초록 ▼

Biodegradable molded articles; a process for producing the same: and compositions for foam molding packed in a packaging film bag to be used in the production. A bowl-type container(10a), which is one of the biodegradable molded articles as described above, consists of a bowl body(11a) comprising st

Biodegradable molded articles; a process for producing the same: and compositions for foam molding packed in a packaging film bag to be used in the production. A bowl-type container(10a), which is one of the biodegradable molded articles as described above, consists of a bowl body(11a) comprising starch as the main component and a coating film(12) having at least hydrophobic properties and comprising a biodegradable plastic as the main component which is bonded to the surface of the bowl body(11a). This bowl body(11a) is formed by steam-foaming molding a material to be molded which is in the form of a slurry or a dough containing starch and water. The coating film(12) is closely bonded to the surface of the bowl body(11a) either directly or via an adhesive layer. Compositions for foam molding packed in such packaging film bags can be easily stored and molded.

대표청구항 ▼

What is claimed is: 1. A biodegradable molded article, comprising: a biodegradable expanded molded article molded in a specified shape; and a coating film attached on a surface of the biodegradable expanded molded article, wherein a boundary surface of a layer of the coating film and the surface of

What is claimed is: 1. A biodegradable molded article, comprising: a biodegradable expanded molded article molded in a specified shape; and a coating film attached on a surface of the biodegradable expanded molded article, wherein a boundary surface of a layer of the coating film and the surface of the biodegradable molded article is an irregular surface with bumps and dips, and wherein the biodegradable expanded molded article is mainly made of starch or a derivative thereof and molded through steam expansion of a slurry or dough molding material prepared by adding water to the starch or the derivative thereof, and wherein the coating film is mainly made of a biodegradable plastic and has at least hydrophobicity, and the coating film has a melting point of 170�� C. or higher, and wherein the biodegradable molded article is obtainable by simultaneously molding the biodegradable expanded molded article and attaching the coating film, the molding being carried out by heating the slurry or dough molding material and the coating film in a mold and by steam-expanding the biodegradable expanded molded article into the specific shape, and the attaching being carried out by compress-bonding the coating film through heating and thereby softening the film so that the coating film is attached on the surface of the biodegradable expanded molded article in the end. 2. The biodegradable molded article as set forth in claim 1, wherein the biodegradable expanded molded article accounts for not less than 60 weight % of the biodegradable molded article. 3. The biodegradable molded article as set forth in claim 1, wherein a gas phase included in the biodegradable expanded molded article accounts for more than 30 volume % of the biodegradable molded article. 4. The biodegradable molded article as set forth in claim 1, wherein the molding material includes water within a range between not less than 20 weight % and not more than 70 weight %, assuming that the biodegradable molded article is 100 weight %. 5. The biodegradable molded article as set forth in claim 1, wherein the coating film is directly attached on the surface of the biodegradable expanded molded article so as to substantially adhered to the surface. 6. The biodegradable molded article as set forth in claim 1, wherein the coating film is attached on the surface of the biodegradable expanded molded article by using a biodegradable adhesive. 7. The biodegradable molded article as set forth in claim 1, wherein a final water content of the biodegradable expanded molded article is not less than 3 weight % and not more than 20 weight %. 8. The biodegradable molded article as set forth in claim 1, wherein the coating film starts to be softened at a temperature of 130�� C. or higher. 9. A manufacturing method of a biodegradable molded article, comprising the step of: simultaneously molding a biodegradable expanded molded article and attaching a coating film, the molding being carried out by heating a slurry or dough molding material and the coating film in a mold and by steam-expanding the biodegradable expanded molded article into a specific shape, and the attaching being carried out by compress-bonding the coating film through heating and thereby softening the film so that the coating film is attached on a surface of the biodegradable expanded molded article in the end, wherein heating is carried out at a temperature not less than a softening point and less than a melting point of the biodegradable plastic, wherein the molding material is mainly made of starch or derivative thereof and prepared by adding water to the starch or the derivative thereof, and the coating film is mainly made of a biodegradable plastic having at least hydrophobicity, and the coating film has a melting point of 170�� C. or higher, and wherein the coating film is further transformed to be a bag shape used for storing the molding material therein. 10. A biodegradable molded article, comprising: a biodegradable expanded molded article molded in a specified shape; and a coating film attached on a surface of the biodegradable expanded molded article, wherein the biodegradable expanded molded article is mainly made of starch or a derivative thereof and molded through steam expansion of a slurry or dough molding material prepared by adding water to the starch or the derivative thereof, and wherein the coating film is mainly made of a biodegradable plastic and has at least hydrophobicity, and wherein a gas phase included in the biodegradable expanded molded article accounts for more than 30 volume % of the biodegradable molded article, and wherein the biodegradable molded article is obtainable by simultaneously molding the biodegradable expanded molded article and attaching the coating film, the molding being carried out by heating the slurry or dough molding material and the coating film in a mold and by steam-expanding the biodegradable expanded molded article into the specific shape, and the attaching being carried out by compress-bonding the coating film through heating and thereby softening the film so that the coating film is attached on the surface of the biodegradable expanded molded article in the end; wherein a boundary surface of a layer of the coating film and the surface of the biodegradable expanded molded article is an irregular surface with bumps and dips. 11. A manufacturing method of a biodegradable molded article, comprising the step of: simultaneously molding a biodegradable expanded molded article and attaching a coating film, the molding being carried out by heating a slurry or dough molding material and the coating film in a mold and by steam-expanding the biodegradable expanded molded article into a specific shape, and the attaching being carried out by compress-bonding the coating film through heating and thereby softening the film so that the coating film is attached on a surface of the biodegradable expanded molded article in the end, wherein the molding material is mainly made of starch or derivative thereof and prepared by adding water to the starch or the derivative thereof, and the coating film is mainly made of a biodegradable plastic having at least hydrophobicity, and the coating film has a melting point of 170�� C. or higher; and wherein the coating film is further transformed to be a bag shape used for storing the molding material therein.