wet integrity and relatively high concentrations of hydrogel-forming absor.
Goldman Stephen Allen (Wyoming OH) Haynes Nancy Ann (Okeana OH) Mansfield Todd Leon (Cincinnati OH) Plischke Manfred (Steinbach DEX) Retzsch Herbert Louis (Cincinnati OH) Walker Trevor (Cincinnati OH, Absorbent members for body fluids having good wet integrity and relatively high concentrations of hydrogel-forming absor.
Dahmen Kurt (Mnchengladbach-Rheydt DEX) Mertens Richard (Krefeld DEX), Aqueous-liquid and blood-absorbing powdery reticulated polymers, process for producing the same and their use as absorbe.
Funk Rudiger,DEX ; Herfert Norbert,DEX ; Wanior Mariola,DEX ; Brown Patricia D. ; Engelhardt Fritz ; Woodrum Guy T., Crosslinked, hydrophilic, highly swellable hydrogels, production thereof and use thereof.
Mertens, Richard; Harren, Jorg, Powdery, cross-linked polymers which absorb aqueous liquids and blood, method for the production thereof and their use.
Wada Katsuyuki,JPX ; Nagasuna Kinya,JPX ; Fujino Shin-ichi,JPX ; Masuda Yoshihiko,JPX, Process for manufacturing an absorbing agent and absorbent material.
William G. Reeves ; Emmanuelle C. Damay ; Wendy L. Hamilton ; Patsy A. Hansen ; Jack N. Lindon ; Heather A. Sorebo, Process for preparing superabsorbent-containing composites.
Choi Su B. (Daejeon KPX) Lee Hyung M. (Daejeon KPX), Process for the preparation of a highly water absorptive resin from acrylic resin, epoxy crosslinker and hydrophilic sil.
Chambers Douglas R. (Chesapeake VA) Chiang William G-J (Virginia Beach VA) Woodrum Guy T. (Chesapeake VA), Superabsorbent polymers and products therefrom.
Sun Fang ; Jones Heather S. ; Kaiser Thomas A. ; Hsu Whei-Neen ; Molen Ronald L. ; Deaton Peter A. ; Messner Bernfried A., Superabsorbent polymers having anti-caking characteristics.
William G. Reeves ; Emmanuelle C. Damay ; Wendy L. Hamilton ; Patsy A. Hansen ; Jack N. Lindon ; Heather A. Sorebo, Superabsorbent-containing composites.
Sumiya Takashi,JPX ; Koike Masami,JPX ; Fujiura Yoji,JPX ; Nomoto Mihoko,JPX, Water-absorbent or water-retention material and production method thereof.
Kazuhisa Hitomi JP; Yuji Yamamoto JP; Shigenori Kirimura JP; Nobuyuki Harada JP, Water-absorbing composition and production process for water-absorbing agent.
Brehm, Helmut; Harren, Jorg; Issberner, Jorg; Mertens, Richard, Water-absorbing polymers having interstitial compounds, a process for their production, and their use.
Stanley ; Jr. ; deceased Frederick W. ; Lamphere Jack C. ; Wilson Larry R., Wrinkled absorbent particles of high effective surface area having fast absorption rate.
Daniel, Thomas; Stueven, Uwe; Krüger, Marco; Blei, Stefan; Lopez Villanueva, Francisco Javier; Herfert, Norbert, Method for producing permeable water-absorbing polymer particles through polymerization of drops of a monomer solution.
Tian, Gonglu; Ondisco, Matthew Thomas; Bergman, David L.; Messner, Bernfried; Smith, Scott J., Particulate superabsorbent polymer composition having improved stability.
Nagashima, Teruhisa; Nakamura, Masatoshi; Watanabe, Yusuke; Nogi, Kozo; Ishizaki, Kunihiko, Particulate water absorbing agent and method for producing the same.
Fujimaru, Hirotama; Ishizaki, Kunihiko; Nakahara, Sei, Polyacrylic acid (salt) water-absorbent resin, production process thereof, and acrylic acid used in polymerization for production of water-absorbent resin.
Gartner, Herbert; Harren, Jorg; Hager, Marc; Plochinger, Harald; Fricker, Daniel; Kohler, Hans-Peter; Auernig, Sabine, Process for the production of a superabsorbent polymer.
Azad, Michael M.; Smith, Scott J.; Joy, Mark; Blake, Geoffrey Wyatt; Jarman, Michael S., Superabsorbent polymer containing clay particulate, and method of making same.
Azad, Michael M.; Smith, Scott J.; Joy, Mark; Blake, Geoffrey Wyatt; Jarman, Michael S., Superabsorbent polymer containing clay, particulate, and method of making same.
Nakatsuru, Reiko; Sakamoto, Shigeru; Torii, Kazushi; Takaai, Toshihiro, Water-absorbable polyacrylic acid resin powder, and process for production thereof.
※ AI-Helper는 부적절한 답변을 할 수 있습니다.